Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
Potensi CuBi2O4 sebagai fotokatoda telah banyak dikembangkan sebagai salah satu material yang menjanjikan dalam bidang fotoelektrokimia, salah satunya pada aplikasi pemecahan air dan fotoreduksi CO2. Pada penelitian ini, telah dilakukan sintesis CuBi2O4 dengan variasi campuran pelarut (air:etanol, air:etilena glikol, air:gliserol), rasio pelarut (3:7, 7:3, 1:1), serta suhu reaksi (40o, 50o, 70o, 80o). Pengaruh dari masing-masing variabel sintesis ditentukan terhadap CuBi2O4 yang dihasilkan. Karakteristik CuBi2O4 yang dihasilkan dianalisis menggunakan difraksi sinar–x (XRD), scanning electron microscope (SEM), analisis Bruenauer-Emmet-Teller (BET), spektrospkopi reflektansi difui (DRS) UV-Vis, dan spektroskopi fotoluminesensi. Kemudian, dilakukan pula pengukuran fotoelektrokimia dari material yang dihasilkan pada tiap variasi sintesis menggunakan teknik chopped linear sweep voltammetry. Pengukuran tersebut dilakukan, untuk menentukan kondisi optimum sintesis dalam memperoleh material yang diinginkan. ......The potential of CuBi2O4 as a photocathode has been widely developed as one of the promising material in the field of photoelectrochemistry such as for water splitting and CO2 photoreduction applications. In this study, the synthesis of CuBi2O4 has been carried out with variation of solvent misture (water:ethanol, water:ethylene glycol, water:glycerol), solvent ratio (3:7, 7:3, 1:1), and reaction temperature (40oC, 50oC, 70oC, 80oC). The effect of each synthesis variable was determined on the CuBi2O4 produced. The characteristics of CuBi2O4 were analyzed using x-ray diffraction (XRD), scanning electron microscope (SEM), Brunauer-Emmet-Teller’s analysis (BET), difuse reflectance spectroscopy (DRS) UV-Vis, and photoluminescence (PL) spectroscopy. Then, photoelectrochemical measurment of the material produced in each synthesis variation were carried out using the chopped linear sweep voltammetry technique. The purpose is to determine the optimum condition of synthesis in obtaining the desired material.

Abstrak :
Limbah zat warna merupakan salah satu kontributor terbesar dalam terjadinya polusi air. Degradasi limbah zat warna menggunakan suatu fotokatalis perlu dilakukan untuk menangani permasalahan limbah tersebut. CuBi2O4 dan CuO merupakan suatu semikonduktor tipe-p berbasis oksida logam yang memiliki celah pita sempit, menunjukkan respons yang sangat baik terhadap cahaya tampak, dan dapat digunakan sebagai fotokatalis. Akan tetapi, kedua  material tersebut menunjukkan aktivitas fotokatalitik yang buruk akibat laju rekombinasi pasangan elektron dan hole yang cepat, sehingga sintesis material heterojunction dilakukan untuk mengatasi kekurangan ini. Komposit CuBi2O4/CuO disintesis dengan berbagai variasi rasio massa CuBi2O4:CuO (1:1, 1:2, dan 2:1) menggunakan metode grinding annealing. Lebih lanjut, CuBi2O4/CuO CuBi2O4, dan CuO yang dihasilkan kemudian dikarakterisasi menggunakan instrumen XRD, FTIR, UV-Vis DRS, dan TEM. CuBi2O4 dan CuO menunjukkan celah pita sebesar 1,76 eV dan 1,55 eV. Perubahan nilai energi celah pita teramati ketika modifikasi dilakukan, yakni 1,73 eV, 1,70 eV, dan 1,59 eV. Pengujian aktivitas fotokatalitik terhadap metilen biru di