Abstrak :
ABSTRACT
There has been a constant need in developing new ways of extracting valuable elements from its ore from time to time. There is always an effort made by scientists and engineers all around the globe in the pursuit of extraction methods that is more efficient and beneficial than ever before. Rice husk is the byproduct of rice production. It is estimated that nowadays the utilization of this byproduct is not maximized yet, while the rice production in Indonesia itself keeps on increasing. This research was intended to study the utilization of rice husk as the reduction agent of lateritic nickel ore. The reduction process done have been able to reduce the limonite ore to NiO and magnetite. The beneficiation process that was done in this research includes roasting ndash quenching and reduction process. The best result of the Fe and Ni concentration of the final product was 19.81 wt. and 1.23 wt. respectively. The nickel beneficiation have been succeeded having increased the initial nickel content in the limonite ore of 1.19 wt. to 1.23 wt. in the final product. The beneficiation process that was done in this research includes roasting ndash quenching and reduction process.

---

ABSTRAK
Kebutuhan untuk mengembangkan cara ndash; cara baru untuk proses ekstraksi elemen berharga dari sumbernya terus menerus meningkat dari waktu ke waktu. Para peneliti selalu berusaha untuk mengembangkan cara ekstraksi yang lebih efisien dan bermanfaat dari yang sebelumnya. Sekam merupakan hasil sambilan dari proses produksi beras. Diperkirakan pada masa ini, pemanfaatan sekam belum maksimal sebanding dengan penghasilannya yang terus meningkat di Indonesia. Riset ini ditujukan untuk mempelajari penggunaan sekam dalam proses benefikasi bijih limonit. Proses benefisiasi yang dilakukan dalam riset ini meliputi proses roasting ndash; quenching dan reduksi. Proses reduksi yang dilakukan telah berhasil mereduksi limonit menjadi NiO dan magnetit. Hasil konsentrasi Fe dan Ni terbaik adalah 19.81 dan 1.23 berturut ndash; turut. Proses benefisiasi nikel telah berhasil dengan meningkatkan konsentrasi nikel dari 1.19 menjadi 1.23.

Abstrak :
ABSTRAK Pengembangan cara baru untuk mengekstrak logam dari bijihnya terus di coba dari waktu ke waktu. Seiring berlalunya waktu, ilmuwan dan insinyur di seluruh dunia telah berusaha menemukan metode ekstraksi yang lebih efisien dan bermanfaat. Indonesia adalah salah satu produksi beras unggulan dengan produk sampingan dari produksinya yaitu sekam padi. Pemanfaatan produk sampingan ini belum maksimal. Penelitian ini dilakukan dengan tujuan untuk mempelajari pemanfaatan sekam padi sebagai bahan reduksi bijih nikel laterit. Proses reduksi telah diketahui dapat mereduksi bijih limonit menjadi NiO dan magnetit. Proses dilakukan telah meningkatkan kadar nikel dari bijih limonit dengan kadar terbaik 1.17 wt. dan telah meningkatkan kadar dengan kadar 1.15 wt. sebelumnya. Proses yang dilakukan dalam penelitian ini meliputi roasting-quenching dan reduction process.

---

ABSTRACT
Developing a new way to extract metal from its ore has been demanded from time to time. As the time goes on, scientists and engineers all around the globe have been trying to find the more efficient and beneficial extraction method. Indonesia is one of the leading production of rice with the byproduct of that production is rice husk. The utilization of this byproduct has not been maximized yet. This research is conducted with the aim to study the utilization of rice husk as the reduction agent for nickel laterite ore. The reduction process has been known to reduce limonite ore to NiO and magnetite. Best result of Ni concentrate of the final product is 1.17 wt. . nickel content has increased from the initial concentration which is 1.15wt. . Process done in this research include roasting quenching and reduction process.

