"Investigate the optical properties and structures of CdS thin film as functions of deposition rate and annealing process, it was made the CdS thin film on the substrate glass by thermal co-evaporation CdS+S methode.To investigate the optical properties and structures of CdS thin film as functions of deposition rate and annealing process, it was made the CdS thin film on the substrate glass by thermal co-evaporation CdS+S methode. The deposition rates were adjusted to 4 A/s, 8 A/s, 12 A/s and 16 A/s and the annealing temperatures were to 200 °C, 300 °C and 400 °C- The thickness of thin films were around 7000 A. The optical constant and band gap energy were calculated from the Reflectance ( R ) and Tansmittance (T) by using O.S. Heavens formula. The value of R and T were obtained from UV-VIS Spectrofotometre with the wavelength from 400 inn to 800 run. From the calculations it was found that the deposition rate affected the optical properties and structures. At wave length 550 nm, the deposition rates 4 A/s, 8 A/s, 12 A/s and 16 A/s give the real refractive index n 2.534; 2.503; 2.46; 2.505 respectively and the absorption coefficient a 1.15 x 103, 5.96 x 103, 4.38 x 103, 7.33 x 103 /cm respectively and the band gap energy 2,46 eV, 2,44 eV, 2,42. eV, 2.40 eV respectively and the grain sizes 816 4 A, 291.5 A, 256.7 A, 251.1 A respectively. The annealing process to 200 °C, 300 0C and 400 0C also affected the optical properties and structures. At deposition rate 4 A/s the process without annealing, annealing to 200 °C, 300 °C and 400 °C give the real refraction index 2.513, 2.56, 2.54, 2.53 respectively and the absorption coefficient l .15x 103, 6 x 103, 7 x 103, 4 x 103 /cm respectively and the band-gap energy 2.46 eV, 2,43 eV, 2,40 eV, 2,42 eV respectively. At deposition rate 8 A/s the process without annealing, annealing to 200 °C, 300 °C and 400 0C give the real refraction index n 2.503, 2.527, 2.504, 2.505 respectively and the absorption coefficient 5.96x103, 6.5 x I03, 7.17 x l03 , 3-37 x 103 /cm respectively and the band gap energy 2,44 eV, 2,43 eV, 2.40 eV, 2,41 eV respectively. At deposition rate 12 A/s the process without annealing, annealing to 200 °C, 300 °C and 400 0C give the real refraction index n 2.46, 2.546, 2.495, 2.485 respectively and the absorption coefficient 4.38 x 103, 1.27 x 103, 0.15 x 103, 0.23 x 103 /cm respectively and the band gap energy 2.42 eV, 2,42 eV, 2,43 eV, 2,44 eV respectively. At deposition rate 16 A/s the process without annealing, annealing to 200 °C. 300 °C and 400 0C give the real refraction index n 2.505, 2.498, 2.499, 2.497 respectively and the absorption coefficient 7.33 x 103, 2.9 x 103, 1.7 x 103, 1.95 x 103 1cm respectively and the band gap energy 2,40 eV, 2,41: eV, 2,4.2 eV, 2,43 eV respectively. The c3-stall structures of thin film are found to be hexagonal with preferred orientation (002). The annealing processes affect the grain size. At the deposition rate 4 A's, the annealing process to 400 °C changed the grail? size from 816 A to 193,5 A. At the deposition rate 8 A/s, the amtealing process to 400 0C changed the grain size from 291,5 A to 168 A. At the deposition ratel2 A/s, the annealing process to 400 °C changed the grain size from 256,7 A to 198,2 A. At the deposition rate 16 A/s, the annealing process to 400 °C also changed the grain size from 251,1 A to 235,9 A.

