Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
As a result of waterflooding, inorganic salt precipitation occurs in the different parts of an oil production system, thereby leading to damage of production equipment. Different parameters affect the kinetics of salt precipitation. Scale inhibitors are widely used to prevent inorganic salt formation. In this study, the effect of reservoir pressure, temperature, and mixing ratio of injection to formation water on calcium sulfate and barium sulfate precipitation was investigated. For this purpose, two different formation waters and one injection water were used. In addition, the effect of temperature and mixing ratio on inhibition performance was studied. Four different existing industrial scale inhibitors and one new scale inhibitor were used. The performance of the scale inhibitors was determined under static and dynamic conditions. Results of the study showed that calcium sulfate precipitation increased with an increase in temperature and a decrease in pressure. Barium sulfate precipitation was found to increase with a decrease in the temperature. The effect of pressure on barium sulfate formation was negligible. The developed scale inhibitor showed the highest performance for the prevention of calcium sulfate and barium sulfate formation. A change in temperature from 60°C to 120°C reduced the inhibitor performance by 3%. In the cases of calcium sulfate and barium sulfate, the minimum performance of the scale inhibitor was observed when the mixing ratios of injection to formation waters were 60:40 and 50:50, respectively.

Abstrak :
As a result of waterflooding, inorganic salt precipitation occurs in the different parts of an oil production system, thereby leading to damage of production equipment. Different parameters affect the kinetics of salt precipitation. Scale inhibitors are widely used to prevent inorganic salt formation. In this study, the effect of reservoir pressure, temperature, and mixing ratio of injection to formation water on calcium sulfate and barium sulfate precipitation was investigated. For this purpose, two different formation waters and one injection water were used. In addition, the effect of temperature and mixing ratio on inhibition performance was studied. Four different existing industrial scale inhibitors and one new scale inhibitor were used. The performance of the scale inhibitors was determined under static and dynamic conditions. Results of the study showed that calcium sulfate precipitation increased with an increase in temperature and a decrease in pressure. Barium sulfate precipitation was found to increase with a decrease in the temperature. The effect of pressure on barium sulfate formation was negligible. The developed scale inhibitor showed the highest performance for the prevention of calcium sulfate and barium sulfate formation. A change in temperature from 60°C to 120°C reduced the inhibitor performance by 3%. In the cases of calcium sulfate and barium sulfate, the minimum performance of the scale inhibitor was observed when the mixing ratios of injection to formation waters were 60:40 and 50:50, respectively.

Abstrak :
Telah dilakukan penelitian untuk mengetahui pengaruh air formasi berinhibitor terhadap perilaku korosi dan laju korosi baja API 5L Grade B. Metode yang digunakan yaitu Weight loss dan Polarisasi Potensiodinamik. Uji celup dilakukan dengan variasi waktu 8, 11, dan 14 hari. Hasil penelitian menunjukkan bahwa kondisi baja API 5L dalam larutan air formasi berinhibitor mengalami pemasifan dan laju korosi semakin menurun seiring pertambahan waktu. Hasil pengujian XRD menunjukkan bahwa produk korosi yang dihasilkan adalah Fe3O4. ......A research has been conducted to know the influences formation water with presence of inhibitor to the corrosion behaviour and corrosion rate API 5L Grade B steel. Weight loss and Potentiodynamic Polarization methodology has been carried out. An immersion test with various time 8,11, and 14 days has been done. This research has show that passivity happened and the corrosion rate has decreased as the increased of time. The corrosion product of Fe3O4 has been known as the result of XRD test.