Abstrak :
Nikel merupakan logam hasil ekstraksi dari bijih sulfida, bijih laterit, dan batuan mineral laut dalam. Nikel banyak dibutuhkan di sektor industri logam paduan, baterai, electroplating, dan lainnya. Nikel biasanya diekstraksi dalam bentuk feronikel atau nikel murni sesuai kebutuhan industri. Bijih nikel yang paling banyak ditemukan di Indonesia merupakan mineral jenis laterit. Nikel laterit di Indonesia terbagi menjadi jenis limonit dan saprolit. Mineral jenis limonit memiliki kandungan nikel lebih rendah daripada jenis saprolit. Bijih nikel jenis saprolit biasa diolah dengan metode pirometalurgi dan jenis limonit diolah dengan metode hidrometalurgi, dimana hal ini ditentukan berdasarkan kandungan nikelnya. Proses hidrometalurgi bijih nikel laterit dilakukan dengan teknik pelindian menggunakan larutan asam sulfat pada temperatur tinggi untuk menghasilkan perolehan kadar nikel yang tinggi. Pada temperatur atmosfer, perolehan nikel bernilai rendah. Oleh karena itu, penelitian ini bertujuan untuk melakukan karakterisasi elektrokimia bijih nikel laterit menggunakan larutan asam sulfat pada temperatur atmosfer. Larutan asam sulfat yang digunakan divariasikan untuk penelitian ini dengan konsentrasi larutan 1 M, 2 M, 4 M, dan 6 M. Metodologi penelitian dilakukan dengan alur preparasi sampel dan larutan, karakterisasi dengan SEM-EDAX dan metode Petrografi, serta karakterisasi elektrokimia menggunakan metode OCP, EIS, dan LSV. Hasil dari ketiga pengujian tersebut menunjukkan laju pelarutan tertinggi terjadi pada pelarutan dengan konsentrasi 6 M. Peningkatan konsentrasi menurunkan nilai OCP pengujian. Berdasarkan uji LSV, lapisan pasif terbentuk pada pelarutan pada tiap konsentrasi. Peningkatan konsentrasi menyebabkan pemecahan lapisan pasif hingga konsentrasi 4 M, namun lapisan pasif terbentuk kembali pada peningkatan hingga 6 M berdasarkan uji EIS. Ketiga pengujian tersebut menunjukkan perilaku pelarutan meningkatnya laju pelarutan dengan penambahan konsentrasi, namun menimbulkan pembentukan kembali lapisan pasif pada konsentrasi asam melebihi 4 M. ......Nickel was an extracted metal from sulphide ore, laterite ore, and deep-sea mineral rocks. Nickel was needed in the industrial sector of alloy metal, batteries, electroplating, and others. Nickel was usually extracted in the form of pure ferronickel or nickel according to industrial needs. The nickel ore most commonly found in Indonesia was laterite type minerals. Laterite nickel in Indonesia was divided into limonite and saprolite types. Limonite minerals had lower nickel content than saprolite types. Saprolite type nickel ore was usually processed by the pyrometallurgical method and the limonite type was processed by the hydrometallurgical method, where was determined based on the nickel content. The hydrometallurgical process of laterite nickel ore was carried out by leaching technique using a solution of sulfuric acid at high temperatures to produce high nickel content. At atmospheric temperatures, recovery of nickel was low. Therefore, this study aimed to conduct an electrochemical caharacterization of laterite nickel ore using a solution of sulfuric acid at atmospheric temperature. The sulfuric acid solution used for this study was varied with concentration of 1 M, 2 M, 4 M, and 6 M. The research methodology flow was carried out first with sample and solution preparation, SEM-EDAX characterization and Petrographic method, and electrochemical studies using the OCP, EIS, and LSV methods. The results showed the highest dissolution rate occurred at dissolution of 6 M concentration. The increasing concentration decreased the OCP value. Based on the LSV test, a passive layer was formed at each concentration of dissolution. Increased concentration causes the breakdown of the passive layer for adding concentration to 4 M, but the passive layer was formed again at increasing concentration up to 6 M based on the EIS test. The electrochemical characterization revealed the dissolution behavior increased the dissolution rate with the addition of concentration, but caused the formation of the passive layer again at the acid concentration exceeding 4 M.

Abstrak :
Penelitian ini dilakukan untuk mengetahui efek basisitas kuartener dengan variasi basisitas CaO dan MgO pada selektif reduksi bijih nikel limonit. Bijih nikel limonit yang digunakan dalam penelitian ini mengandung 1,38% Ni dan 38,2% Fe. Selain itu reduktor yang digunakan dalam proses ini ialah batubara antrasit dengan variasi jumlah penambahan dalam stoikiometri 0,0625-1,5. Penelitian ini juga menggunakan 10% berat natrium sulfat (Na₂SO₄) dan direduksi pada temperatur 1150^oC dengan waktu tahan selama 1 jam. Sampel yang telah direduksi kemudian dipisahkan secara magnetik. Studi ini menghasilkan bahwa jumlah penambahan batubara antrasit yang optimal, yaitu pada stoikiometri 0,125 dan menghasilkan kadar dan recovery nikel masing-masing sebesar 4,76% dan 85,87% serta kadar dan recovery besi masing-masing sebesar 75,51% dan 36,28%. Selain itu, studi ini juga menghasilkan bahwa semakin meningkat basisitas, maka semakin meningkat pula kadar dan recovery Ni hanya sampai pada basisitas optimum dan kemudian kadar dan recovery nikel semakin menurun. Begitupula pada rata-rata ukuran feronikel.

