Edwin Arfiansyah
Perubahan Sifat Termal Akibat Waktu dan Kecepatan Pengadukan TiO2 dalam Parafin pada Sintesa Bahan Berubah Fasa Nano Komposit = Thermal Properties Change due to Stirring Time and Speed of TiO2 in Paraffin on the Synthesis of Nano Composite Phase Change Material
"Teknologi bahan berubah fasa (BBF) atau phase change material (PCM) merupakan
salah satu teknologi rekayasa bahan sangat luas manfaat dan perannya dalam aplikasi
penggunaan fitur manajemen termal yang dikenal dengan istilah “bahan cerdas”. Salah
satu teknik pembuatan BBF pengkondisi pasif berkinerja tinggi adalah dengan
menggabungkan bahan dasar BBF dengan bahan nano oksida logam TiO2 yang memiliki
sifat stabilitas termal yang sangat tinggi.
Tujuan penelitian ini untuk menganalisa perbandingan karakteristik sifat termal utama
nano komposit BBF parafin/TiO2 yang dibuat dengan proses in situ mekanik dengan
surfaktan sebagai pemacu dispersi karena variasi pengaruh waktu dan pengadukan pada
kecepatan tinggi.
Penelitian ini menggunakan prosedur eksperimental melalui pencampuran mekanik in
situ BBF berbasis parafin dan rutil Titanium dioksida (TiO2) 4 wt% untuk membentuk
Nano Komposit Bahan berubah fasa (NKB) dengan variasi pengadukan kecepatan tinggi
(700, 900 dan 1100 rpm pada 90°C selama 45, 60, dan 90 menit) dan dicampur dengan
Natrium Dodesil Sulfat (Sodium Dodecyl Sulphate (SDS)) sebagai dispersan dengan
mengaplikasikan premixing larutan polar (distilasi H20 + 4 wt% SDS dispersan) ke
larutan berbasis parafin non-polar (lilin parafin + 4 wt% TiO2) dengan perbdaningan 1:4,
kemudian didinginkan secara alami. Spektrum Fourier Transient Infrared (FTIR) dan pola
X-Ray Diffraction (XRD) menunjukkan ciri khas sistem komposit. tidak ada sistem
material baru yang tersusun. Bilangan gelombang khas komposit PW + TiO2 (2918 cm-1,
2851cm-1, 1471 cm-1, 720cm-1 dan 469 cm-1) terlihat pada FTIR, sedangkan puncak
intensitas tinggi 2θ = 21,4° dan 23,8 dan puncak intensitas rendah 27,4° dan 36,1°, pola
XRD dapat dikaitkan dengan kristal parafin monoklinik dengan difraksi bidang tipikal
(110) dan (200) dan TiO2. Sifat termal komposit diukur dengan menggunakan
Kalorimetri Pemindaian Diferensial. Temuan menunjukkan bahwa BBFberbasis parafin
memiliki kapasitas penyimpanan termal yang lebih tinggi sebesar 144,3 J/g dibandingkan
dengan nilai umumnya 104,5 J/g. Dengan Persamaan Patel diperoleh nilai konduktifitas
NKB-MY2 (Nano Komposit BBF Parafin/TiO2- Mekanik - 900rpm- 60 menit), sebesar
0,41 W/m.K dan NKB-SY2 (Nano Komposit BBF Parafin/TiO2- SDS- 900rpm -
60menit), sebesar 0,43 W/m.K yaitu meningkat 69% dan 75,6% dari BBF Parafin murni.
Pengamatan Scanning Electron Microscope menunjukkan dispersi cluster TiO2 yang
lebih baik (mengkilap, halus, bulat, dan menyebar). Hal ini menunjukan bahwa kecepatan
pengadukan dan suhu yang tepat dapat meningkatkan kapasitas untuk mengisolasi suhu.
Phase change material (PCM) technology is one of the most widely used materials
engineering technologies and its role in the application of thermal management features
known as "smart materials". One of the techniques for making high-performance passive
conditioning PCM is by combining PCM base material with TiO2 metal oxide nano
material which has very high thermal stability properties.
