Abstrak :
Hidrogel poli([3-((2-(metakriloiloksi)etil)dimetilammonia) propana-1-sulfonat-ko-N-isopropilakrilamida) (P(SPE-ko-NIPAM)) memiliki responsivitas terhadap temperatur yang dimodifikasi dari dua tipe polimer berbeda yaitu bertipe LSCT dan UCST, dengan tujuan sebagai bahan penghantar aktif farmasi. Hidrogel P(SPE-ko-NIPAM) berhasil disintesis melalui metode polimerisasi radikal bebas menggunakan ammonium persulfat (APS) sebagai inisiator dan N-N’ metilenebisakrilamida (MBA) sebagai agen pengikat silang. Keberhasilan sintesis hidrogel P(SPE-ko-NIPAM) dibuktikan menggunakan fourier transform infrared (FTIR) yang ditandai dengan hilangnya puncak serapan C=C vinil. Nilai gel content menunjukkan bahwa hidrogel dengan komposisi 20 mol% SPE memiliki gel content paling kecil dan nilai gel content pada variasi waktu polimerisasi meningkat seiring dengan semakin lama waktu polimerisasi. Hasil uji responsivitas hidrogel P(SPE-ko-NIPAM) terhadap temperatur dipengaruhi oleh komposisi PSPE dan PNIPAM. Pengaruh waktu polimerisasi terhadap responsivitas temperatur yaitu semakin lama waktu polimerisasi akan menurunkan rasio kesetimbangan swelling (ESR), dan waktu polimerisasi tidak memberikan pengaruh terhadap nilai Tc. Hasil uji kinetika deswelling, bertambahnya komposisi SPE dan semakin lama waktu polimerisasi memiliki laju deswelling paling lambat. Berdasarkan uji swelling di berbagai temperatur menunjukkan bawah ESR terbesar dimiliki oleh hidrogel P(SPE20-ko-NIPAM80) dengan waktu polimerisasi 1 jam. Didapatkan hidrogel P(SPE20-ko-NIPAM80) memiliki kemampuan menjebak 2,75% dan mampu melepaskan 26,33% metformin-HCl dalam buffer pH 7,4 pada temperatur 37?C dalam rentang waktu selama 15 jam. ......Poly([3-((2-(methacryloyloxy)ethyl)dimethylammonio))propane-1-sulfonate-co-N isopropylacrylamide) (P(SPE-co-NIPAM)) hydrogels with temperature responsive properties modify of two different polymer types, namely the LSCT and UCST types, to be active pharmaceutical carrier materials. P(SPE-ko-NIPAM) hydrogel were synthesized by the mechanism of free-radical polymerization using ammonium persulfate (APS) as initiator and N-N' methylene bisacrylamide (MBA) as crosslinking agent. Hydrogel were characterized by using the Fourier Transform Infrared (FT-IR) and resulting in the nonappearance of C=C vinyl peak that indicates the polymerization process success. Gel content with a composition of 20 mol% SPE has the lowlest gel content and at various polymerization times increased with increasing polymerization time. The swelling test on several scales of temperature influenced by the composition of PSPE and PNIPAM. The effect of polymerization time on swelling test with several scales temperatureis ESR an increases with the polymerization time decrease, and polymerization time does not affect Tc value. Results of the rasio deswelling, an increase SPE composition and polymerization time have the slowest deswelling rate. The highest ESR results were obtained from hydrogel hydrogel P(SPE20-co-NIPAM80) with a polymerization time of 1 hour. Hydrogel P(SPE20-co-NIPAM80) was able to encapsulate 2.75% and the cumulative release 26.33% of metformin-HCl in buffer pH 7.4 at 37?C within 15 hours.

Abstrak :
Hidrogel semi-IPN merupakan suatu jaringan polimer yang memiliki kemampuan menyerap air yang besar dan cenderung mempertahankan strukturnya. Sintesis hidrogel kitosan-polistirena dengan metode semi-IPN dilakukan dengan dua tahap. Pada tahap pertama dibentuk jaringan kitosan terikat silang dengan menggunakan variasi agen pengikat silang yaitu, asetaldehida, formaldehida, dan glutaraldehida. Pada tahap kedua dilakukan polimerisasi polistirena di dalam jaringan kitosan terikat silang. Kondisi optimum dalam sintesis hidrogel kitosan-polistirena semi-IPN diperoleh dengan waktu reaksi polimerisasi polistirena selama 4 jam, komposisi kitosan dan stirena sebesar 80:20, dan agen pengikat silang asetaldehida. Pada kondisi optimum, hidrogel kitosan-polistirena semi-IPN memiliki sifat mekanik yang lebih baik dibandingkan dengan hidrogel kitosan dan mampu mempertahankan kemampuan swelling yang baik. Nilai rasio swelling dan derajat ikat silang hidrogel kitosan-polistirena semi-IPN pada kondisi optimum sebesar 751,2% dan 24,1% secara berurutan. Karakterisasi hidrogel kitosan-polistirena semi-IPN dilakukan dengan spektrofotometer Fourier Transform Infrared (FTIR), Differential Scanning Calorimetry (DSC), dan Scanning Electron Microscope (SEM).