---

This study was conducted to determine the effects of quaternary bases with variations of CaO and MgO on selective reduction of nickel limonitic ore. Limonitic nickel ore used in this process contained 1.38% Ni and 38.2% Fe. Additionally, this process used variants of anthracite coal based on stoichiometry (0.0625-1.5) and a 10wt.% of sodium sulphate (Na₂SO₄). Temperature needed for reduction was 1150^oC at 1 hour of holding time. Magnetic separation was performed afterwards. The results of this study show the addition of anthracite coal as a reducing agent was optimal in the stoichiometric ratio of 0.125 ; grade and recovery of nickel was 4.76% and 85.87% and grade and recovery of Fe was 75.51% and 36.28 %. In addition, this study showed that the higher basicity, increases the grade and recovery of nickel but only until the optimum basicity, as exceeding optimum basicity could decrease the grade and recovery of nickel well as the average size of ferronickel.

Abstrak :
Cadangan bijih nikel laterit yang dimiliki oleh Indonesia diperkirakan mencapai 1,391 milyar ton 16% dari cadangan bijih nikel laterit dunia atau menempati urutan kedelapan terbesar di dunia. Permasalahan utama yang sedang dihadapi oleh industri pertambangan dunia adalah proses pemurnian bijih nikel laterit tersebut mempertimbangkan aspek ekonomi maupun energi. Penelitian ini bertujuan untuk mempelajari variabel reduksi selektif yang paling optimal terhadap perolehan dan kadar nikel yang tinggi. Penelitian ini menggunakan bijh nikel saprolit dengan kadar Ni 1,74% dan kadar Fe 15,63% dengan penambahan aditif Na2SO4 10%wt, pada variasi temperatur reduksi 950˚C, 1050˚C, 1150˚C, variasi stoikiometri 0,5; 1,0; 1,5, dan reduktor sulfur 2,68% dan 5%. Penelitian ini menunjukkan pada reduktor sulfur 2,68% menghasilkan kadar dan perolehan nikel yang paling optimal. ......Indonesia supply accounts for 16% of the worlds lateritic nickel ore, with the estimation reaching 1.391 billion tons. The process of refining lateritic nickel ore can be considered as one of the main problems faced by the world mining industry, taking into account the economic and energy aspects. This research was carried out to investigate the effect of sulfur in reductants in the selective reduction process of saprolitic nickel ore. This research used saprolitic ore with 1.74% Ni and 15.63% Fe content with the addition of 10 wt.% additive Na2SO4, at a reduction in temperature variations 950˚C, 1050˚C, 1150˚, stoichiometric variations of two kind reductants 0.5, 1.0, 1.5 containing 2.68% and 5% of sulfur. This research shows that at 2.68% sulfur in reductants produced the most optimal grade and nickel recovery.