---

Guna mengetahui perubahan sifat optis dan struktur terhadap laju deposisi pembuatan lapisan tipis dan juga terhadap anil, dibuat lapisan Cds dengan co-evaporasi termal CdS dan S diatas substrat kaca. Laju deposisi dibuat pada 4 A/s, 8 A/s, 12 As dan 16 A/s. Anil dilakukan pada setiap laju deposisi dengan 3 macam teinperatur yaitu: 200 0C, 300 oC dan 400 0C_ Ketebalan lapisan yang dibuat berkisar 7000 A. Konstanta optis yaitu koefisien absorpsi dan indek bias dihitung dari reflektansi R dan transmisi T berdasarkan metode fungsi minimal dengan menggunakan persamaan O.S. Heavens. Dad kurva koefisien abrsoipsi terhadap energi foton dibuat lebar pita terlarang CdS. Pengukuran nilai R dan T dilakukan dengan alat UV-VIS Spektrofotometer pada panjang gelombang 400 nm - 800 nm. Dari penelitian didapatkan bahwa laju deposisi mempengaruhi sifat optis material. Didapatkan nilai indek bias nyata pada laju deposisi 4 Als, 8 A/s, 12 A/s dan 16 A/s pada panjang gelombang 550 nm masing masing 2,534; 2,503; 2,46; 2,505 dan koefisien absorpsi masing-masing adalah 1,15 x 103; 5,96 x 103; 4,38 x I03; 7,33. x 103 /cm dan lebar pita terlarang masing-masing adalah 2,46 eV, 2,44 eV, 2.42 eV dan 2,40 eV. Besar butir menurun dengan meningkatnya laju deposisi. Besar butir pada laju deposisi 4 Als. 8 A/s, 12 AN dan 16 A/s berturut-turut adalah 816 A , 291,5 A, 256,7 A dan 251,1 A. Proses anil memberikan basil bahwa dari suhu 200 0C sampai 400 oC terjadi perobahan sifat optis dan struktur. Pada laju deposisi 4 A/s berturut-turut untuk proses tanpa anil, anil 200 0C, 300 oC dan 400 oC indek bias nyata n adalah 2,513; 2,56; 2,54 dan 2.53 dan nilai koefisien absorpsi adalah 1,15x103; 6 x 103; 7 x 103; 4 x 103 /cm dan lebar pita terlarang adalah 2.46 eV, 2,43 eV, 2,40 eV dan 2,42 eV. Piida laju deposisi 8 A/s berturut-turut untuk proses tanpa anil, anil 200 0C, 300 oC dan 400 oC indek bias nyata n adalah 2,503; 2,527; 2,504 dan 2,505 dan nilai koefisien absorpsi adalah 5.96x 103; 6,5 x 103; 7,17 x 103; 3,37 x 103 /cm dan lebar pita terlarang adalah 2,44 eV, 2,43 eV, 2,40 eV dan 2,41 eV. Pada laju deposisi 12 A/s berturut-turut tmtuk proses tanpa anil, anil 200 0C, 300 'DC dan 400 oC indek bias nyata n adalah 2,46; 2,546: 2,495 dan 2,485 dan nilai koefisien absorpsi adalah 4,38 x 103; 1,27 x 103; 0,15 x 103; 0,23 x 103 /cm dan lebar pita terlarang adalah 2.42 eV, 2,42 eV, 2,43 eV dan 2,44 eV. Pada laju deposisi 16 A/s berturut-turut untuk proses tanpa aril, aril .200 0C, 300 oC dan 400 0C indek bias nyata n adalah 2,505; 2,498; 2,499 dan 2.497 dan nilai koefisien absorpsi adalah 7,33 x 103; 2,9 x 103; 1,7 x 103; 1,95 x 103 /cm dan lebar pita terlarang adalah 2,40 eV, 2,41 eV, 2,42 eV dan 2,43 eV. Stniktur kristal lapisan tipis CdS yang terbentuk adalah heksagonal dengan prefi-'rred 0i-lank-Ilion (002). Proses anil inerubah besar ukuran butir. Pada sampel dengan laju deposisi 4 A/s anil 400 oC inerubah besar butir dart 816 A ke 193,5 A. Sampel dengan laju deposisi 8 A/s anil 400 oC merubah besar butir dari 291,5 A ke 168 A. Sampel dengan laju deposisi l2 A/s anil 400 oC merubah besar butir dari 256,7 A ke 198,2 A. Sampel dengan laju deposisi 16 A/s anif 400 oC merubah besar butir dari 251,1 Ake 235,9 A."

