Hasil Pencarian  ::  Simpan CSV :: Kembali

"Metanol dianggap sebagai pembawa hidrogen yang menjanjikan karena kemampuannya untuk melepaskan hidrogen. Katalis berbasis tembaga umumnya digunakan memiliki stabilitas termal rendah di atas ambang batas keamanan. Platinum dapat memfasilitasi dispersi nanopartikel tembaga, mencegah aglomerasi, dan memastikan distribusi seragam pada permukaan katalis, meningkatkan aksesibilitas dan reaktivitas situs aktif tembaga. Penelitian ini mengeksplorasi penggunaan katalis bimetal tembaga-platinum sebagai peningkatan stabilitas katalis penyangga Ca(Ce0.5Zr0.5)O3 pada reaksi methanol steam reforming. Penggunaan support perovskite Ca(Ce0.5Zr0.5)O3 memberikan potensi peningkatan laju reaksi pada water-gas shift reaction dalam reaksi methanol steam reforming. Karakterisasi katalis dilakukan dengan menggunakan XRD, XRF, SAA, Spektroskopi Raman, dan TEM. Aktivitas katalitik pada reaksi methanol steam reforming diuji dengan adanya variasi komposisi dan temperatur. Katalis Cu0.75Pt0.25/Ca(Ce0.5Zr0.5)O3 memiliki aktivitas katalitik tertinggi dengan menghasilkan konsentrasi hidrogen sebesar 24,15% dan produksi hidrogen sebesar 0,0069 mol/min/g. Didapatkan temperatur yang optimal dengan aktivitas katalitik yang baik, yaitu temperatur 350ºC.

---

Methanol is considered a promising hydrogen carrier due to its ability to release hydrogen. Commonly used copper-based catalysts have low thermal stability above the safety threshold. Platinum can facilitate the dispersion of copper nanoparticles, prevent agglomeration, and ensure uniform distribution on the catalyst surface, improving the accessibility and reactivity of copper active sites. This study explores the use of platinumcopper bimetal catalysts as an improvement in the stability of the Ca(Ce0.5Zr0.5)O3 support catalyst in the methanol steam reforming reaction. The use of perovskite support Ca(Ce0.5Zr0.5)O3 provides the potential for increasing the reaction rate in the water-gas shift reaction in the methanol steam reforming reaction. Catalyst characterization was carried out using XRD, XRF, SAA, Raman spectroscopy, and TEM. Catalytic activity in the methanol steam reforming reaction was tested in the presence of composition and temperature variations. Cu0.75Pt0.25/Ca(Ce0.5Zr0.5)O3 catalyst has the highest catalytic activity by producing hydrogen concentration of 24.15% and hydrogen production of 0.0069 mol/min/g. The optimal temperature with a good catalytic activity is 350ºC."

"Sektor energi menjadi penyumbang 75% emisi gas rumah kaca yang dilaporkan oleh International Energy Agency tahun 2021. Oleh karena itu, transisi penggunaan energi fosil ke energi alternatif, salah satunya energi hidrogen (H2), harus diimplementasikan lebih luas lagi terutama terhadap kedua sektor tersebut untuk mengurangi emisi gas rumah kaca. Penelitian ini bertujuan untuk mengembangkan katalis berbasis tembaga (Cu) yang tinggi aktivitas katalitiknya pada reaksi methanol steam reforming (MSR) untuk memproduksi H2. Pemilihan support yang baik penting untuk performa katalis Cu. Dalam penelitian ini, Ce diperkenalkan sebagai dopan Zr pada sistem support CaZrO3. CeO2 dikenal sebagai support sekaligus promoter yang baik karena karakteristik oxygen storage capacity (OSC) yang tinggi sehingga dapat meningkatkan aktivitas katalitik Cu/CaCe(x)Zr(1-x)O3. Cu/CaCe(x)Zr(1-x)O3 disintesis dengan metode sol-gel dan dry impregnation dan diuji aktivitasnya pada reaksi MSR pada 250, 300, dan 350 °C. Komposisi Ce-Zr dan variabel temperatur dievaluasi pada penelitian ini. Cu/CaCe(x)Zr(1-x)O3 dikarakterisasi dengan XRF, XRD, Spektroskopi Raman, SAA, O2-TPO, dan TEM. Hasilnya, variasi rasio Ce-Zr telah sesuai dengan yang diharapkan, Cu telah berhasil diimpregnasi ke permukaan support, kelima katalis adalah material mesopori, dan Cu/CaCeO3 diketahui memiliki densitas oxygen vacancy (Ovac) tertinggi, yang menandakan OSC yang juga tinggi. Sesuai dengan perolehan densitas Ovac tertinggi, Cu/CaCeO3 unggul dalam uji reaksi MSR di ketiga temperatur uji, dengan konversi metanol, yield H2, dan produksi H2 pada temperatur tertinggi berturut-turut sebesar 98,37%, 86,59%, dan 0,0539 mol/min/gcat.