Abstrak :
Indonesia adalah salah satu produsen dan eksportir nikel terbesar di dunia dengan cadangan mencapai 21 juta metrik ton. Indonesia telah mengekspor berton-ton bijih nikel mentah ke seluruh dunia. Jumlah bijih nikel yang diekspor dari Indonesia telah meningkat pesat hingga tahun 2014. Pada tahun 2014, Pemerintah mengeluarkan larangan ekspor bijih nikel mentah. Namun, karena kurangnya persiapan fasilitas smelter, Pemerintah memberikan relaksasi pada tahun 2017 untuk membangun smelter. Pada tahun 2020, pemerintah memperkuat kebijakan larangan ekspor bijih nikel mentah. Indonesia bertujuan untuk membangun rantai pasokan domestik end-to-end untuk Baterai Kendaraan Listrik dan menjadi pemain utama di pasar Kendaraan Listrik global pada tahun 2030 berdasarkan tata letak roadmap EV yang merupakan salah satu ambisi Indonesia. Kebijakan pelarangan ekspor bijih nikel mentah, meskipun dituding menghambat kinerja ekspor jangka pendek, sebenarnya merupakan upaya mendorong hilirisasi yang akan memberikan dampak ekonomi yang lebih besar berupa nilai tambah, pengembangan industri maju, penyerapan tenaga kerja, dan penerimaan negara.Tujuan dari tesis ini adalah untuk menemukan dampak terukur dari Kebijakan Larangan Ekspor Nikel terhadap Perkembangan Industri Nikel Indonesia dengan menggunakan pendekatan Analisis Dampak berdasarkan Model Sistem Dinamis. Hasil yang diharapkan dari model dan temuan tesis ini adalah model sistem dinamis yang mengelaborasi dampak kebijakan larangan ekspor bijih nikel mentah terhadap perkembangan Industri Nikel Indonesia...... Indonesia is one of the largest nickel producers and exporters in the world with reserves reaching 21 million metric tons. Indonesia has been exporting tonnes of raw nickel ore worldwide. The number of nickel ore exported from Indonesia had been rapidly increasing until 2014. In 2014, the Government issued a ban on the export of raw nickel ore. However, due to a lack of preparation for smelter facilities, the Government provide relaxation in 2017 for building smelters. In 2020, the government reinforce the raw nickel ore export ban policies. Indonesia aims to build an end-to-end domestic supply chain for Electric Vehicle Batteries and become a major player in the global Electric Vehicles market by 2030 based on the EV roadmap layout which is one of Indonesia’s ambitions. The raw nickel ore export ban policy, although it is accused of hampering short-term export performance, is actually an effort to encourage downstream which will have a greater economic impact in the form of added value, advanced industrial development, employment, and state revenue. The goal of this thesis is to find the measurable effect of the Nickel Export Ban Policy on the Development of Indonesia's Nickel Industry using the Impact Analysis approach based on the System Dynamics Model. The expected outcome of the model and finding of this thesis is a system dynamic model that elaborates the effects of the raw nickel ore export ban policy on the development of Indonesia’s Nickel Industry.

Abstrak :
Deposit laterite merupakan salah satu jenis bijih nikel yang paling berlimpah di alam. Di Indonesia khususnya di Kabupaten Pomala, Sulawesi Tenggara memiliki deposit laterite yang tergolong tinggi. Salah satu mineral yang ada di dalam lapisan laterite yaitu bijih nikel saprolit yang memiliki kadar unsur nikel yang lebih tinggi dibandingkan lapisan lainnya seperti limonit. Untuk mendapatkan recovery nikel yang efektif dan efisien, diperlukan suatu pengembangan penelitian proses ekstraksi. Pada penelitian ini akan dilakukan beberapa proses seperti separasi dengan fluida air, pirometalurgi (roasting reduction) dan hidrometalurgi (pelindian). Penelitian ini akan membahas pengaruh penambahan reduktor yang berasal dari batubara dengan kadar yang berbeda-beda yaitu 8%, 16%, 24% dan 32%. Untuk mengetahui komposisi kimia dari bijih saprolit yang murni dan yang telah dilakukan proses separasi, akan dilakukan pengujian EDX (Energy Dispersive X-Ray) terlebih dahulu. Sebelum ketahap hidrometalurgi, sampel dengan masing-masing penambahan batubara tersebut dilakukan proses roasting reduction pada temperatur 1250oC di dalam furnace carbolyte. Selanjutnya akan dilakukan pengujian STA dan XRD dengan tujuan untuk melihat senyawa-senyawa yang terdapat pada bijih nikel saprolit tersebut. Setelah tahap ini selesai dilakukan, sampel dilindi dengan menggunakan larutan Asam Sulfat 1 Molar dalam waktu 90 menit. Dari hasil yang diperoleh, pada proses pelindian asam sulfat dengan konsentrasi 1 Molar, persentase recovery nikel yang tertinggi berada pada bijih saprolit yang ditambahkan dengan batubara sebanyak 16% dengan perolehan Nikel nya yaitu sebesar 59.85% (persentase optimum). ......Laterite deposit is one of the most abundant ore in nature. In Indonesia, especially in Pomala regency, Southeast Sulawesi, has a high laterite deposit. One of the minerals in the laterite layer is saprolite nickel ore which has a higher nickel content than the other layers, such as limonite. To get recovery of nickel with effective and efficient, a study about development of extraction process is needed. This research will conduct several processes such as float and sink process, pyrometallurgy (roasting reduction) and hydrometallurgical (leaching). This research also will disscus the effect of addition of coal as reductor, with varied levels of coal: 8%, 16%, 24% and 32%. To determine the chemical composition of saprolite ore that have been treated by float and sink process, EDX (Energy dispersive X-Ray) test is performed. Before hydrometallurgy process is conducted, the samples that have been added by varied levels of coal was reduction roasted at temperature 1250oC in Carbolyte furnace. Further testing will be conducted by the STA and XRD with purpose to determine the compounds presence in the saprolite nickel ore. After that stage, the sample is leached in Sulfuric Acid at 1 Molar for 90 minutes. From the obtained results, the process of leaching with sulfuric acid at 1 Molar, the recovery percentage of nickel from 16% of coal addition is the highest with obtained value 59.85% (optimum percentage).