"Micro CDS/ISIS is an advanced non-numerical information storage and retrieval software developed by UNESCO since 1985 to satisfy the need expressed by many institutins, especially in developing countries, to be able to streamline their information processing activities by using modern (and relatively inexpensive) technologies. The software was originally based on the mainframe version of CDS/ISIS, started in the late'60s, thus taking advantage of several years of experience acquired in database management software development. Several partners contributed to its development trough the years."

"Penelitian ini bertujuan menganalisis pengaruh variabel ekonomi makro yang terdiri dari pertumbuhan inflasi, pertumbuhan depresiasi nilai tukar Rupiah terhadap US Dollar, pertumbuhan cadangan devisa, pertumbuhan yield obligasi pemerintah Amerika Serikat serta pertumbuhan premi Credit Default Swap terhadap pertumbuhan yield obligasi global pemerintah Indonesia - Indo16 yang berdenominasi US Dollar di pasar keuangan dunia selama periode Januari 2007 sampai dengan April 2014. Setelah dilakukan pengujian regresi melalui metode Ordinary Least Squares, penelitian ini menunjukkan adanya hubungan positif antara pertumbuhan inflasi, pertumbuhan depresiasi nilai tukar Rupiah terhadap US Dollar, pertumbuhan yield obligasi pemerintah Amerika Serikat terhadap pertumbuhan yield Indo16. Selain itu terdapat hubungan negatif antara pertumbuhan cadangan devisa terhadap pertumbuhan yield Indo16. Pertumbuhan premi Credit Default Swap memiliki hubungan positif terhadap pertumbuhan yield Indo16. Pertumbuhan yield obligasi pemerintah Amerika Serikat dan pertumbuhan CDS Indonesia memiliki pengaruh positif signifikan terhadap pertumbuhan yield obligasi global Indo16 yang berdenominasi US Dollar.

---

This study aimed to analyze the effect of macroeconomic variables: inflation growth, foreign exchange growth, foreign reserves growth, U.S. government bond yield growth and credit default swap growth to the growth of Indonesian sovereign global bond yield - INDO16 (denominated in US Dollar) in global financial market during the period January 2007 to April 2014.

After testing through an Ordinary Least Squares (OLS) test, this study showed a positive relationship between inflation growth, foreign exchange growth, U.S. government bond yield growth to the growth of Indonesian sovereign global bond yield -INDO16. In addition there is a negative relationship between Indonesian foreign reserve growth to INDO16 global bond yield growth. Credit Default Swap growth has a positive relationship to INDO 16 global bond yield growth. The growth of U.S. government bond yield and the growth of CDS has a significant influence to the growth of Indonesian global bond yield INDO-16."

"Produksi hidrogen dan degradasi 2,4,6-Triklorofenol secara simultan sudah dilakukan pada berbagai fotokatalis yaitu P25-TiO2, Titania Nanotube Arrays (TNTAs), dan variasi TNTAs-CdS selama 240 menit. VariasiTNTAs-CdS menggunakanperbandingan mol dari prekursor CdS yaitu CdCl2:CH3CSNH2dengan 0,2:0,12; 0,1:0,06; dan 0,05:0,03 mol/L. Hasil karakterisasi UV-Vis DRS menunjukkanenergy band gap berkisar antara 2,71- 2,89 eV.Fotokatalis terbaik didapat pada perbandingan 0,1:0,06 (TNTAs-CdS-2) karena menghasilkan hidrogen (3,17𝜇𝜇mol/g.s) dan degradasi 2,4,6-Triklorofenol (mencapai 80%) yang paling baik dibandingkan dengan katalis lainnya. Fotokatalis tersebut menghasilkan hidrogen 1,5 kali dibandingkan TNTAs dan 7 kali dibandingkan dengan P25-TiO2. Produksi hidrogen berjalan simultan dengan pendegradasian 2,4,6-Triklorofenol, dimana kinerja keduanya bergantung pada katalis yang digunakan. Disamping itu, pengaruh konsentrasi 2,4,6-Triklorofenol (10, 20, dan 40 ppm) dipelajari dengan menggunakan fotokatalis TNTAs-CdS-2 dan menghasilkan total produksi hidrogen berturut-turut 1,008; 1,061; dan 1,197𝜇𝜇mol/g.s. Semakin besar konsentrasi 2,4,6-Triklorofenol, semakin besar pula hidrogen yang dihasilkan.