The purpose of this study was to analyze the comparison of the main thermal
characteristics of PCM paraffin / TiO2 nano composites made with a mechanical in situ
process using surfactants as dispersion promoters due to variations of time and at high
speed stirring.
This study used an experimental procedure through in situ mechanical mixing of paraffinbased
PCM and 4 wt% rutile titanium dioxide (TiO2) to form nano composite PCM with
high-speed stirring variations (700, 900 and 1100 rpm at 90° c for 45, 60, and 90 minutes)
and mixed with Sodium. Dodecyl Sulphate (SDS) as a dispersant by applying a polar
solution premixing (distillation H20 + 4 wt% SDS dispersant) to a non-polar paraffinbased
solution (paraffin wax + 4 wt% TiO2) in a ratio of 1: 4, then cooled naturally.
Fourier Transient Infrared (FTIR) spectra and X-Ray Diffraction (XRD) patterns showed
the characteristics of a composite system. no new material system was composed. The
typical wave numbers of the PW + TiO2 composite (2918 cm-1, 2851cm-1, 1471 cm-1,
720cm-1 and 469 cm-1) were observed in FTIR, while the high intensity peaks were 2θ =
21.4°, 23.8° and low intensity peaks of 27.4°, 36.1°, XRD patterns were attributed to
monoclinic paraffin crystals with typical plane diffraction (110) and (200) and TiO2. The
thermal properties of the composites were measured using Differential Scanning
Calorimetry. The findings indicated that paraffin-based PCM had a higher thermal
storage capacity of 144.3 J/g compared to the typical value of 104.5 J/g. With the Patel
equation, the conductivity value of NKB-MY2 (Nano Composite PCM Paraffin / TiO2-
Mechanical - 900rpm- 60 minutes) is 0.41 W / mK and NKB-SY2 (Nano Composite
PCM Paraffin / TiO2- SDS- 900rpm - 60min), is 0.43 W / mK, which is an increase of
69% and 75,6% of pristine Paraffin PCM. Scanning Electron Microscope observations
show better TiO2 cluster dispersion (shiny, smooth, round, and diffuse). This showed that
the stirring speed and the right temperature can increase the capacity to isolate
temperatures"
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2021
T-Pdf
UI - Tesis Membership  Universitas Indonesia Library
cover
Muhammad Farel Ferian
Pengaruh Durasi Penyimpanan Terhadap Kualitas DNA Biospesimen Kanker FFPE Yang Disimpan Di BioBank Riset FKUI-RSCM Tahun 2015-2018 = The Effect of Storage Period on DNA Quality of FFPE Cancer Biospecimen Stored in FKUI-RSCM Research BioBank in 2015-2018
"Dewasa ini perkembangan ilmu biologi molekular semakin berkaitan dengan peningkatan kebutuhan biospesimen manusia. DNA yang terkandung didalamnya dapat mendukung penemuan terobosan baru. DNA terkandung dalam jaringan awetan formalin-fixed and paraffin-embedded (FFPE) berpotensi menjadi sumber penelitian yang baik. BioBank Riset FKUI-RSCM menyimpan FFPE dari tahun 2014 untuk berbagai aplikasi salah satunya adalah penelitian. Maka itu diperlukan uji  kualitas FFPE milik BioBank Riset FKUI-RSCM sebagai dasar penelitian yang akurat. Tujuan: Penelitian ini bertujuan untuk mengetahui pengaruh durasi waktu penyimpanan FFPE yang disimpan di atas dan di bawah 2 tahun terhadap kualitas DNA yang diukur melalui paremeter kemurnian, konsentrasi, dan tingkat degradasi. Metode:Desain penelitian ini merupakan retrospektif menggunakan FFPE kanker jaringan di atas 2 tahun (N=20) dan di bawah 2 tahun (N=30) yang disimpan di BioBank Riset FKUI-RSCM. Dilakukan ekstraksi DNA menggunakan QIAamp DNA FFPE Tissue Kit. Digunakan spektrofotometer Nanodrop 2000 untuk menguji kemurnian DNA (rasio A260/A280) dan mengukur konsentrasi DNA total; Qubit fluorometer untuk mengukur konsentrasi DNA utuh; dan elektroforesis gel agarosa untuk melihat terjadinya degradasi DNA. Hasil: ecara keseluruhan tidak terdapat perbedaan kualitas DNA antara kedua kelompok. Pemisahan uji berdasarkan asal jaringan mendapatkan perbedaan rata-rata kemurnian DNA bermakna pada kelompok jaringan ovarium (p=0,034) serta perbedaan rata-rata konsentrasi DNA total (p=0,022) dan DNA utuh (p=0,008) bermakna pada kelompok jaringan serviks. namun tidak terdapat perbedaan rata-rata degradasi DNA (p=1,00). Simpulan: Durasi penyimpanan berpengaruh terhadap kemurnian DNA (jaringan ovarium), konsentrasi DNA total (jaringan serviks), dan DNA utuh (jaringan serviks), tetapi durasi penyimpanan tidak berpengaruh terhadap degradasi DNA.