---

Semi-IPN hydrogel is a polymer network that has a great ability to absorb water and tend to maintain its structure. Synthesis of hydrogel chitosan -polystyrene by semi-IPN method performed by two steps. First step, chitosan crosslinked network formed by using a variety of crosslinking agents, namely acetaldehyde, formaldehyde, and glutaraldehyde. In the second step, polymerization polystyrene in chitosan crosslinked network. The optimum conditions in synthesis of chitosan hydrogel-polystyrene semi-IPN is obtained with a reaction time of polymerization of polystyrene for 4 hours, composition of chitosan and styrene is 80:20, and the crosslinking agent is acetaldehyde. At the optimum conditions, hydrogel chitosan- polystyrene semi-IPN has better mechanical properties compared with the chitosan hydrogel and able to maintain good swelling capability. The value of swelling ratio and the degree of crosslinking of hydrogel chitosan-polystyrene semi-IPN in optimum condition are 751.2% and 24.1%. Characterization of hydrogel chitosan-polystyrene semi-IPN has been done by Spectrophotometer Fourier Transform Infrared (FTIR), Differential Scanning Calorimetry (DSC), and Scanning Electron Microscope (SEM).

Abstrak :
In order to develop the applications of radiations for biomaterial preparation, a non - toxic superabsorbent has been sinthesized. A series of superbaorbent hydrogel were prepared from aqueous solution containing 5% polyethylene oxide (PEO) with different concertration of alginate (0,5-2.0%) were irradiated at the doses of 20,30 and 40 kGy by gamma radiation. The gel fraction, swelling kinetics and the equilibrium degree of swelling (EDS) of the hydrogels were studied. It was found that the incorporation of even 2 % alginate (sodium salt) increased the EDS of the hydrogels from 20 g to 320 g/g. At a dose of 20 kGy, PEO - alginat hydrogels with high gel fraction (-80%) and very high EDS (-30 g/g) were obtained. The hydrogels were also found to be sensitive to the ionic solution of NaCL. The PEO - alginate hydrogels could be considered as candidate biomaterials in health care.

Abstrak :
ABSTRAK
Today, the global industry has recognised and applied a principal of reverse osmosis process for many water desalination plants worldwide. It is knowingly to account to more than half of the world rsquo s capacity. However, such method comes at a disposable cost in providing a high level of pressure as driving force for the saline water to permeate through the semipermeable membrane for separation process before ultimately producing fresh and clean water as a final purpose. The energy source generally comes from non renewable energy such as coals and other fossil burning fuels which can severely damage the environments.This phenomena has led to researchers to search for a more efficient method for water purification, which is the forward osmosis. Instead of applying external pressure, a smart polymer hydrogel is used as a draw agent to absorb the saline water with large impurities, contains them and deswells while releasing a clean water. To get a better understanding of an optimum performance in forward osmosis, various parameter of the hydrogels are investigated by experimental approach with the aid of supporting literature review.Experimental works include hydrogel synthesis, forward osmosis testing and dewatering process. The increasing of water content were observed to decrease the average flux rate, whereas a higher NIPAM composition is desirable as they increase the water flux rate. Dewatering experiment resulted that by increasing the initial water content, NIPAM composition and temperature would increase the water recovery in the process.