bawah cahaya tampak selama 180 menit menunjukkan bahwa sintesis CuBi2O4/CuO efisien dalam meningkatkan aktivitas fotokatalitiknya dengan persentase degradasi sebesar 81,1%. Sedangkan CuO dan CuBi2O4 masing-masing menunjukkan persentase degradasi sebesar 73,3% dan 64,2%. ......Dye waste is one of the biggest contributors to water pollution. Degradation of dye waste using a photocatalyst needs to be done to deal with this waste problem. CuBi2O4 and CuO are metal oxide-based p-type semiconductors that have a narrow band gap, responsive to visible light, and can be used as photocatalysts material. Synthesis of CuBi2O4 and CuO using solvothermal and hydrothermal methods was successfully carried out which was confirmed by XRD, FTIR, TEM, and UV-Vis DRS. CuBi2O4 and CuO show bandgap energy 1.76 eV and 1.55 eV, respectively. However, both materials exhibit poor photocatalytic performance due to the fast recombination rate of electron-hole pairs, so that the synthesis of heterojunction materials was carried out to overcome this deficiency. CuBi2O4/CuO composite was synthesis by grinding annealing method using various CuBi2O4:CuO mass ratios (1:1, 1:2, and 2:1). Furthermore, CuBi2O4/CuO composite were characterized using XRD, FTIR, UV-Vis DRS, and TEM. Changes in the value of the band gap energy observed when modifications were made to 1.73 eV, 1.70 eV and 1.59 eV. The heterojunction CuBi2O4/CuO showed an enhanced photocatalytic performance with 81,1% removal of methylene blue within 180 min of visible light irradiation, compared to the results obtained with the pristine materials. While CuO and CuBi2O4 only showed 73,3% and 64,2% removal of methylene blue within 180 min of visible light irradiation.

Abstrak :
Limbah zat warna dari industri tekstil dan garmen merupakan salah satu penyumbang kerusakan lingkungan perairan. Saat ini, metode fotokatalitik telah banyak diteliti untuk mendegradasi polutan zat warna. Penelitian ini telah berhasil mensintesa CuBi2O4 dan nanopartikel ZnO, serta CuBi2O4/ZnO. Komposit CuBi2O4/ZnO yang dihasilkan dari beberapa CuBi2O4: ZnO, 1:1 ; 2:1 dan 1:2 mempunyai energi celah pita sebesar 1,8 eV dan 3,02 eV ; 1,76 eV dan 2,97 eV ; 1,82 eV dan 3,10 eV masing-masing. Semua fotokatalis telah dikarakterisasi dengan FTIR, XRD, UV-DRS dan TEM, serta telah diaplikasikan pada degradasi zat warna metilen biru. Fotokatalis CuBi2O4/ZnO (1:2) menghasilkan degradasi metilen biru yang terbesar, 78,88% dibandingkan dengan lainnya ......Dye waste from the textile and garment industry is one of the contributors to damage to the aquatic environment. Currently, photocatalytic methods have been widely studied to degrade dye pollutants. This research succeeded in synthesizing CuBi2O4 and ZnO nanoparticles, as well as CuBi2O4/ZnO composites. CuBi2O4/ZnO composites produced from several ratios of CuBi2O4 : ZnO, 1:1 ; 2:1 and 1:2 have band gap energies of 1.80 eV and 3.02 eV ; 1.76 eV and 2.97 eV ; 1.82 eV and 3.10 eV respectively. All photocatalysts have been characterized by FTIR, XRD, UV DRS, SEM and TEM, and have been applied to the degradation of methylene blue dye. The CuBi2O4/ZnO nanocomposite with a ratio of 1:2 resulted in the greatest degradation of methylene blue, 78.88% compared to other nanocomposites.