---

Hydrogen production and 2,4,6-Trichlorophenoldegradationhave been investigated simultanously usingP25-TiO2, TNTAs, and variation of TNTAs-CdS for 240 minutes. TNTAs-CdS variations use mol ratio of CdS precursor that isCdCl2:CH3CSNH2 with ratio 0.2:0.12, 0.1:0.06, and 0.05:0.003.Rever to UVVis analysis, the TNTAs-CdS prepared have the band gap energy in the range of 2.71-2.89 eV. Among them, the optimum composition is0.1:0.06 (TNTAs-CdS- 2) which results in the highest total hydrogen production (3,17𝜇𝜇mol/g.s) and 2,4,6-Trichlorophenol degradation(achieve 80%) compared toothers. TNTAs- CdS-2 produces total hydrogen 1.5 and 7 times compared with TNTAs and P25- TiO2, respectively.Hydrogen production and 2,4,6-Trichlorophenol degradation could be perormed simultaneously and it depands on the catalyst employed. Furthermore, the effect of2,4,6-Trichlorophenol initial concentrations (10, 20, and 40 ppm) was also studied using TNTAs-CdS-2 and produced1.008,1.061, and1.197 𝜇𝜇 mol/g.s respectively.The higherthe 2,4,6-Trichlorofenol initial concentration, the more hydrogen produced."

"The Optical Properties of Cadmium Sulfide Thin Films Prepared by co-evaporation Deposition Methods of CdS and Sulfur. Cadmium Sulfide Thin Films have been deposited by thermal co-evaporation methods of CdS + S. The films were prepared on glass substrate and were varied by changing these deposition rates into 4-16 AIs. The thickness of the films and the real part of refractive indexes have been determined based on interference method using maximum and minimum of reflectance spectrum. The optical parameters a of these films have been determined by reflectance and transmittance spectrum using Hishikawa formulation of T/(1-R). The real part of refractive index and optical parameter a reduce with the higher deposition rate for transparency region - (E<2.6 eV). The optical gap almost did not show a certain tendency by deposition rate variation. The complex dielectric functions of these films reflect the real part of refractive indexes and extinction coefficients.

---

Lapisan tipis CdS telah dideposisi dengan metode co-evaporasi termal CdS+S. Lapisan tipis dideposisi di atas substrat kaca dan divariasi laju deposisinya 4 -16 AIs. Ketebalan dan indeks bias lapisan tipis ditentukan berdasarkan prinsip interferensi dengan menggunakan maksimum dan minimum spektrum reflektansi. Parameter optis a lapisan tipis ditentukan dari spektrum reflektansi dan transmitansi dengan menggunakan formulasi Hishikawa T/(1-R). Indeks bias rill dan parameter optis a berkurang dengan meningkatnya laju deposisi di daerah transparan (E < 2.6 eV). Gap optis tidak menunjukkan kecenderungan tertentu dengan variasi laju deposisi. Fungsi dielektrik kompleks lapisan tipis CdS mewakili indeks bias riil dan koefisien ekstinksi."

