Hasil Pencarian  ::  Simpan CSV :: Kembali

"ABSTRAKPada penelitian ini dilakukan pembuatan dan karakterisasi sampel Sn-xBi dan SnxBi-yAl sebanyak 10 sampel dengan variasi logam Bi dan Al dalam %berat yang berbeda menggunakan X-Ray Diffraction (XRD). Penentuan kapasitas panas sebagai fungsi temperatur Cp (T) dari material solder Sn-Bi dan Sn-Bi-Al menggunakan alat uji DSC pada rentang temperatur 30°C hingga 450oC dan laju 10 oC/menit. Hasil karakterisasi XRD selanjutnya diolah menggunakan aplikasi GSAS untuk mendapatkan informasi tentang struktur dan ukuran kristal, parameter kisi yang dimiliki terhadap pengaruh variasi Bi dan Al %berat, serta informasi lainnya yang dapat berpengaruh. Berdasarkan ukuran kristal pada paduan Sn-xBi diketahui bahwa semakin banyak penambahan logam Bi maka ukuran kristal Sn yang terbentuk akan semakin kecil.

---

ABSTRACT

In this research, manufacture and characterization of samples Sn and Sn-xBi-yAL as many as 10 samples with metal variation% Bi and Al in different weight using X-Ray Diffraction (XRD). Determination of the heat capacity as a function of temperature Cp (T) of the solder material of Sn-Bi and Sn-Bi-Al using a DSC test at 30oC to 450°C temperature range and a rate of 10 °C/min. XRD characterization results further processed using GSAS application to obtain information about the structure and size of the crystal, the lattice parameter of the effect of variation owned Bi and Al% by weight, as well as other information that can be influential. Based on the size of the crystals in the alloy Sn-xBi known that the more the addition of the metal Bi Sn formed crystal size will be smaller."

"Salah satu anoda korban yang paling banyak dipelajari adalah paduan Al-Zn-Sn, yang memiliki efisiensi arus sekitar 70%. Untuk meningkatkan efisiensi anoda korban paduan aluminium, logam tanah jarang seperti lantanum sering ditambahkan. Dari beberapa penelitian, penambahan logam tanah jarang menunjukkan efek yang berbeda, mulai dari peningkatan efisiensi arus hingga sealing effect pada lapisan pasif. Oleh karena itu, diperlukan penelitian lebih lanjut mengenai pengaruhnya terhadap struktur mikro dan sifat korosi dari penambahan lantanum pada salah satu paduan aluminium yang sering digunakan, seperti Al-Zn-Sn. Variasi sampel uji adalah Al-Zn-0.5Sn-xLa dan Al-Zn-1Sn-xLa (x= 0,1; 0,3; 0,5). Sampel akan diuji mikroskop optik, SEM-EDS, polarisasi siklik, EPMA dan EIS. Dari pemetaan unsur dengan EDS dan EPMA, lantanum terdistribusi dalam matriks Al dan presipitat dengan membentuk senyawa intermetalik Al11La3. Hasil OCP menunjukkan penurunan seiring dengan peningkatan lantanum. Hasil OCP sekitar -1,2 V dimana hasil tersebut lebih tinggi dari OCP anoda korban tegangan rendah yaitu -0.85 vs SCE. Dari hasil polarisasi siklik, potensi pitting corrosion terlihat menurun seiring dengan meningkatnya konsentrasi lantanum. Dari hasil EIS, resistansi transfer muatan meningkat seiring dengan penambahan konsentrasi lantanum. Dari hasil pengujian tersebut, paduan Al-Zn-Sn-La tidak dapat diklasifikasikan sebagai anoda korban tegangan rendah.