Abstrak :
Penelitian ini telah berhasil menyintesis fotokatalis CuBi2O4 yang dimodifikasi dengan nanopartikel Co3O4 untuk mendegradasi zat warna Metilen Biru. Nanokomposit CuBi2O4/Co3O4 dibuat pada beberapa rasio CuBi2O4 dan Co3O4, yaitu 1:2, 1:1, dan 2:1. Semua produk nanokomposit CuBi2O4/Co3O4 telah dikarakterisasi dengan XRD, FTIR, UV-Vis DRS, dan TEM, dan juga diuji aktivitasnya dalam degradasi metilen biru. Pada jumlah 7,5 gram nanokomposit CuBi2O4/Co3O4 dengan rasio 1:2 dalam waktu paparan sinar tampak yang sama (180 menit), menghasilkan persen degradasi terbesar (58,53%) dibandingkan dengan nanokomposit lainnya. ......This research has succeeded in synthesizing CuBi2O4 photocatalyst modified with Co3O4 nanoparticles to degrade Methylene Blue dye. The CuBi2O4/Co3O4 nanocomposite was prepared at several ratios of CuBi2O4 and Co3O4, namely 1:2, 1:1, and 2:1. All CuBi2O4/Co3O4 nanocomposite products have been characterized by XRD, FTIR, UV-Vis DRS, TEM, and BET, and also tested for their activity in methylene blue degradation. At the amount of 7.5 grams of CuBi2O4/Co3O4 nanocomposite with a ratio of 1:2 in the same visible light exposure time (180 minutes), produced the largest percent degradation (58.53%) compared to other nanocomposites.

Abstrak :
Perkembangan sektor industri, khususnya industri tekstil, menyebabkan peningkatan pencemaran lingkungan perairan. Salah satu komponen utama dalam industri tekstil adalah zat warna seperti metilen biru. Metilen biru merupakan polutan organik yang dapat mencemari lingkungan. Degradasi metilen biru dapat dilakukan melalui proses fotokatalisis menggunakan semikonduktor berbasis oksida logam. CuBi2O4 adalah salah satu contoh semikonduktor tipe-p yang dapat digunakan sebagai fotokatalis. Namun, CuBi2O4 memiliki keterbatasan dalam melakukan degradasi metilen biru. Nanopartikel emas (AuNP) diketahui memiliki efek plasmonik yang dapat digunakan untuk meningkatkan efisiensi aktivitas fotokatalitik semikonduktor. Pada penelitian ini, dilakukan sintesis nanokomposit Au/CuBi2O4 dengan variasi rasio mol 1:1; 2:1; 1:2 melalui metode presipitasi-reduksi. Keberhasilan sintesis fotokatalis CuBi2O4 dan Au/CuBi2O4 diuji dengan karakterisasi XRD, TEM, FTIR, dan UV-Vis DRS. Energi celah pita CuBi2O4 adalah sebesar 1,75 eV dan Au/CuBi2O4 1:1, 2:1, dan 1:2 adalah sebesar 1,57 eV, 1,56 eV, dan 1,62 eV. Selanjutnya, CuBi2O4 dan Au/CuBi2O4 diuji aktivitas fotokatalitiknya dalam mendegradasi metilen biru selama 3 jam dalam daerah sinar tampak. Hasil pengujian menunjukkan Au/CuBi2O4 memiliki persentase degradasi sebesar 83,29% sedangkan CuBi2O4 sebesar 64,75%. ......The development of the industrial sector, particularly the textile industry, has led to an increase in water pollution. One of the main components in the textile industry is dyes such as methylene blue. Methylene blue is an organic pollutant that can contaminate the environment. The degradation of methylene blue can be achieved through photocatalysis using metal oxide-based semiconductors. CuBi2O4 is an example of a p-type semiconductor that can be used as a photocatalyst. However, CuBi2O4 has limitations in degrading methylene blue. Gold nanoparticles (AuNP) are known to have plasmonic effects that can be used to enhance the photocatalytic activity of semiconductors. In this study, Au/CuBi2O4 nanocomposites were synthesized with varying mole ratios of 1:1, 2:1, and 1:2 using the precipitation-reduction method. The successful synthesis of CuBi2O4 and Au/CuBi2O4 photocatalysts was tested through XRD, TEM, FTIR, and UV-Vis DRS characterizations. The band gap energy of CuBi2O4 was found to be 1.75 eV, while for Au/CuBi2O4 1:1, 2:1, and 1:2, it was 1.57 eV, 1.56 eV, and 1.62 eV, respectively. Furthermore, the photocatalytic activity of CuBi2O4 and Au/CuBi2O4 was tested in degrading methylene blue for 3 hours under visible light. The results showed that Au/CuBi2O4 achieved a degradation percentage of 83.29%, while CuBi2O4 achieved 64.75%.