---

ABSTRACT
Dalam situasi sekarang, industri global telah mengenal dan mengaplikasikan prinsip reverse osmosis untuk banyak pabrik yang mengerjakan proses desalinasi air. Proses ini diketahui untuk mencakup lebih dari setengah kapasitas bumi in. Tetapi, method tersebut diketahui untuk memakan biaya tinggi dalam penggunaan tekanan tinggi sebagai tenaga penggerak untuk membuat air garam dapat menembus membrane semipermeable dalam proses pemisahan sebelum akhirnya menghasilkan air bersih. Sumber energy untuk proses ini sering menggunakan energy yang tidak dapat diperbahurui seperti batu bara atau minyak fosil yang dapat merusak lingkungan.Fenomena ini telah menarik para peneliti untuk mencari metode yang lebih efisien dalam purifikasi air, seperti forward osmosis. Sebagai ganti dari penggunaan tekanan dari luar, smart polymer hydrogel menggunakan agen penarik draw agent untuk menghisap air garam dengan tingkat kemurnian yang kecil, lalu menahan komponen yang tidak murni itu di dalamnya dan melepas air bersih sebagai hasil prosesnya. Untuk pengertian lebih lanjut menganai performa optimum di proses osmosis ini, beberapa parameter hydrogel ini diteliti lebih lanjut dengan menggunakan eksperimen dan bantuan tinjauan pustaka.Proses eksperimen yang dikerjakan antara lain termasuk proses sinstesis hydrogel, percobaan forward dan proses pengeringan hydrogel. Observasi menunjukan bahwa kenaikan konten air di dalam hydrogel akan menurunkan rata ndash; rata tingkat flux air, sedangkan kenaikan komposisi NIPAM akan lebih diinginkan untuk kenaikan tingkat flux air. Proses pengeringan menunjukan bahwa kenaikan kadar air awal, komposisi NIPAM dan suhu akan meningkatkan tingkat flux air dalam proses.

Abstrak :
Ekstrak flavonoid yang terkandung didalam propolis telah terbukti dapat meningkatkan fungsi jantung pasca myocardial infarction (MI). Penelitian ini bertujuan untuk mempelajari pengaruh propolis terhadap karakteristik swelling, profil rilis, degradasi, dan toksisitas hidrogel polivinil alkohol (PVA)-gelatin untuk aplikasi perancah patch jantung. Perancah hidrogel PVA/gelatin difabrikasi menggunakan metode freeze thaw dengan penambahan propolis sebanyak 3%, 7%, dan 10%. Inkorporasi propolis didalam matriks hidrogel menyebabkan penurunan swelling ratio hidrogel menjadi sekitar 254%, 221% dan 190% saat penambahan propolis sebanyak 3%, 7%, dan 10% secara berurutan. Kemampuan swelling ini mampu menjadikan hidrogel sebagai sistem penghantar obat yang melepas propolis melalui mekanisme sustained released. Dalam durasi 6 jam, perancah hidrogel mampu melepas propolis sebanyak 4,30%, 4,86%, dan 5,68% seiring dengan meningkatnya kandungan propolis 3%, 7%, dan 10%.  Penambahan konsentrasi propolis terbukti memodifikasi laju degradasi hidrogel dimana seiring penambahan propolis, weight loss yang diamati semakin tinggi. Sampel dengan propolis 3%, 7%, dan 10% mengalami pengurangan berat sebanyak 31%, 41%, dan 48% secara berurutan. Degradasi yang terjadi pada hidrogel mengikuti mekanisme surface erosion sehingga memampukan patch terdegradasi dalam lingkungan biologis seiring perbaikan jaringan jantung. Hasil uji sitotoksisitas mendapati nilai viabilitas sel pada kadar propolis 3%, 7% dan 10%, adalah 77%, 94%, dan 80% secara berurutan.  Nilai viabilitas sel menunjukkan bahwa propolis tidak menghambat metabolisme sel HEK-293 dan tidak bersifat toksik. Penelitian ini menunjukkan propolis dapat dienkapsulasi ke dalam matriks hidrogel sebagai sistem penghantaran obat maupun sebagai perancah patch jantung yang berpotensi mempercepat regenerasi jaringan baru. ......Flavonoid extracts contained in propolis have been shown to improve heart function after myocardial infarction (MI). This study aims to study the effect of propolis on swelling characteristics, release profile, degradation, and toxicity of hydrogels made from polyvinyl alcohol (PVA)-gelatin for cardiac patch scaffold applications. The PVA/gelatin hydrogel scaffolds were fabricated using the freeze thaw method with the addition of 3%, 7% and 10% propolis. The incorporation of propolis in the hydrogel matrix led to a decrease in the swelling ratio of the hydrogel to around 254%, 221% and 190% when the concentration of propolis was 3%, 7% and 10% respectively. This swelling behavior turns the hydrogel into a drug delivery system that releases propolis through a sustained release mechanism. Within 6 hours, the hydrogel scaffolds were able to release 4.30%, 4.86%, and 5.68% of propolis as the propolis concentration increased by 3%, 7%, and 10%. The addition of propolis concentration has been shown to modify the hydrogel degradation rate as when propolis is added, the observed weight loss is higher. Samples with 3%, 7%, and 10% propolis experienced a weight reduction of 31%, 41%, and 48%, respectively. The degradation that occurs in the hydrogel follows the surface erosion mechanism so that it enables the patch to degrade in a biological environment as cardiac tissue repairs. Cytotoxicity test results found cell viability values at propolis levels of 3%, 7% and 10% were 77%, 94% and 80% respectively. This research shows that propolis can be incorporated into a hydrogel matrix as a drug delivery system or as a cardiac patch scaffold which has the potential to accelerate the regeneration of new tissue.