......Development of molecular biology is associated with an increased need for human biospecimen. DNA contained within could support new discoveries. DNA in formalin-fixed and paraffin-embedded (FFPE) tissues have the potential to be a viable resource for research. BioBank Riset FKUI-RSCM has been storing them since 2014 for various application including research. Thus, quality check on their samples are needed as basis for accurate research.Objective this research aimed to study the effects of FFPE storage period stored for greater and lesser than 2 years on DNA quality measured by purity, concentration and degree of degradation. Methods This retrospective research used FFPE cancer tissue samples stored greater than 2 years (N=20) and lesser than 2 years (N=30) from various tissues stored in BioBank Riset FKUI-RSCM. DNA extraction is done using QIAamp DNA FFPE Tissue Kit. DNA purity (A260/A280 ratio) and total DNA concentration is measured using Nanodrop spectrophotometer; whole DNA is measured using Qubit Fluorometer; DNA degradation is observed by agarose gel electrophoresis. Results There were no overall significant mean differences in DNA quality of both groups. Analysis based on tissue origin found a significant mean difference of DNA purity in ovarium tissue group (p=0,034) as well as total DNA (p=0,022) and whole DNA (P=0,008) in cervix tissue group. However, there was no significant mean difference in DNA degradation (p=1,00). Conclusion: Storage period of FFPE significantly impacts DNA purity (ovaries), and total DNA (cervix) and whole DNA (cervix), however storage period does not significantly impact DNA degradation."
Depok: Fakultas Kedokteran Univeritas Indonesia, 2019
S-pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Algan Tian Mahatma
Konversi Asam Palmitat Menjadi Parafin Sebagai Bahan Baku Bioavtur Melalui Reaksi Deoksigenasi Dengan Katalis Bimetal Oksida NiMoO4/SBA-15 = Conversion Of Palmitic Acid Into Bio-Avtur Raw Material Through Deoxygenation Reaction With NiMoO4/SBA-15 Bimetallic Oxide Catalyst
"Bahan bakar fosil yang semakin terbatas dan disertai pemanasan global meningkatkan urgensi akan bahan bakar alternatif. Bioavtur merupakan bahan bakar yang dapat disintesis dari asam lemak seperti asam stearat (C18) dan asam palmitat (C16), sehingga dapat digunakan sebagai bahan bakar alternatif untuk mengurangi emisi gas buangan dari mesin pesawat. Pada penelitian ini disintesis nanokomposit NiMoO4/SBA-15 untuk mengubah asam palmitat menjadi parafin melalui reaksi deoksigenasi. SBA-15 disintesis dengan metode sol-gel, dan NiMoO4/SBA-15 dengan metode impregnasi kering. Sintesis NiMoO4/SBA-15 dilakukan dengan memvariasikan komposisi massa Ni:Mo, yaitu: 10:0, 2,5:7,5, 5:5, dan 7,5:2,5 serta variasi waktu, yaitu 150 dan 90 menit untuk diamati pengaruhnya terhadap struktur, %yield dan %konversinya. Uji katalitik dilakukan di dalam reaktor semi-batch­ 250 mL pada suhu 350 °C dan produk yang dihasilkan dianalisis dengan menggunakan GC-MS. Hasil analisis dengan variasi waktu menunjukkan reaksi dengan waktu reaksi 90 menit didapat baik %yield maupun %konversi berada di kisaran ~45% sedangkan pada waktu reaksi 150 menit didapat baik %yield maupun %konversi berada dikisaran ~60% dan katalis NiMoO4/SBA-15 (2,5:7,5) merupakan katalis paling optimum yang menghasilkan nilai %Yield (66.45%) dan %Konversi (73%) pada waktu reaksi 150 menit