Abstrak :
Karbon dioksida (CO2) merupakan gas rumah kaca yang berperan penting dalam peningkatan suhu bumi yang memicu terjadinya pemanasan global. Untuk mengurangi konsentrasi CO2, harus dilakukan konversi CO2 menjadi produk yang memiliki nilai tambah. Pada penelitian ini, metode fotoelektrokimia digunakan untuk mengkonversi CO2 dalam bentuk bikarbonat menggunakan fotokatoda CuBi2O4 yang telah dimodifikasi dengan nanopartikel perak. CuBi2O4 disintesis dengan metode solvotermal dan nanopartikel perak disintesis dengan menggunakan kompleks asam tanat dan natrium sitrat. Fabrikasi fotokatoda dilakukan menggunakan metode doctor blade pada FTO 1x1 cm2. Fotokatoda dimodifikasi menggunakan nanopartikel perak dengan variasi waktu pencelupan yaitu 10s, 30s, dan 50s. Berdasarkan karakterisasi UV-Vis DRS, energi celah pita FTO/CBO (1,77 eV) menurun setelah dimodifikasi dengan nanopartikel perak menjadi 1,71 eV. Hal ini menunjukkan bahwa modifikasi nanopartikel perak dapat memengaruhi sifat elektronik dari semikonduktor CuBi2O4. Pengujian fotoelektrokimia dilakukan dengan sistem tiga elektroda dengan metode linear sweep voltammetry (LSV) dan chronoamperometry (transient chopped light photocurrent) selama 120 detik dengan mati nyala lampu setiap 10 detik. Didapatkan fotokatoda FTO/CBO/Ag 30s memiliki performa yang paling baik, yaitu memiliki onset potensial sebesar -0,008 V, densitas arus sebesar -12,859 mA/cm2 dengan stabilitas foto arus tertinggi yaitu 84,4%. ......Carbon dioxide (CO2) is a greenhouse gases that has an important role in increasing the average temperature of the earth which triggers global warming. In order to reduce the concentration of CO2, it is necessary to convert CO2 into other products that have added value. In this experiment, a photoelectrochemical method was used to convert CO2 in the form of bicarbonate into formic acid using CuBi2O4 photocathode that had been modified with silver nanoparticles. CuBi2O4 was synthesized by solvotermal method and silver nanoparticles were synthesized using a complex of tannic acid and sodium citrate. Fabrication of photocathode was carried out using the doctor blade method with FTO 1x1 cm2. The photocathode was modified using silver nanoparticles with variations in immersion time of 10s, 30s, dan 50s. Based on the UV-Vis DRS characterization, band gap energies of FTO/CBO (1.77 eV) decreased after being modified with silver nanoparticles to 1.71 eV. This data indicates that the modification of silver nanoparticles can affect the electronic properties of the CuBi2O4 semiconductor. Photoelectrochemical testing was carried out with a three-electrode system with linear sweep voltammetry and chronoamperometry (transient chopped light photocurrent) methode for 120 seconds with chopped light every 10 seconds. It was found that the FTO/CBO/Ag 30s photocathode has the best performance, which has an onset potential of -0.008 V, a current density of -12,859 mA/cm2 with the photocurrent stability of 84.4%.

