Hasil Pencarian  ::  Simpan CSV :: Kembali

"Energi hidrogen yang dipertimbangkan sebagai sumber energi baru ramah lingkungan pengganti energi fosil semakin digencarkan pengembangannya. Salah satu senyawa yang berguna sebagai pembawa hidrogen adalah amonia boran (NH3BH3) dengan kandungan hidrogen sebesar 19,6 wt%. Telah disintesis katalis Rutenium berpenyangga CeO2 Nanosphere untuk reaksi dehidrogenasi amonia boran dan dilakukan penambahan logam Fe ke dalam katalis. Karakterisasi XRD, XRF, SAA, TEM, dan Spektroskopi Raman dilakukan terhadap katalis. Diuji pengaruh variasi morfologi, komposisi, temperatur, konsentrasi NaOH, dan durablitas katalis terhadap reaksi dehidrogenasi amonia boran. Katalis Ru0.75Fe0.25/CeO2 Nanosphere memiliki hasil uji aktivitas katalitik tertinggi dengan nilai TOF sebesar 153,714 h-1 pada suhu 308 K. Nilai energi aktivasi (Ea) yang didapatkan dari variasi temperatur sebesar 37,587 kJ/mol.

---

Hydrogen energy is considered to be the new resource of clean and renewable energy compared to fossil fuel. Ammonia borane (NH3BH3) is known as one of the hydrogen carrier compounds which contain 19,6 wt% of hydrogen. Ruthenium catalyst supported by CeO2 Nanosphere has been successfully synthesized and the addition of Fe metal to the catalyst has been carried out for dehydrogenation of ammonia borane purposes. Some characterizations such as XRD, XRF, SAA, TEM, and Raman Spectroscopy were tested on the catalyst. Variations of morphology, composition, temperature, concentration of sodium hydroxide, and durability tests were carried out to evaluate their effect on the reaction. The result shows that Ru0.75Fe0.25/CeO2 Nanosphere catalyst exhibits the highest catalytic activity measured by TOF value 153,714 h-1 under 308 K. Activation energy is obtained by temperature variation in the value of 37,587 kJ/mol."

"Penggunaan Amonia boran sebagai salah satu metode yang dapat memproduksi hidrogen dilakukan dengan bantuan katalis dan penyangga. Amonia boran digunakan karena memiliki kandungan hidrogen yang besar sehingga menjanjikan untuk aplikasi pembentukan hidrogen. Pada penelitian ini katalis trimetalik RuNiAg dengan penyangga karbon nanosphere berhasil disintesis melalui impregnasi basah lalu dikarakterisasi dengan FTIR, XRD, XRF, Raman, SEM, HRTEM, FESEM, dan SAA. Pengaruh dari variasi komposisi logam, suhu, penambahan NaOH, dan keberulangan pemakaiannya dievaluasi serta dipelajari ditinjau dari aktivitas katalitik serta nilai Turn Over Frequency (TOF). Katalis Ru0.05Ni0.73Ag0.21/CNS memberikan performa aktivitas katalitik terbaik dalam dekomposisi senyawa amonia boran dibandingkan variasi lainnya pada suhu ruang yaitu sebesar 990,91 h-1 serta energi aktivasi (Ea) dihasilkan sebesar 23,36 kJ/mol. Pada penambahan NaOH serta suhu, memberikan peningkatan pada nilai TOF yang dihasilkan pada aktivitas katalitiknya yang menunjukkan efek sinergis dari logam Ru, Ni, dan Ag pada penyangga karbon nanosphere.

---

The use of Ammonia borane as a method to produce hydrogen is carried out with the help of catalysts and supports. Ammonia borane is used because it has a large hydrogen capasity, making it promising for hydrogen forming applications. In this study the trimetallic RuNiAg catalyst with carbon nanosphere support was successfully synthesized via wet impregnation and then characterized by FTIR, XRD, XRF, Raman, SEM, HRTEM, FESEM, and SAA. The effects of variations in metal composition, temperature, addition of NaOH, and reusability were evaluated and studied in terms of catalytic activity and Turn Over Frequency (TOF) values. The catalyst Ru0.05Ni0.73Ag0.21/CNS gave the best performance of catalytic activity in the decomposition of ammonia boranes compared to other variations at room temperature which was 990.91 h-1 and activation energy (Ea) was 23.36 kJ/mol. The addition of NaOH and temperature increases the TOF value resulting in its catalytic activity which indicates a synergistic effect of the metals Ru, Ni, and Ag on the carbon nanosphere support.

"

"Energi hidrogen merupakan salah satu alternatif energi terbarukan yang ramah lingkungan. Hidrogen dapat diproduksi dengan berbagai macam metode salah satunya adalah dehidrogenasi amonia boran. Amonia boran memiliki karakteristik seperti stabilitas di udara dan air, kandungan hidrogen yang tinggi sekitar 19.6 wt% yang pada reaksinya akan terbentuk 3 mol hidrogen. Katalis RuX (X = Ni, Fe, Ag) dengan pendukung karbon nanosphere (CNS) disintesis dengan metode impregnasi basah dan dikarakterisasi dengan TEM, SAA, XRD dan XRF. Pengaruh dari penambahan logam X, variasi suhu, konsentrasi NaOH, dan keberulangan pemakaiannya dievaluasi dan dipelajari terhadap aktivitas katalitik. Kartalis bimetalik RuNi memiliki aktivitas katalitik tertinggi dengan penambahan NaOH 1 M yang menghasilkan nilai TOF 3481,9 h-1 dan energi aktivasi 23,054 kJ/mol yang menunjukkan adanya efek sinergis antara logam Ru dan Ni pada pendukung karbon nanosphere.

---

Hydrogen energy is one of the environmentally friendly renewable energy alternatives. Hydrogen can be produced by various methods, one of which is the dehydrogenation of ammonia borane. Ammonia borane has characteristics such as stability in air and water, a high hydrogen content of about (19.6 wt%) which in the reaction will form 3 moles of hydrogen. RuX catalyst (X = Ni, Fe, Ag) with carbon nanosphere (CNS) support was synthesized by wet impregnation method and characterized by TEM, SAA, XRD and XRF. The effect of addition of metal X, variations in temperature, concentration of NaOH, and its sustainability were evaluated and studied on catalytic activity. The RuNi bimetallic catalyst had the highest catalytic activity with the addition of 1 M NaOH which resulted in a TOF value of 3481.9 h-1 and an activation energy of 23.054 kJ/mol indicating a synergistic effect between Ru and Ni metals on the carbon nanosphere support."