Abstrak :
Latar Belakang: Connective Tissue Graft (CTG) yang menjadi standar baku emas perawatan resesi gingiva memiliki tingkat kesulitan perawatan yang cukup tinggi, serta menimbulkan rasa cemas dan ketidaknyamanan pada pasien. Hidrogel gelatin banyak dikembangkan dalam bidang tissue engineering karena memiliki sifat yang menyerupai matriks ekstraseluler jaringan tubuh. Hidrogel gelatin masih memiliki kekurangan dalam hal sifat mekanisnya, sehingga perlu dilakukan crosslinking secara kimia untuk meningkatkan potensinya sebagai scaffold regenerasi gingiva. Tujuan: Mengevaluasi efek agen crosslinker EDC pada hidrogel gelatin sebagai scaffold regenerasi gingiva. Metode: Pembuatan hidrogel gelatin dilakukan menggunakan bubuk gelatin bovine, sedangkan agen crosslinker yang digunakan adalah 1-(3-dimethylaminopropyl)-3’-ethylcarbodiimide hydrochloride (EDC) yang dikominasikan dengan N-hydroxysuccinimide (NHS). Uji porositas, swelling, dan biodegradasi dilakukan secara in-vitro dan ditriplikasi. Hasil: Penambahan agen crosslinker EDC menurunkan nilai porositas hidrogel gelatin menjadi 89,52%, menurunkan laju swelling, serta menahan biodegradasi hidrogel gelatin menjadi 92,43% pada hari ke-14. Kesimpulan: Agen crosslinker EDC memiliki efek yang dapat membuat struktur serta sifat mekanis scaffold menjadi lebih ideal untuk digunakan sebagai agen regenerasi gingiva. ......Background: Connctive Tissue Graft (CTG), the gold standard treatment for gingival recession, often results in increased patient morbidity. Gelatin-based hydrogel has been extensively explored as a biomaterial for tissue engineering, mimicking the extracellular matrix of host tissue. However, the mechanical strength of this biomaterial requires enhancement to make it an ideal scaffold for gingival regeneration. Aim: Evaluate the effect of EDC as crosslinking agents on gelatin-based hydrogel as a scaffold for gingival regeneration. Methods: Gelatin hydrogels were prepared using bovine gelatin powder, and the crosslinker composed of a combination of 1-(3-dimethylaminopropyl)-3'-ethylcarbodiimide hydrochloride (EDC) and N-hydroxysuccinimide (NHS). In-vitro tests, such as porosity, swelling, and biodegradation, were conducted in triplicate for all samples. Results: Gelatin hydrogels with added EDC as crosslinking agents showed a reduction of porosity by 89.52% (p<0.05), decrease in swelling ratio (p<0.05), and retained hydrogel biodegradation rate to 92,43% (p<0.05) on day-14th. Conclusion: EDC demonstrated the ability to improve the structural and mechanical strength of the scaffold, making it more suitable as a gingival regenerative agent.

Abstrak :
ABSTRACT
Oil palm is an oil plant which is of great importance for both the Thai and the world economies. Oil palm trees have a life span of approximately 20-25 years before a gradual erosion of yield sets in. Oil palm trunk (OPT) is an agricultural residue waste from oil palm re-plantation which is rich in cellulose but utilized ineffectively. One way for OPT utilization is cellulose hydrogel production. In this study, cellulose hydrogel was prepared by dissolving cellulose from OPT with 7% (w/v) of lithium chloride in dimethylacetamide (LiCl/DMAc) to create a porous hydrogel by 1, 3, 5, 8 and 10% (w/v) of (NH4)2SO4 for 3, 5 and 10 minutes. After that, it was found that soaking cellulose hydrogel in 8% (w/v) of (NH4)2SO4 solution for 5 minutes created light-browed cellulose hydrogel with an average Shore A hardness of 41 ± 1.13 and a maximum swelling equal to 90%. The chemical functional group and cross-section morphology of cellulose hydrogel were determined using Attenuated total reflectance - Fourier transform infrared spectroscopy (ATR-FTIR) and Scanning electron microscopy (SEM), respectively.