Abstrak :
Gas karbon dioksida (CO2) merupakan penyumbang utama gas rumah kaca di atmosfer yang berpotensi besar sebagai penyebab pemanasan global. Adanya Sel Fotoelektrokimia (PEC, Photoelectrochemical cells) yang digunakan untuk reaksi reduksi dapat diterapkan dalam konversi CO2 menjadi senyawa yang bernilai. Penelitian ini telah berhasil mensintesis nanopartikel AuAg dan nanopartikel CuBi2O4 (CBO), serta nanokomposit CuBi2O4/AuAg. Semua material telah dikarakterisasi dengan XRD, spektroskopi UV-Vis, dan UV-Vis DRS. Fotokatoda FTO/CuBi2O4 untuk sel fotoelektrokimia, berhasil dibentuk menggunakan metode doctor blade dan preparasi FTO/CuBi2O4/AuAg dilakukan dengan cara mencelupkan FTO/CuBi2O4 ke dalam larutan nanopartikel AuAg dengan variasi waktu pencelupan selama 10 detik, 30 detik, dan 50 detik. Fotokatoda FTO/CuBi2O4/AuAg pada perendaman 50 detik memberikan nilai potensial onset paling positif sebesar -0,038 V dan stabilitas arus foto sebesar 73,33%. Hasil uji seluruh produk Fotokatoda, dengan sistem fotoelektrokimia menggunakan Linear Sweep Voltammetry (LSV), didapatkan bahwa Fotokatoda FTO/ CuBi2O4/AuAg 50s memberikan kinerja arus katodik terbaik dalam reaksi reduksi untuk konversi ion bikarbonat dalam sistem PEC. Namun, pada pengujian Chronoamperometry, FTO/ CuBi2O4/AuAg 30s menghasilkan stabilitas foto arus terbaik mencapai 82.56%. ......Carbon dioxide (CO2) gas is the main contributor to greenhouse gases in the atmosphere, which is most likely the cause of global warming. The existence of Photoelectrochemical Cells (PEC) is used for reduction reactions and it can be applied in the conversion of CO2 into valuable compounds. This research has succeeded in synthesizing AuAg nanoparticles, CuBi2O4 (CBO) nanoparticles, and CuBi2O4/AuAg nanocomposites. All materials were characterized by XRD, UV-Vis spectroscopy, and UV-Vis DRS. The FTO/CuBi2O4 photocathode for photoelectrochemical cells was successfully formed using the doctor blade method and the FTO/CuBi2O4/AuAg preparation was carried out by dipping FTO/CuBi2O4 into a solution of AuAg nanoparticles with variations in immersion time of 10 seconds, 30 seconds, and 50 seconds. Photocathode FTO/CuBi2O4/AuAg immersion for 50 seconds gave the most positive onset potential value of -0.038 V and the photo current stability was 73.33%. The test results of all photocathode products, with a photoelectrochemical system using Linear Sweep Voltammetry (LSV), it was found that the FTO/CuBi2O4/AuAg 50s photocathode gave the best cathodic current performance in the reduction reaction for the conversion of bicarbonate ions in the PEC system. However, in Chronoamperometry, FTO/CuBi2O4/AuAg 30s produced the best photo current stability of 82.56%.

Abstrak :
Metilen biru merupakan pewarna organik berbahaya dari limbah industri tekstil yang menyebabkan permasalahan lingkungan yang serius. Degradasi metilen biru dapat dilakukan melalui proses fotokatalisis dengan semikonduktor berbasis oksida logam seperti NiO dan CuBi2O4. Pada penelitian ini, NiO disintesis melalui metode sol-gel, sedangkan CuBi2O4 disintesis melalui metode solvotermal. Nanokomposit NiO/CuBi2O4 telah berhasil dikembangkan dengan memodifikasi NiO dan CuBi2O4 melalui metode grinding-annealing, yang dikonfirmasi oleh hasil karakterisasi XRD, FTIR, TEM, dan UV-Vis DRS. Penurunan nilai energi celah pita NiO dari 3,39 eV akibat keberadaan CuBi2O4 dapat diamati. Energi celah pita NiO pada NiO/CuBi2O4 1:1, 1:2, dan 2:1 yang diperoleh dari hasil karakterisasi UV-Vis DRS adalah 2,95 eV, 2,89 eV, dan 3,15 eV. Selain itu, aktivitas fotokatalitik NiO, CuBi2O4, dan NiO/CuBi2O4 sebagai katalis juga dievaluasi melalui degradasi metilen biru di bawah radiasi sinar tampak selama 3 jam. Hasil menunjukkan bahwa modifikasi NiO dengan CuBi2O4 dapat meningkatkan aktivitas fotokatalitik. Persentase fotodegradasi metilen biru dengan 10 mg katalis NiO/CuBi2O4 2:1 adalah 74,12% dengan konstanta laju sebesar 6,07×10–3 menit–1, yang lebih tinggi dibandingkan NiO dan CuBi2O4 