---

The energy sector accounted for 75% of greenhouse gas emissions reported by the International Energy Agency in 2021. Therefore, the transition from fossil fuels to alternative energy sources, one of which is hydrogen (H₂) energy, must be widely implemented especially in those two sectors to reduce greenhouse gas emissions. This research aims to develop a copper (Cu)-based catalyst with high catalytic activity in the methanol steam reforming (MSR) reaction for H2 production. The selection of a suitable support is crucial for the performance of the Cu-based catalysts. In this study, Ce is introduced as a dopant in Zr within the CaZrO3 support system. CeO₂ is well-known to be an excellent support and promoter due to its high oxygen storage capacity (OSC) characteristic, which can enhance the catalytic activity of Cu/CaCe(x)Zr(1-x)O3. Cu/CaCe(x)Zr(1-x)O3 was synthesized using sol-gel and dry impregnation methods and tested for activity in the MSR reaction at temperatures of 250, 300, and 350 °C. The Ce-Zr composition and temperature variables are evaluated in this study. Cu/CaCe(x)Zr(1-x)O3 was characterized using XRF, XRD, Raman spectroscopy, SAA, O2-TPO, dan TEM. The results indicate that the desired and obtained ratios of the catalyst are in agreement with one another, Cu is successfully impregnated onto the surface of CaCe(x)Zr(1-x)O3, all five catalysts are mesoporous materials, and Cu/CaCeO3 exhibits the highest density of oxygen vacancies (Ovac), indicating a high OSC. Consistent with the highest Ovac density obtained, Cu/CaCeO3 excels in MSR reaction tests at all three test temperatures, with methanol conversion, H₂ yield, and H₂ production at the highest temperature being 98,37%, 86,59%, dan 0,0539 mol/min/gcat."

"Untuk menjawab tantangan global terhadap persediaan sumber energi konvensional yang terus berkurang, energi hidrogen hadir sebagai kandidat sumber energi alternatif yang menjanjikan. Salah satu material cairan pembawa hidrogen adalah metanol. Melalui reaksi methanol steam reforming, metanol dapat direformasi membentuk hidrogen dengan rasio H/C yang tinggi pada suhu rendah. Pada penelitian ini, titanate nanotubes (TNTs) yang dimodifikasi dengan MoOx disintesis dengan metode hidrotermal dan presipitasi sebagai pendukung katalis Cu. Modifikasi bertujuan untuk memfasilitasi pembentukan karakteristik oxygen vacancy, yang dianggap menguntungkan reaksi water gas-shift dalam reaksi methanol steam reforming. Katalis berhasil disintesis dibuktikan dengan karakterisasi XRF, XRD, SAA-BET, Raman, dan TEM. Efek sinergis katalis terhadap reaksi methanol steam reforming dijelaskan dengan karakterisasi H2-TPR. Dari hasil uji aktivitas katalitik ditemukan katalis Cu@TNTs-MoOx 10% memberikan konversi metanol (~94,2%) dan produksi hidrogen (0,0043 mol/min/g) yang tinggi pada suhu optimal 400°C. Meskipun katalis ini selektif terhadap reaksi metanasi, tetapi menawarkan kestabilan termal, selektivitas CO yang rendah, dan meminimalkan pembentukan coke melalui pembentukan spesi MoOxCy.

---

To address the global challenge of diminishing conventional energy supplies, hydrogen energy has emerged as a promising candidate for alternative energy sources. One of the liquid hydrogen carriers is methanol, which can be reformed to produce hydrogen with a high H/C ratio at low temperatures through the methanol steam reforming reaction. In this study, titanate nanotubes (TNTs) modified with MoOx were synthesized via hydrothermal and precipitation methods as a support for copper catalysts. This modification aims to facilitate the formation of oxygen vacancy characteristics, which are considered beneficial for the water-gas shift reaction during methanol steam reforming. The catalysts were successfully synthesized, as confirmed by XRF, XRD, SAA-BET, Raman, and TEM characterizations. The synergistic effects of the catalysts on the methanol steam reforming reaction were analyzed using H2-TPR characterization. Catalytic activity tests revealed that the Cu@TNTs-MoOx 10% catalyst achieved high methanol conversion (~94.2%) and hydrogen production (0.0043 mol/min/g) at an optimal temperature of 400°C. Although this catalyst is selective toward methanation reactions, it offers thermal stability, low CO selectivity, and minimizes coke formation through the generation of MoOxCy species."