"Telah dibuat lapisan tipis CdS dengan metode koevaporasi CdS dan S dan telah diuji dengan XRD, UV-VIS Spectrophotometer, dan pengukuran hambatan. Lapisan yang terbentuk dipengaruhi beberapa parameter seperti, temperatur substrat, jarak antara sumber dan substrat, dan jarak antara sumber CdS dan sumber S. Hasil XRD menunjukkan bahwa lapisan yang terbentuk adalah CdS dengan preferred orientation pada bidang (0002}, dengan struktur hexagonal. Perlakuan panas yang diberikan pada temperatur 200°C di ruang vakum akan menurunkan besar hambatan, dan menaikkan respon terhadap cahaya."

"ABSTRACTKrisis energi dunia dan tingginya harga sumber energi fosil di Eropa dan negara barat menyebabkan innovasi dalam pemanfaatan energi alternatif yang tidak menimbulkan polusi udara CO2 maupun radio aktif. Sehingga diperlukan sumber energi baru, salah satunya adalah solar sel. CdS merupakan salah satu komponen penting sel surya lapis tipis. Pada pembuatan CdS sebagai lapisan buffer sel surya lapis tipis berbasis CZTS dilakukan dengan metode chemical bath deposition (CBD). CdS dideposisikan pada kaca terlapis CZTS dengan variable yang berbeda untuk mendapatkan kondisi deposisi yang optimal. Deposisi CdS telah berhasil dilakukan, dan temperatur optimalnya adalah 90°C. Temperatur dibawah 90°C akan menghasilkan lapisan antar muka yang dapat mengurangi sifat transmitansi lapisan CdS. Konsentrasi optimal pada [S]:[Cd] = 5, karena memiliki nilai transmitansi terbaik.

---

ABSTRACTThe world energy crisis and the high price of fossil energy sources in Europe and the western countries have led to innovation in the use of alternative energy that does not cause CO2 or radioactive air pollution. So that new energy sources are needed, one of which is solar cells. CdS is one of the important components of thin film solar cells. In making CdS as CZTS thin layer solar cell buffer layer was carried out by chemical bath deposition (CBD) method. CdS is positioned on CZTS coated glass with different variables to obtain optimal deposition conditions. CdS deposition has been successfully carried out, and the optimal temperature is 90°C. Temperatures below 90°C will produce an interface layer that can reduce the transmittance properties of the CdS layer. The optimal concentration at [S]: [Cd]=5, because it has the best transmittance value."

"Dalam setiap kegiatan automasi perpustakaan, dua hal pokok yang harus dilakukan ialah merancang format cantuman dan memilih perangkat lunak yang sesuai untuk menangani format cantuman tersebut. Kegiatan automasi perpustakaan akan lebih berdaya guna bila format cantuman yang digunakan memungkinkan pelaksanaan tukar-menukar data antar perpustakaan. Indonesia telah menyusun format komunikasi untuk digunakan sebagai sarana tukar-menukar data bibliografi antar perpustakaan, yang disebut INDOMARC. Di bidang perangkat lunak, UNESCO telah menyebarkan MICRO CDS/ISIS secara cuma-cuma kepada lembaga yang tidak mencari keuntungan. Perangkat lunak ini merupakan sistem simpan dan temu kembali informasi umum, yang secara khusus dirancang untuk tata laksana pangkalan data non-numerik. Dengan pertimbangan keadaan ini banyak perpustakaan di Indonesia akan memanfaatkan perangkat lunak ini. Bertolak dalam dua kenyataan tersebut itulah penelitian ini dilaksanakan. Tujuan penelitian ini ialah untuk melihat sejauh mana MICRO CDS/ISIS dapat menangani format INDOMARC. Analisis dilakukan atas struktur format INDOMARC dan struktur pangkalan data Micro CDS/ISIS. Dalam praktek dicoba penyusunan pangkalan data bibliografi dalam format INDOMARC dengan perangkat lunak Micro CDS/ISIS. Hasil analisis menunjukkan bahwa struktur data dalam Micro CDS/ISIS lebih sederhana daripada struktur format INDOMARC, yaitu bahwa dalam Micro CDS/ISIS tidak terdapat indikator dan keterulangan subruas. Berdasarkan hasil analisis disimpulkan bahwa perangkat lunak Micro CFDS/ISIS dapat digunakan untuk menangani format INDOMARC, tetapi dengan kompromi bahwa indikator dituliskan pada subruas 1 dan 2, dan keterulangan subruas dituliskan sebagaimana keterulang an ruas."