tanpa modifikasi ......Methylene blue is a hazardous organic dye from textile industrial effluents which causes serious environmental problems. Degradation of methylene blue could be carried out through photocatalysis process using metal oxide-based semiconductors such as NiO and CuBi2O4. In this study, NiO was synthesized by sol-gel method, while CuBi2O4 was synthesized by solvothermal method. NiO/CuBi2O4 nanocomposite was successfully developed by modifying NiO and CuBi2O4 through grinding-annealing method, which was confirmed by the results of XRD, FTIR, TEM, and UV-Vis DRS characterization. The decrease in bandgap energy value of NiO from 3.39 eV due to the presence of CuBi2O4 could be observed. The bandgap energies of NiO in NiO/CuBi2O4 1:1, 1:2, and 2:1 obtained from the results of UV-Vis DRS characterization were 2.95 eV, 2.89 eV, and 3.15 eV. Furthermore, the photocatalytic activity of NiO, CuBi2O4, and NiO/CuBi2O4 as catalysts were also evaluated by methylene blue degradation under visible light irradiation for 3 hours. The results showed that modification NiO with CuBi2O4 could enhance the photocatalytic activity. The percentage of methylene blue photodegradation using 10 mg NiO/CuBi2O4 2:1 catalyst was 74.12% with a rate constant of 6.07×10–3 min–1, which was higher than NiO and CuBi2O4 without modification.

Abstrak :
Industri tekstil merupakan penyumbang terbesar limbah zat warna ke dalam air, contohnya zat warna metilen biru yang bersifat racun, karsinogenik, dan tidak dapat terurai secara alami. Salah satu teknik mengurangi kadar metilen biru adalah melalui degradasi secara fotokatalitik dengan menggunakan semikonduktor. CuBi2O4 merupakan semikonduktor tipe-p dengan celah pita yang sempit (1,5 – 1,8 eV) dapat digunakan sebagai fotokatalis untuk degradasi metilen biru karena memiliki respon cahaya tampak. Penambahan logam mulia Paladium (Pd) dapat meningkatkan kinerja aktivitas fotokatalitik CuBi2O4 karena dapat menekan rekombinasi pasangan e− dan h+. Penelitian ini, telah berhasil mensintesis CuBi2O4 melalui metode solvotermal, dan mensintesis nanokomposit Pd/CuBi2O4 dengan variasi perbandingan rasio mol Pd:CuBi2O4 (1:1, 1:2, dan 2:1) melalui metode presipitasi dan reduksi. CuBi2O4 dan Pd/CuBi2O4 hasil sintesis telah dibuktikan melalui karakterisasi dengan XRD, TEM, FTIR, dan UV-Vis DRS. Uji sifat katalis dilakukan pada larutan Metilen Biru dengan variasi penambahan massa katalis sebesar 5 mg, 10 mg, dan 15 mg, serta variasi kondisi (fotolisis dan adsorpsi). Persentase degradasi metilen biru paling optimum adalah pada katalis Pd/CuBi2O4 (2:1) 10 mg, yaitu sebesar 82,63% dengan laju degradasi 8,9 × 10-3 min-1. ......Textile industry is the largest contributor of colorant waste into water, for instance, the toxic, carcinogenic, and non-biodegradable dye methylene blue. One of the techniques to reduce the concentration of methylene blue is through photocatalytic degradation using a semiconductor. CuBi2O4 is a p-type semiconductor with a narrow bandgap (1.5 - 1.8 eV) that can be utilized as a photocatalyst for methylene blue degradation due to its visible light response. The addition of the noble metal Palladium (Pd) can enhance the photocatalytic activity of CuBi2O4 by suppressing the recombination of electron-hole pairs (e− dan h+). In this research, CuBi2O4 has been successfully synthesized through the solvothermal method, and Pd/CuBi2O4 nanocomposites have been synthesized with various ratios of Pd:CuBi2O4 (1:1, 1:2, and 2:1) using the precipitation and reduction method. CuBi2O4 and Pd/CuBi2O4 synthesized products have been characterized using XRD, TEM, FTIR, and UV-Vis DRS. The catalytic properties test was performed on Methylene Blue solutions with varying catalyst masses of 5 mg, 10 mg, and 15 mg, as well as different conditions (photolysis and adsorption). The optimum percentage of methylene blue degradation was observed with the catalyst Pd/CuBi2O4 (2:1) 10 mg, which was 82.63%, with a degradation rate of 8,9 × 10-3 min-1.

