Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
ABSTRAK Beton merupakan salah satu material yang mengalami perkembangan signifikan pada industri konstruksi. Salah satu inovasi material beton adalah beton ringan dengan penggunaan agregat kasar ringan berbahan dasar polypropylene PP . Penggunaan beton ringan memungkinkan pengurangan berat sendiri sehingga elemen struktur yang didesain bisa lebih efisien dan ekonomis. Penulis menggunakan agregat halus Cimangkok dan melaksanakan pengujian berat jenis, berat isi, dan analisis saringan. Rancang campur yang digunakan adalah metode volume dengan perbandingan semen : pasir : agregat : air adalah 1 : 2 : 2.6 : 0.9. Penulis merencanakan pengecoran benda uji silinder 15x30 cm dan benda uji balok 7x10x150 cm. Benda uji balok terdiri dari 3 jenis, yaitu P polos , T tulangan tarik , dan K tulangan tarik, tekan, dan sengkang . Seluruh tulangan dan sengkang yang dipakai berdiameter 4 mm. Benda uji balok diuji lentur dengan menggunakan dua metode yaitu lentur murni dan lentur dengan pengaruh geser. Kapasitas momen nominal untuk balok T dan K adalah masing-masing 1.29 kNm dan 2.38 kNm. Berat isi beton ringan adalah 1,690.98 kg/m3. Kuat tekan fc rsquo; aktual silinder umur 28 hari untuk pengujian destruktif dan UPV ultrasonic pulse velocity adalah masing-masing 22.63 MPa dan 26.11 MPa. Kuat tekan aktual balok menggunakan UPV adalah 20.58 MPa. Pada pengujian lentur murni dan lentur dengan pengaruh geser, balok K menunjukkan kurva kekakuan yang relatif besar dibanding balok T dan balok P. Secara umum, pengujian lentur dengan geser menyebabkan balok mengalami keruntuhan terlebih dahulu dibandingkan dengan pengujian lentur murni. Hal ini disebabkan oleh besarnya gaya dalam momen lentur dan gaya geser yang bekerja maksimum pada tengah bentang.

---

ABSTRACT Concrete is one of the most developed material in construction industry. This thesis portrays innovation in structural lightweight concrete by using lightweight polypropylene PP aggregates. The use of lightweight concrete has been usually predicated on the reduction of its dead load so the structural elements can be designed efficiently. Researcher chose Cimangkok sand as fine aggregates and performed specific gravity, unit weight, and sieve analysis testing. Volume based mix design is used with ratio 1 2 2.6 0.9 cement fine aggregates coarse aggregates water . Concrete batching was performed to mold cylinder 15x30 cm and beam 7x10x150 cm. Beams are designed into 3 categories, P without rebar , T single rebar at bottom , and K confined rebar . 4 mm diameter rebars are used for specimen T and K. Beams are tested flexurally in 2 methods, pure bending and bending with shear. Nominal moment capacity for beam T and K are respectively 1.29 kNm and 2.38 kNm. The average unit weight of concrete cylinder speciments is 1,690.98 kg m3. 28 days compressive strength for destructive and UPV ultrasonic pulse velocity tests are respectively 22.63 MPa and 26.11 MPa. 28 days equivalent compressive strength for beam using UPV test is 20.58 MPa. In pure bending and bending with shear testing, beam K shows greater flexural rigidity than beam T and beam P. Bending with shear in beams caused early failure rather than pure bending. The failure occured due to the combination of bending moment and shear force at middle span.

Abstrak :
This paper presents the structural behavior of newly-developed hybrid structural insulated panels (SIPs) formed by incorporating lignocellulosic composites—jute fiber composite (JFC) and medium-density fiber (MDF)—as intermediate layers between aluminum skin and an expanded polystyrene (EPS) core. The investigation was conducted as an experimental work. A four-point bending load was performed to create pure bending conditions, and the samples were prepared in accordance with ASTM C 393-00 standards. Testing was performed using a 100 kN servo-hydraulic machine with a loading rate of 5 mm/min. The results show that the incorporation of intermediate JFC or MDF layers enhanced the flexural behavior of the SIPs. The ultimate loads of hybrid SIPs with JFCs or MDF were, respectively, approximately 62.59% and 168.58% higher than the ultimate load achieved by SIPs without intermediate layers. Hybrid SIPs exhibited a much larger area under the load-deflection curve than those of conventional SIPs; this points to the toughness of the material and its ability to sustain larger compression strain prior to reaching their ultimate loads, which prevents them from prematurely failing under buckling or indentation.

Abstrak :
Pertumbuhan penduduk di Indonesia semakin bertambah tiap tahunnya, mengakibatkan kebutuhan akan rumah tinggal juga meningkat. Hal tersebut akan berdampak pada penggunaan material beton sebagai bahan utama dari dalam pembuatan komponen struktural maupun non struktural dari rumah bangunan. Dengan keterbatasan sumber daya alam sebagai bahan penyusun beton, maka diperlukan pemanfaatan limbah yang dapat digunakan sebagai bahan penyusun beton. Berdasarkan penelitian yang telah dilakukan sebelumnya didapatkan bahwa dengan penggunaan limbah cangkang kelapa sawit sebagai pengganti agregat kasar dalam campuran beton ringan mendapatkan hasil kuat tekan berkisar antara 20-23 MPa, nilai kuat tekan tersebut tergolong beton struktural. Beton ringan cangkang kelapa sawit tersebut dapat diaplikasikan pada komponen struktural yaitu pelat lantai, dimana pada sebuah bangunan yang mempunyai volume paling besar dibandingkan komponen lainnya yaitu pelat lantai. Penelitian ini menggunakan proporsi campuran beton pada penelitian yang telah dilakukan sebelumnya tetapi tidak menggunakan bahan tambah untuk diaplikasikan pada pelat beton sebagai komponen struktural dalam rumah tinggal. Dengan ukuran sampel pelat yaitu 65x125x300 cm sebanyak 3 sampel. Hasil yang didapatkan berupa respon mekanik akibat lentur murni yang terjadi pada pelat beton ringan cangkang kelapa sawit. ......In accordance with the high demand of building and housing materials, the use of alternative materials from industrial waste is challenging nowadays in Indonesia. As the production of palm oil in Indonesia is large, the solid end from oil manufacturing process is also high. This by products is often called Oil Palm Shell (OPS). In this research, the solid OPS is used as coarse aggregate material to replace the natural ones. Previous research in laboratory shows that the structural requirements of concrete compressive strength is achieved, around 20-23 MPa. In this paper, study on larger element structure, such as slab is performed. To do so, a campaign of experiment was conducted on three samples of identical slab with 12 × 60 × 300 cm3 of size. Mechanical response due to bending that occurs in OPS lightweight concrete slab is presented. Investigation on the slab is emphasized on the pure bending area.