"Penelitian ini bertujuan untuk mengevaluasi penggunaan metode difusi cakram standar CLSI dan CDS dalam menentukan pola kepekaan Neisseria gonorrhoeae terhadap antibiotik. Pada metode difusi cakram standar CLSI dapat terjadi double zone inhibition yang dapat mempersulit dalam interpretasi zona hambat yang sesungguhnya. Dengan metode difusi cakram standar CDS diharapkan hal tersebut tidak terjadi. Penelitian ini merupakan uji kesetaraan antara hasil uji kepekaan antibiotik metode difusi cakram menurut standar CDS dan standar CLSI yang dibandingkan dengan Etest sebagai baku emas. Dari penelitian ini didapatkan hasil metode difusi cakram standar CDS lebih sesuai dengan Etest daripada standar CLSI pada tiga antibiotik yaitu azitromisin (total agreement 96,7%), seftriakson (total agreement 80,0%) dan penisilin (total agreement 73,3%) sedangkan metode difusi cakram standar CLSI lebih sesuai dengan Etest daripada standar CDS pada dua antibiotik yaitu siprofloksasin (total agreement 73,3%) dan spektinomisin (total agreement 73,3%). Pola kepekaan Neisseria gonorrhoeae terhadap antibiotik di RSCM dan pelayanan kesehatan jejaring menurut metode difusi cakram yang paling sesuai dengan Etest yaitu: dengan standar CDS didapatkan azitromisin 86,7%, seftriakson 76,7%, penisilin 16,7% dan dengan standar CLSI didapatkan siprofloksasin 0% dan spektinomisin 70%. Pola kepekaan Neisseria gonorrhoeae terhadap sefiksim yaitu 46,7% yang hanya diujikan dengan standar CLSI. Pemberian sefiksim dan seftriakson yang merupakan terapi pilihan untuk gonore harus diberikan secara bijak, untuk menghindari kejadian resistensi yang lebih luas.

---

This study aimed to evaluate the use of CLSI and CDS standard disc diffusion method in determining the sensitivity patterns of Neisseria gonorrhoeae to antibiotics. In the CLSI standard disc diffusion method can occur double inhibition zone that can complicate the interpretation of the actual inhibition zone. With the CDS standard disc diffusion method expected it does not happen. This study was a test of equivalence between the results of antibiotic susceptibility test disc diffusion method according to CLSI standards and standardized CDS compared with the Etest as gold standard.

From this study, compared with Etest, the results of the standard disc diffusion method in accordance with CDS over the CLSI standard than three antibiotics, namely azithromycin (total agreement 96.7%), ceftriaxone (total agreement 80.0%) and penicillin (total agreement 73.3%) whereas the standard disc diffusion method according to CLSI more than CDS standard on the two antibiotics are ciprofloxacin (total agreement 73.3%) and spectinomycin (total agreement 73.3%). Neisseria gonorrhoeae patterns of sensitivity to antibiotics in RSCM and health care networks by disc diffusion method that best suits the Etest are with the standard CDS obtained azithromycin 86,7%, ceftriaxone 76.7%, penicillin 16,7% and with the CLSI standards obtained ciprofloxacin 0% and spektinomisin 70%. Neisseria gonorrhoeae pattern of sensitivity to cefixime is 46.7 % which is only tested with the CLSI standard. Cefixime and ceftriaxone as the drug of choice for gonorrhea should be given prudently to prevent the occurrence of resistance more extensive."