Hasil Pencarian  ::  Simpan CSV :: Kembali

"ABSTRACTMost commodities in agriculture produce biomass that can be used as an alternative energy source. One of the biomass that is abundant in Indonesia is rice husks which has high levels of lignocellulose. The aim of this study was to use carbon dioxide as the pyrolysis carrier gas and observe the resulting product distribution. The type and composition of the catalyst and operating temperature can affect the value of the conversion and selectivity of end product. For this study, the catalysts used is Nickel-alumina (Ni/Al2O3). The method used is catalytic pyrolysis. Biomass pretreatment given in the form of drying and enumeration, and then inserted into the pyrolysis reactor. Liquid products from pyrolysis are incorporated into the catalytic reactor to be converted and then analyzed by its content of compounds using chromatography (GCMS).

---

ABSTRACTSalah satu biomassa yang berlimpah di Indonesia yang bias digunakan untuk energy alternative adalah sekam padi. Sekam padi mengandung lignoselulosa dengan konsentrasi tinggi. Tujuan dari penelitian ini adalah menggunakan karbon dioksida sebagai Carrier Gas dalam proses pirolisis dan mengamati distribusi produk hasil Catalytic Cracking. Tipe dan kandungan katalis yang digunakan dan temperature operasi akan memengaruhi konversi dan perolehan dari produk. Katalis yang digunakan pada studi ini adalah Nickel-alumina (Ni/Al2O3). Metode yang digunakan adalah pirolisis dan catalytic cracking. Pretreament Biomassa seperti menggunting dan memblender, akan dilakukan untuk mengurangi ukuran dari sekam padi, lalu hasilnya akan di lakukan proses pirolisis. Minyak cair dari pirolisis akan digunakan untuk proses catalytic cracking, Lalu gas hasil proses catalytic cracking akan dianalisis dengan menggunakan GC/MS."

"Limbah sekam padi mengandung selulosa dengan jumlah yang besar yaitu sekitar 50%. Asam levulinat merupakan platform chemical berbagai industri kimia yang dapat diperoleh dari reaksi dehidrasi selulosa yang merupakan hasil hidrolisis dari selulosa. Dalam penelitian Chen (2011), Mn/ZSM-5 merupakan katalis heterogen yang dapat meningkatkan % yield asam levulinat yang terbentuk dalam sistem reaksi mirip Fenton. Selulosa dari limbah sekam padi ini dapat diisolasi melalui proses pretreatment, yaitu dewax dan delignifikasi. Penggunaan NaOH 10% masih menghasilkan kandungan lignin yang tinggi sehingga dibutuhkan proses delignifikasi lanjutan menggunakan NaOCl. Hasil dari proses pretreatment kemudian dihidrolisis dengan H3PO4 20%, 30%, dan 40% dengan dikatalisis oleh Mn/ZSM-5 mesopori. Diperoleh asam levulinat pada variasi konsentrasi H2O2 30% dengan konsentrasi asam levulinat 11,9585 mg/L. Sekam padi yang didelignifikasi lebih lanjut dengan NaOCl menghasilkan selulosa dengan karakter Iα dan Iβ. Tidak diperoleh asam levulinat dari hasil reaksi konversi selulosa dari sekam padi yang didelignifikasi dengan NaOCl dengan konsentrasi H3PO4 40%. Dan diperoleh asam levulinat pada reaksi konversi selulosa dari limbah sekam padi yang didelignifikasi dengan NaOH.

---

Rice husk waste contains high number of cellulose, it’s about 50%. Levulinic acid is a platform chemical a variety of chemical industry that can be obtained from dehydration reaction of cellulose that is a hydrolysis product of cellulose. On the research of Chen (2011), Mn/ZSM-5 is a heterogeneous catalyst that can increase the % yield levulinic acid formed in the reaction system similar Fenton. Cellulose from rice husk waste can be isolated through pretreatment process, which dewax and delignification. The use of NaOH 10% still produces high number of lignins, so continued delignification is needed and the use of NaOCl is suggested.

The results of the pretreatment process then hydrolyzed with H3PO4 20%, 30%, and 40% which is catalyzed by mesoporous Mn/ZSM-5. Levulinic acid is produced with concentration of 11,9585 mg/L at the concentration of H2O2 is 30%. Rice husks which is delignified with NaOCl produces cellulose Iα and Iβ. Levulinic acid isn’t produced from the reaction of cellulose conversion from rice husks which is delignified with NaOCl and concentration of H3PO4 is 40%. And levulinic acid was formed on the reaction of cellulose conversion in which the cellulose obtained by deliginifying the rice husks with NaOH."

"Sintesis nanokomposit dari nanoselulosa sekam padi dan zat anorganik telah dibuat. Digunakan TiO2 sebagai zat anorganik sehubungan dengan sifatnya yang green chemistry. Selulosa di isolasi dari sekam padi dengan tahapan maserasi lemak dengan toluena : etanol(2:1). Penghilangan hemiselulosa dan lignin dengan menggunakan NaClO2 1,4% pH asam. Rendemen selulosa yang diperoleh adalah 46,169 % untuk metode I dan 31,178 % untuk metode II. Spektrum FTIR selulosa menunjukkan hilangnya lignin pada bilangan gelombang 1750 cm-1 untuk selulosa metode I sedangkan selulosa metode II masih terdapat lignin. Indeks kristalinitas dari selulosa diperoleh dari analisis XRD sebesar 60,265% untuk selulosa I sedangkan selulosa II 53,78%. Rendemen nanoselulosa yang disintesis dari selulosa sekam padi menurun dengan meningkatnya konsentrasi asam sulfat. Indeks Kristalin dari nanoselulosa yang diperoleh dari analisis XRD sebesar 80% untuk konsentrasi asam sulfat 60%. Analisis dengan SEM menunjukkan morfologi permukaan nanoselulosa yang halus merata. Analisis dengan TEM menunjukkan ukuran partikel yang cukup baik dengan naiknya konsentrasi asam sulfat. Ukuran yang terbaik di peroleh dengan menggunakan asam sulfat 60% yaitu 100 x 30 nm. Nanokomposit dapat diperoleh dengan impregnasi zat anorganik TiO2 pada nanoselulosa, hal ini ditunjukkan dengan FTIR dan TEM.

---

Synthesis of cellulose rice husk nanocomposite and inorganic substances have been made. TiO2 is used as inorganic substance with respect to the nature of green chemistry. Cellulose in isolation from rice husk with maceration stage fat with toluene:ethanol (2:1). The elimination of hemicellulose and lignin by using NaClO2 1.4% acidic pH. The yield of cellulose obtained was 46.169% to of the methods I and 31.178% to the method II. FTIR spectra at wave number 1750 cm-1 showed a loss of lignin cellulose for method I while the cellulose method II still contained lignin. Crystallinity index of cellulose obtained from XRD analysis of 60.265% for the first cellulose while the cellulose II 53,78%. The yield synthesized nanocellulose from rice husk cellulose decreased with increasing concentrations of sulfuric acid. Crystalline index of nanocellulose obtained from XRD analysis of 80% to 60% concentration sulfuric acid. Analysis by SEM showed a smooth surface morphology nanoselulosa evenly. Analysis by TEM showed the particle size is pretty good with the increasing concentration of sulfuric acid. The best size is obtained by using sulfuric acid 60%, 100 x 30 nm. Nanocomposite can be obtained by impregnating an inorganic substance TiO2 on nanocellulose, as shown by FTIR and TEM."