Abstrak :
Seiring dengan pertambahan penduduk, kebutuhan akan energi terus meningkat. Salah satu cara yang dapat dilakukan adalah dengan fotoelektroreduksi CO2 menjadi bahan kimia yang berguna sebagai sumber energi terbarukan menggunakan bantuan cahaya matahari. Material CuBi2O4 dapat menjadi fotokatalis sinar tampak yang baik karena celah pitanya relatif sempit, yaitu sekitar 1,5-1,8 eV. Pada penelitian ini telah berhasil disintesis material CuBi2O4 dengan metode drop-casting dan solvotermal. Strukur kristal CuBi2O4 yang disintesis adalah tetragonal (kusachiite). Energi celah pita yang diperoleh adalah berkisar dari 1,5 hingga 1,8 eV. Hasil CuBi2O4 metode drop-casting tidak 100% murni karena ditandai dengan munculnya puncak milik Bi2O3 pada spektrum XRD. Hasil karakterisasi dengan SEM menunjukkan morfologi material yang dihasilkan membentuk struktur seperti jaringan yang terhubung satu sama lain. Karakterisasi dengan TEM menunjukkan bahwa material kristal yang disintesis adalah polikristalin. Hasil CuBi2O4 metode solvotermal menghasilkan material dengan kemurnian tinggi yang ditunjukkan dari hasil spektrum XRD. Intensitas yang tinggi pada sudut 2θ 27,97o menunjukkan material cenderung tumbuh ke arah bidang 211. Modifikasi FTO/CuBi2O4 dengan bismuth melalui elektrodeposisi menunjukkan hasil yang tidak bagus karena menyebabkan kristal CuBi2O4 terdegradasi. Hal ini dapat dilihat pada difraktogram yang menunjukkan terjadinya penurunan puncak khas dari CuBi2O4. ......As the population grows, energy demand will continue to increase. One way to solve this problem is by converting CO2 into chemicals that are useful as a source of renewable energy. CuBi2O4 material is a good visible light photocatalyst because the band gap is relatively narrow, which is about 1.5-1.8 eV. In addition, previous studies have shown that bismuth exhibits high performance in reducing CO2 to formate with excellent selectivity. In this research, CuBi2O4 material has been successfully synthesized by drop-casting and solvothermal methods. The crystal structure of CuBi2O4 is tetragonal (kusachiite). The bandgap energy of the material is about 1.5 to 1.8 eV. The results of CuBi2O4 by drop-casting method has low purity because the diffractogram showed a peak belonging to Bi2O3. The SEM images showed the morphology of the resulting material forms a network-like structure. Characterization by TEM showed that the material is polycrystalline. The solvothermal method CuBi2O4 results in high purity materials. The highest peak at 27.97o indicates that the material tends to grow along 211 direction. The modification of FTO/CuBi2O4 with bismuth through electrodeposition method showed poor results because it causes the CuBi2O4 crystal lost its structure. This can be seen on the diffractogram data which shows a significant decrease in the typical peak of CuBi2O4.