---

One of the most studied sacrificial anodes is the Al-Zn-Sn alloy, which has a current efficiency of about 70%. To increase the efficiency of aluminium alloy sacrificial anodes, rare earth metals such as lanthanum are often added. From several studies, the addition of rare earth metals shows different effects, from increasing current efficiency until sealing effect on passive layer. Therefore, further research is needed on the effects on microstructure and corrosion properties of adding lanthanum to one of the frequently used aluminium alloys, such as Al-Zn-Sn. The variations of the test samples were Al-Zn-0.5Sn-xLa and Al-Zn-1Sn-xLa (x= 0.1, 0.3, 0.5). The samples were tested for optical microscope, SEM-EDS, EPMA cyclic polarization and EIS. From mapping from EDS and EPMA, lanthanum was distributed in Al matrix and precipitate by forming an intermetallic compound αAl11La3. OCP result shown decreasing as lanthanum increases. OCP result is about -1.2 V that higher than low voltage sacrificial anode OCP (-0.85V vs SCE). From the cyclic polarization result, potential of pitting corrosion was shown decreasing as the lanthanum concentration increased. Charge transfer resistance shown increasing as lanthanum concentration is increasing in EIS result. Therefore, Al-Zn-Sn-La cannot be classified as low voltage sacrificial anode."

"Meningkatnya kekhawatiran terhadap dampak dari penggunaan Pb dari sisi kesehatan mendorong industri-industri elektronik mulai mencari material solder bebas Pb. Paduan yang berpotensi sebagai material solder pengganti Sn-Pb adalah Sn-0,7Cu, tetapi paduan tersebut memiliki titik leleh tinggi yaitu 216-227 ◦C, paduan lain yang berpotensi besar adalah Sn-9Zn dengan titik leleh 199° C, tetapi Zn sangat mudah teroksidasi dan mengalami korosi. Pada penelitian ini akan dilakukan pembuatan dan karakterisasi paduan 3 logam (ternary system) yaitu Sn-Zn-Cu, paduan baru ini diharapkan dapat memperbaiki kelemahan dari paduan Sn-Cu dan Sn-Zn. Karakterisasi paduan logam Sn-Cu-Zn menggunakan XRF (X-Ray Fluorescence) dan XRD (X-Ray Diffraction) menunjukkan adanya logam Sn, Cu dan Zn dalam setiap paduan logam dengan komposisi (% berat) Sn-0,8Cu, Sn-0,6Cu-10,4Zn dan Sn-0,5Cu-23,6Zn. Paduan logam Sn-0,5Cu-23,6Zn adalah paduan logam yang paling berpotensi sebagai pengganti Sn-37Pb, dengan titik leleh terendah 204,13 oC, nilai pasty range 9,33 oC yang mendekati paduan logam Sn-37Pb dan nilai heat of fusion/ΔH 65,33 J/g yang lebih rendah dari paduan Sn-37Pb.

---

Increasing concerns over the impact of the use of Pb from the health side drive electronics industries began to search for Pb-free solder material. Alloy material that has potential as a substitute for Sn-Pb solder is Sn-0.7Cu, but these alloys have high melting point is 216-227 ◦C, another potential alloys are Sn-9Zn in melting point of 199 ° C, but Zn is susceptible to oxidation and corrosion experience. This research will be done the manufacture and characterization of metal alloy 3 (ternary system) the Sn-Zn-Cu, the new alloy is expected to improve the weaknesses of the alloy Sn-Cu and Sn-Zn. Characterization metal alloy Sn-Cu-Zn used XRF (X-Ray Fluorescence) and XRD (X-Ray Diffraction) indicate the presence of metallic Sn, Cu and Zn in each metal alloy with a composition (wt%) Sn-0.8Cu, Sn-0.6Cu-10.4Zn dan Sn-0.5Cu-23.6Zn. Sn-0.5Cu-23.6Zn is metal alloy with the most potential as a replacement for Sn-37Pb, with the lowest melting point 204.13 °C, the pasty range is close to 9.33 ° C metal alloy Sn-37 Pb and the heat of fusion/ΔH 65.33 J/g lower than Sn-37Pb alloy. Surface characterization using SEM (Scanning Electron Microscopy) show the existence of phases rich in Sn, Cu-Zn and Zn-rich alloy surfaces supported by the data of EDS (Energy Dispersive X-Ray Spectroscopy)."