Abstrak :
Secara umum penelitian ini bertujuan untuk mengeksplorasi kemungkinan penggunaan limbah biomassa dalam proses reduction roasting bijih besi nikel laterite Indonesia. Adapun motif di balik penelitian ini adalah untuk meningkatkan nilai tambah dari bijih besi kadar rendah dan mendapatkan bio-reduktor baru yang akan menjadi alternatif pengganti batu bara di masa depan. Dalam penelitian ini diteliti tiga limbah biomassa sebagai agen pereduksi bijih besi nikel laterite dari Sorowako, yaitu: ampas tebu dari kabupaten Cirebon, cangkang sawit dari Palangkaraya - Kalimantan Tengah, dan sekam padi dari Kerawang - Jawa Barat. Adapun metode yang digunakan adalah reduction roasting dengan variasi parameter temperatur, rasio massa, dan waktu reduksi. Selanjutnya dilakukan analisis berdasarkan pola difraksi hasil X-Ray Diffraction (XRD), X-Ray Fluorescence (XRF), dan Induced Couple Plasma Mass Spectroscopy (ICP-MS). Hasil yang diperoleh dalam penelitian ini menunjukkan bahwa ampas tebu, cangkang sawit, dan sekam padi terbukti mampu digunakan sebagai agen pereduksi alternatif pengganti batu bara. Pada penelitian ini, ampas tebu hanya mampu menghasilkan fasa wustite dalam reduction roasting bijih besi nikel laterite, di mana hasil reduksi tertinggi diperoleh pada sampel dengan rasio massa 1:4 yang direduksi pada temperatur 1000°C selama 30 menit. Sementara itu, cangkang sawit mampu mereduksi bijih besi nikel laterite menjadi Fe metal, dimana parameter optimalnya adalah: rasio massa = 1:3, durasi waktu reduksi = 30 menit, dan temperatur reduksi 1000°C. Di samping itu, meskipun sekam padi hanya mampu mereduksi bijih besi sampai fasa magnetite (dimana hasil optimal diperoleh pada penambahan padi sebesar 20%), tetapi dari sekam padi berhasil diperoleh bio-silika amorf dengan tingkat kemurnian 99,99% dan specific surface area (luas permukaan spesifik) 192 m2/g.

---

In general, this study aims to explore the utilization of local biomass as renewable reducing agents in the reduction roasting of Indonesian nickel laterite iron ore. The motive behind this research is to increase the added value of low grade iron ore and to obtain reducing agents to substitute coal in the reduction process. In this study, the three of biomass which have potential to be used as reducing agents for coal substitutes in reducing nickel laterite iron ore from Sorowako, are: bagasse from Cirebon, palm shells from Palangkaraya - Central Kalimantan, and rice husk from Kerawang - Jawa Barat. The reduction method used is reduction roasting with various temperature, mass ratio, and reduction time. And the analysis is based on the diffraction pattern of X-Ray Diffraction (XRD), X-Ray Fluorescence (XRF), and Induced Couple Plasma Mass Spectroscopy (ICP-MS). The results obtained in this study indicate that bagasse, palm kernel shells, and rice husks have been proven to be able to be used as an alternative reducing agent for coal substitution. In this study, bagasse was only able to produce the wustite phase in the reduction roasting of nickel laterite iron ore, where the highest reduction results were obtained in samples with a mass ratio of 1: 4 which was reduced at a temperature of 1000°C for 30 minutes. Meanwhile, palm kernel shells could reduce nickel laterite iron ore to Fe metal, where the optimal parameters were: mass ratio = 1: 3, reduction time duration = 30 minutes, and reduction temperature = 1000°C. In addition, although rice husk was only able to reduce iron ore to magnetite phase (where optimal results are obtained by adding rice by 20%), but from rice husk it was successfully obtained amorphous bio-silica with a purity level of 99.99% and specific surface area 192 m2/g.