......Fossil fuels that are increasingly limited and accompanied by global warming increase the urgency of alternative fuels. Bioavtur is a fuel that can be synthesized from fatty acids such as stearic acid (C18) and palmitic acid (C16), so that it can be used as an alternative fuel to reduce exhaust emissions from aircraft engines. In this research, NiMoO4/SBA-15 nanocomposite was synthesized to convert palmitic acid into paraffin through deoxygenation reaction. SBA-15 was synthesized by the sol-gel method, and NiMoO4/SBA-15 by the dry impregnation method. The synthesis of NiMoO4/SBA-15 was carried out by varying the mass composition of Ni:Mo, namely: 10:0, 2.5:7.5, 5:5, and 7.5:2.5 and varying the time, namely 150, 120, and 90 minutes to observe the effect on structure, % yield and % conversion. The catalytic test was carried out in a 250 mL semi-batch reactor at 350 °C and the resulting product was analyzed using GC-MS. The results of the analysis with variations in time showed that the reaction with a reaction time of 90 minutes obtained both % yield and % conversion in the range of ~45% while in the reaction time of 150 minutes both % yield and % conversion were in the range of ~ 60% and the catalyst NiMoO4/SBA-15 (2.5:7.5) is the most optimum catalyst that produces % Yield (66.45%) and % Conversion (73%) at a reaction time of 150 minutes."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2022
S-pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Adhityo Nugroho Edisworo
Pengaruh surfaktan anionik terhadap interaksi permukaan minyak dan air = Influence of anionic surface active agent surfactant on the interactions between oil and water interfaces
"Studi prihal pengaruh surfaktan anionik terhadap interaksi permukaan minyak dan air dilakukan dengan cara membandingkan volume segmen-segmen dua buah tetesan yang terbuat dari dua bahan yang berbeda yaitu larutan sodium dodesil sulfat 0.01 molar dan air suling. Penelitian ini dilakukan didalam tabung yang terbuat dari plexiglass yang dirancang oleh penulis bersama tim. Penelitian ini dilakukan dalam dua tahap, yang pertama adalah perancangan tabung percobaan dan fabrikasi tabung percobaan. Tahap kedua adalah pemilihan bahan kimia yang cocok dan di tahap kedua ini percobaan surfaktan anionik dilakukan. Bahan-bahan yang digunakan dalam penelitian ini adalah air suling, minyak paraffin, dan sodium dodesil sulfat. Tabung yang digunakan dalam percobaan ini terbuatdari plexiglass dan memiliki penampang tampak atas berbentuk bujur sangkar untuk meminimalisasi distorsi foto kedua jenis tetesan.
Penelitian ini menemukan bahwa sodium dodesil sulfat dengan konsentrasi 0.01 molar mampu menurunkan tegangan permikaan tetesan air suling sehingga menghasilkan bentuk tetesan yang ellipsoid. Lebih lagi, sifat amfifilik yang dimiliki oleh sodium dodesil sulfat diperkuat kecendrungan lipofiliknya untuk menempel pada minyak paraffin karena bertambahnya luas penampang tetesan yang semula berbentuk bola menjadi ellipsoid akibat berkurangnya tegangan permukaan tetesan. Rasio volume segmen-segmen kedua tetesan menunjukkan bahwa sodium dodesil sulfat memiliki kecendrungan untuk sedikit lebih lipofilik daripada hidrofilik.
......The study of the influence of anionic surface active agent (surfactant) on the interactions between oil and water interfaces was done by comparing the volumes of droplet which were divided into segments in a controlled environment using a column designed by the team. The experiment involves two phases; the first were column design and fabrication while the next were the selection of suitable chemicals and the commencement of the anionic surface active agent experiment. The substances used in this experiment were deionised water, paraffin oil, and sodium dodecyl sulphate 0.01 molar solution. The column was made of plexiglass with rectangular cross-section to minimise optical distortion of the droplet image.