Abstrak :
Pada penelitian kali ini dibuat sistem pengantar obat mengapung dengan sediaan hidrogel kitosan poli N-vinil pirrolidon dengan komposisi Kitosan : monomer PVP 70:30 dan agen pengikat silang formaldehida 2 . Kemudian menggunakan dua jenis agen pembentuk pori yaitu kalium karbonat K2CO3 dan kalium bikarbonat KHCO3 konsentrasi divariasikan dengan persentasi 0 , 1 , 2,5 , 5 , dan 7,5 terhadap massa total reagen awal. Parameter keberhasilan dari penelitian ini adalah didapatkan data kondisi optimum dari mikrokapsul yang disintesis berupa floating lag time waktu mikrokapsul untuk mencapai ke permukaan yang cepat, floating time waktu mikrokapsul mengapung yang panjang, persentase obat ter-loading yang banyak ke dalam hidrogel kitosan serta pelepasan obat yang terkontrol. Karakterisasi yang digunakan adalah FTIR untuk mengetahui perubahan gugus fungsi dan Mikroskop Stereo Optik untuk melihat morfologi permukaan sampel hidrogel dan mikrokapsul. Konsentrasi optimum yang diperoleh berdasarkan hasil pengujian yaitu hidrogel dengan agen pembentuk pori KHCO3 7,5 dengan floating lag time 14 menit 2 detik, floating time > 3 jam, efisiensi enkapsulasi amoksisilin trihidrat sebesar 86 dan disolusinya mampu hingga 100.

---

This research was releated the preparation of Floating Drug Delivery System, consisted of hydrogel chitosan poly N vinyl pyrrolidone with compositions chitosan PVP monomer 70 30 and used formaldehida 2 as crosslinking agent. Two kinds of pore forming agent were used in this research which were potassium carbonate K2CO3 and potassium bicarbonate KHCO3 with variation of concentrations 0 , 1 , 2.5 , 5 , and 7.5 to the total mass of initial reagents. The success of this research depends on the fast floating lag time and the longest floating time, as much as the percentage of the drug amoxycillin loading in the hydrogel and controlled drug release. FTIR characterization was used to analyzes the changes of functional groups. Microscope Stereo Optical was used to identify the morphology of hydrogel and microcapsules. The best result showed that KHCO3 7,5 produced hydrogel which have floating lag time 14 minutes 2 seconds, floating time 3 hours, 86 encapsulation efficiency of amoxycillin trihydrate and dissolution capable up to 100.

Abstrak :
ABSTRACT
Pengobatan tuberkulosis tulang saat ini berupa konsumsi obat oral selama 6 bulan setelah operasi, dimana hal itu menjadi beban berat bagi pasien, menimbulkan efek negatif terhadap hati, dan membuat bakteri kebal terhadap obat. Sistem pelepasan lambat menjadi cara untuk meminimalkan dosis dan mengurangi dampak akibat konsumsi obat tuberkulosis, salah satunya dengan hidrogel polyvinyl alcohol PVA, polimer sintetis yang hidrofilik, biodegradable, non-toksik, dan biokompatibel. Penelitian ini bertujuan untuk mengetahui pengaruh penambahan kitosan dan konsentrasi penaut-silang sodium tripolifosfat terhadap efisiensi pemuatan obat dan profil pelepasan obat dari hidrogel PVA, serta mengetahui formulasi yang paling baik. Preparasi sampel dilakukan dengan metode casting/penguapan pelarut, dengan karakterisasi SEM Scanning Electron Microscopy, XRD X-Ray Diffraction, uji efisiensi pemuatan obat, dan uji pelepasan obat dalam larutan PBS phospate buffer solution pH 7,4. Secara keseluruhan, penambahan kitosan menurunkan efisiensi pemuatan obat dan menurunkan laju pelepasan obat. Penambahan sodium tripolifosfat meningkatkan efisiensi pemuatan obat hingga batas tertentu, memperlambat laju pelepasan obat, dan menurunkan jumlah obat yang dilepas. Sehingga untuk mendapatkan matriks dengan efisiensi pemuatan obat maksimal, formulasi tanpakitosana dalah yang terbaik, sedangkan profil pelepasan obat yang paling cocok untuk pengobatan TBC adalah formulasi dengan 40 kitosan dengan 4 sodium tripolifosfat.

---

ABSTRACT
Current osteoarticular tuberculosis treatment is an oral consumption of drug for 6 months after surgery, causing patient rsquo s inconvenience, liver damage, and potential drug resistent bacteria. Controlled drug release is a way for minimizing drug doses and reduce negative effect from tuberculosis drug consumption, such as polyvinyl alcohol PVA hydrogel, a hydrophilic, biodegradable, non toxic, and biocompatible synthetic polymer. This researchs aim is to find out the effect of chitosan addition and the concentration of sodium tripolyphosphate crosslinker to drug loading efficiency and drug release profile from PVA hydrogel. The method used is casting solvent evaporation method, characterized by SEM Scanning Electron Microscopy, XRD X Ray Diffraction, drug loading efficiency test, and drug release test in PBS phospate buffer solution pH of 7,4. The result of this research shows that chitosan addition will decrease drug loading efficiency. Increasing sodium tipolyphosphate concentration will increase drug loading efficiency until certain concentration, decrease the rate of drug release profile and decrease the amount of drugs being released. Therefore, to get a polymeric matrix with high drug loading efficiency, 0 chitosan formulation is the best, and for the highest drug release, formulation of 40 chitosan with 4 sodium tripolyphosphate is chosen.

Abstrak :
Pada penelitian ini, telah berhasil dilakukan sintesis hidrogel nanokomposit NaAlg-PVA-g-AAm termodifikasi nanopartikel ZnO dengan pembentukan ZnO secara in situ di dalam matriks hidrogel dengan metode hidrotermal. Karakteristik hidrogel diamati dengan FTIR, SEM, TEM, EDX, XRD, AAS serta kapasitas swelling-nya. Hidrogel NaAlg-PVA-g-AAm dengan kapasitas swelling terbaik disintesis didapatkan dengan menambahkan PVA dan alginat dengan perbandingan massa sebesar 0,6:3. Hidrogel nanokomposit setelah dimodifikasi dengan ZnO memiliki kapasitas swelling yang lebih tinggi dibandingkan hidrogel yang belum dimodifikasi. Didapatkan hasil untuk hidrogel nanokomposit NaAlg-PVA-g-AAm termodifikasi nanopartikel ZnO yaitu kapasitas swelling maksimumnya 215,5278 g/g, loading ion Zn2 sebesar 285,82 ppm dan kapasitas release 3maksimumnya sebesar 0,9832 ppm. Kinetika swelling hidrogel NaAlg-PVA-g-AAm mengikuti orde pseudo-pertama dengan parameter laju swelling sebesar 350 menit. Sedangkan kinetika swelling hidrogel nanokomposit NaAlg-PVA-g-AAm termodifikasi nanopartikel ZnO mengikuti orde pseudo-kedua dengan parameter laju swelling sebesar 487,5 menit. Dari hasil uji aktivitas antibakteri yang dilakukan secara in-vitro, diketahui S.aureus lebih resisten dibandingakan P. aeruginosa dengan persen inhibisi S. aureus yang lebih besar pada konsentrasi hambat minimum yang sama yaitu 31,25 ppm. ......In this research, NaAlg PVA g AAm nanocomposite hydrogel had been successfully modified by ZnO nanoparticles in the hydrogel matrix by hydrothermal method. Characteristics of hydrogels were observed with FTIR, SEM, TEM, EDX, XRD, AAS and through their swelling capacities. The NaAlg PVA g AAm hydrogel with the best swelling capacity was synthesized by adding PVA and alginate with a mass ratio of 0.6 3. Obtained results for NaAlg PVA g AAm nanocomposite hydrogel modified ZnO nanoparticles had the maximum swelling capacity of 215.52 g g, Zn2 ion loading of 285.82 ppm and its maximum release capacity of 0.98 ppm, while the maximum swelling capacity for a NaAlg PVA g AAm nanocomposite hydrogel was 73.26 g g. Kinetics swelling of NaAlg PVA g AAm hydrogel followed the first pseudo order with a swelling rate parameter of 350 minutes, whereas kinetics swelling of NaAlg PVA g AAm nanocomposite hydrogel modified ZnO nanoparticles followed the second pseudo order with swelling rate parameter of 487.5 minutes. From in vitro antibacterial activity test, S.aureus was known to be more resistant than P. aeruginosa with a greater inhibition percentage of S. aureus at the same minimum inhibitory concentration of 31.25 ppm.