It was found that sodium dodecyl sulphate solution reduces the surface tension of deionised water of droplet resulting in an ellipsoid shaped droplet. In addition to the amphiphilic nature of sodium dodecyl sulphate; the ellipsoid shape of sodium dodecyl sulphate droplet caused by the reduced surface tension has greater surface area compared to the spherical deionised water droplet which further increased its affinity toward paraffin oil. The volumetric ratio of the droplet segments suggest that sodium dodecyl sulphate has a slight tendency to be more lipophilic that hydrophilic."
Depok: Fakultas Teknik Universitas Indonesia, 2014
S55061
UI - Skripsi Membership  Universitas Indonesia Library
cover
Muh Nur Afif Luthfi
Konversi Asam Palmitat menjadi Parafin melalui Reaksi Deoksigenasi dengan Katalis CoMoO4/SBA-15 = Conversion of Palmitic Acid into Paraffin Through Deoxygenation Reaction with CoMoO4/SBA-15 Catalyst
"Dalam penelitian ini, nanokomposit CoMoO4/SBA-15 disintesis sebagai katalis bimetal untuk mengubah asam lemak menjadi parafin melalui reaksi deoksigenasi tanpa kehadiran hidrogen atau pelarut. SBA-15 disintesis menggunakan metode sol-gel, dan CoMoO4/SBA-15 (Co:Mo = 5:5 wt%) dibuat melalui metode impregnasi kering (incipient wetness), bersama dengan katalis monometalik Co3O4/SBA-15 ( 10% berat Co), dan MoO3/SBA-15 (10% berat Mo) untuk mengamati pengaruhnya terhadap struktur dan yield serta selektivitas produk hidrokarbon. Difraktogram sinar-X dan mikroskop elektron transmisi menegaskan bahwa proses impregnasi kering partikel logam tidak mengubah struktur heksagonal pendukung katalis, SBA-15. Analisis fisisorpsi isoterm N2 menunjukkan bahwa katalis hasil sintesis memiliki struktur meso dengan kisaran diameter pori 5-6 nm. Uji katalitik dilakukan dalam reaktor semi-batch pada suhu 350 °C selama 2 jam, dan produk dianalisis menggunakan metode Kromatografi Gas – Spektroskopi Massa (GC-MS). Terlihat bahwa komponen utama produk hidrokarbon dari reaksi deoksigenasi adalah pentadekana, salah satu komponen dalam bahan bakar penerbangan. Aktivitas katalitik pada proses deoksigenasi menunjukkan bahwa MoO3/SBA-15 memiliki rendemen tertinggi (94,87%) dan Co3O4/SBA-15 memiliki selektivitas tertinggi untuk C-15 (86,32%). Kondisi reaksi optimal untuk katalis CoMoO4/SBA-15 adalah dengan jumlah katalis 5% wt, dan suhu reaksi 375 °C.
......In this study, CoMoO4/SBA-15 nanocomposite was synthesized as a bimetallic catalyst for converting fatty acids into paraffin through a deoxygenation reaction without the presence of hydrogen or solvent. SBA-15 was synthesized using the sol-gel method, and CoMoO4/SBA-15 (Co:Mo = 5:5 wt%) was prepared through dry impregnation (incipient wetness) method, along with monometallic catalysts Co3O4/SBA-15 (10 wt % of Co), and MoO3/SBA-15 (10 wt % of Mo) to observe their effect on the structure and yield and selectivity of the hydrocarbon products. X-ray diffractograms and transmission electron microscopy confirmed that the dry impregnation process of metal particles did not change the hexagonal structure of the catalyst support, SBA-15. Physisorption analysis of the N2 isotherm shows that the as-synthesized catalyst had a meso-structure with a pore diameter range of 5-6 nm. The catalytic test was carried out in semi-batch reactor at 350 °C for 2 hours, and the product was analyzed using Gas chromatography-mass spectroscopy (GC-MS) method. It is shown that the major component of the hydrocarbon product from the deoxygenation reaction is pentadecane, one of components in aviation fuel. The catalytic activity in the deoxygenation process reveals that MoO3/SBA-15 has the highest yield (94.87%) and Co3O4/SBA-15 has the highest selectivity for C-15 (86.32%). The optimal reaction conditions for the CoMoO4/SBA-15 catalyst was 5% by weight of the catalyst, and the reaction temperature was 375 °C."
Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2022
S-pdf
UI - Skripsi Membership  Universitas Indonesia Library
cover
Gadia Ayundya Duhita
Efektivitas Kulit Ikan Tilapia Sebagai Xenograft Dibandingkan dengan Kasa Jenuh Paraffin-Vaselin pada Luka Bakar Full Thickness Pascadebridement Eksisional = Efficacy of Tilapia Fish Skin Xenograft Compared to Paraffin-Vaseline Impregnated Gauze in Full Thickness Burn After Excisional Debridement
"Latar belakang: Pada negara maju, terapi pada luka bakar mayor saat ini telah bergeser dari eksisi segera dan standur kulit menjadi eksisi bertahap dan penutupan luka sementara dengan xenograft, yang tidak tersedia di Indonesia. Saat ini, perawatan luka pada luka bakar masih menggunakan kasa jenuh paraffin-vaselin. Studi ini merupakan studi preliminary untuk clinical trial mengenai kulit ikan tilapia sebagai xenograft. Dilakukan evaluasi terhadap waktu yang diperlukan untuk mencapai dasar luka yang baik, frekuensi redebridement, dan frekuensi penggantian balutan.
Metode: Studi preliminary ini merupakan clinical trial terrandomisasi dengan kasa jenuh paraffin-vaselin sebagai pembanding, dengan analisis intention to treat. Sampel pada studi ini adalah ekstremitas atas atau bawah pasien luka bakar akut dewasa, usia 18-60 tahun, dengan luas area luka bakar 20-40%; yang terdapat luka bakar full thickness. Kedua sisi harus dapat dibandingkan, evaluasi luka dilakukan tiap kali dilakukan penggantian balutan.
Hasil: Total 7 sampel didapatkan dari 4 pasien. Tidak didapatkan adanya reaksi alergi pada semua subjek, baik berdasarkan klinis dan hasil laboratorium. Dua subjek meninggal dunia sebelum dilakukan penggantian balutan pertama, sehingga tidak dapat dilakukan evaluasi luka. Tidak ada perbedaan waktu untuk mencapai bed luka yang baik dan frekuensi redebridement antar kedua kelompok. Ekstremitas dengan balutan kulit ikan tilapia xenograft membutuhkan frekuensi penggantian balutan yang lebih sedikit secara signifikan.
Kesimpulan: Xenograft kulit ikan tilapia dapat digunakan sebagai dressing alternative pada luka bakar. Studi lebih lanjut sangat dibutuhkan.
......Background: In developed countries, major burn treatment have shifted from early excision and skin grafting to staged excision and temporary coverage with xenograft, which were not available in our country. Paraffin-impregnated gauze is still utilized in most of our burn injury cases. Xenografts have been proven to be superior than non –biological dessings. This study was a preliminary to clinical trial of tilapia fish skin xenograft that we put together locally. We evaluated the efficacy based on reduction of time to well granulated wound bed, redebridement frequency and wound dressing change frequency.
Method: This preliminary study is a randomized clinical trial, with paraffin-impregnated gauze as the comparison, with intention to treat analysis. Samples of the study were upper or lower limb pairs of adults, aged 18-60 year old, acute burn patients with total body surface area of burn ranged from 20-40%; which contains full thickness burn. The injury on both sides of the lim pairs have to be comparable. The wound was evaluated every time the dressing was changed.
Result: Total of 7 samples were obtained from 4 subjects. There was no evidence of allergic reaction on all subjects , either clinically or from laboratory examinations. Two subjects passed away before the first dressing change, thus the wound cannot be evaluated. There was no difference in time to well granulated wound bed and redebridement frequency between groups. Limbs treated with tilapia fish skin xenograft significantly require less frequent dressing change.
Conclussion: The tilapia fish skin xenograft appears to be a legible alternative to paraffin impregnated gauze. Further study is strongly advised."
Jakarta: Fakultas Kedokteran Univesitas Indonesia, 2020
SP-pdf
UI - Tugas Akhir  Universitas Indonesia Library