Hasil Pencarian  ::  Simpan CSV :: Kembali

Abstrak :
Aplikasi dari baja perkakas JIS SKD 11 sebagai material cetakan amatlah memegang peranan strategis dalam dunia industri. Agar diperoleh baja perkakas kualitas tinggi, maka terus dilakukan berbagai penelitian, salah satu caranya adalah dengan mengatur perlakuan panas. Pada penelitian ini, material baja perkakas diatur perlakuan panasnya dengan Quenching Partitioning Tempering. Dengan variabel yang digunakan adalah perubahan temperatur perlakuan panas yang dilakukan dengan menahan temperatur kuens pada suhu 100oC dan 150oC yaitu antara suhu Ms dan Mf maka akan diketahui pengaruhnya terhadap sifat mekanis, yaitu kekerasan, laju aus, perubahan dimensi serta struktur mikro material baja perkakas JIS SKD 11. Dalam penelitian ini disimpulkan dengan perlakuan Quenching Partitioning Tempering memberikan pengaruh sifat mekanis dan mikrostruktur baja JIS SKD 11. Nilai kekerasan baja pada perlakuan Quenching Partitioning Tempering (QPT) 950/100 oC pada penelitian ini sanggup mencapai nilai kekerasan 64 HRC. Pada perlakuan panas Quenching Partitioning Tempering (QPT) sifat mekanis kekerasan akan turun bila mana temperatur partitioning bertambah. Perubahan dimensi setelah perlakuan panas pada Quenching Tempering (QT) dan QPT mengalami penyusutan 0.02 mm sedangkan pada perlakuan panas Quenching Partitioning (QP) perubahan dimensi mengalami penambahan/mengembang 0.02 mm. Pada proses QP dan QPT terbentuk fasa martensit dan austenit sisa. ......Application of JIS SKD 11 tool steel as the mold and dies material is very important role in many startegic industries. In order to obtain a high quality tool steel , then continued to do various studies, one way is to set the heat treatment. In this study, tool steel material is regulated by the heat treatment of Quenching Partitioning Tempering (QPT). The variable used is the change of temperature of heat treatment done by holding the temperature quenching at temperature of 100 oC and 150 oC at which temperature between Ms and Mf it will determine its effect on mechanical properties, namely hardness, wear rate, dimensional changes and microstructure of materials tool steel JIS SKD 11. In this study, it is concluded that treatment of QPT influence mechanical properties and microstructure of steel JIS SKD 11. Hardness value of the steel in the treatment of QPT at 950/100 °C in this study could achieve a hardness value of 64 HRC. In the heat treatment of QPT mechanical properties of hardness will drop when partitioning increases. Dimensional change after heat treatment of Quenching Tempering (QT) and QPT shrinkage 0.02 mm, while the heat treatment Quenching Partitioning (QP) experienced a change in the dimensions of the addition 0.02 mm. In the process of QP and QPT, martensite and retained austenite phase are formed.

Abstrak :
Teknik pengaplikasian dari aluminium yang cukup menyita perhatian adalah penggunaan dari material aluminium dalam proses die casting. Semakin banyak komponen yang dapat diproduksi dengan menggunakan sebuah cetakan, maka biaya produksi akan semakin rendah. Oleh karena itu, umur pakai sebuah cetakan merupakan faktor penting dalam proses die casting. Namun disisi lain adanya kendala mengenai biaya dari cetakan die casting yang relatif tinggi yaitu mencapai 20% dari biaya produksi total pada industri aluminium die casting. Disamping itu adanya suatu kendala lain di dalam cetakan die casting yang dapat menurunkan produktivitas yaitu adanya kerusakan cetakan yang disebabkan oleh die soldering yang penyebabnya adalah kontak langsung pemukaan dengan logam cair. Terjadinya fenomena Die soldering adalah reaksi kinetik yang tinggi antara besi dan aluminium, dimana besi memiliki afinitas yang sangat tinggi terhadap aluminium sehingga mengakibatkan menempelnya aluminium cair ke permukaan material cetakan. Dalam penelitian ini sampel yang digunakan baja H13 dengan perlakuan over tempering (suhu temper 6000C) yang dicelupkan dalam paduan Al-7%Si dan Al-12%Si yang mengandung 0.1%, 0.3%, 0.5%, dan 0.7%Mn dengan waktu kontak 30 dan 50 menit pada temperatur 700oC. Dalam penelitian ini dihasilkan pembentukan dua lapisan intermetalik pada permukaan baja H13, yaitu compact layer yang merupakan fasa padat, dan broken layer yang merupakan fasa semi padat. Hasil dari penelitian ini menunjukan bahwa Baja H13 dengan perlakuan normal tempering (suhu temper 5500 C) memiliki kekerasan yang lebih tinggi dibandingkan dengan baja H13 dengan perlakuan over tempering (suhu temper 6000C) dan baja H13 dengan kondisi annealed. penambahan unsur Mn pada Al-7%Si dan Al-12%Si tidak berpengaruh terhadap kekerasan pada lapisan intermetalik. Kekerasan compact layer lebih tinggi dibandingkan dengan kekerasan pada broken layer. Kemudian hasil penelitian yang juga didapat yaitu semakin tinggi kadar dari Mn maka kecenderungan dari compact layer dan broken layer pada paduan Al-12%Si dan Al-7%Si akan berkurang. ......Engineering application for aluminum sufficient attention is uses for aluminum in the die casting process. More can be manufactured using a mold, then lower the production cost. Therefore, shelf life of a mold is an important factor in the die casting process. But on the other hand there is constraint on the cost of die casting mold which is relatively high, reaching 20% for total production cost on the aluminum die casting industry. Besides, there is another obstacle in a die casting mold which can lower productivity is the existence of mold damage caused by the die soldering is the cause is direct contact with molten metal surface. Die soldering is the occurrence of the phenomenon of high kinetic reaction between iron and aluminum, where the iron has a very high affinity to the aluminum so that the resulting liquid to the surface attachment of the aluminum mold material. In this research, samples used for H13 steel treated with over-tempering (tempering temperature 6000C) dipped into the molten in the alloy Al-7% Si and Al-12% Si containing 0.1%, 0.3%, 0.5% and 0.7% Mn with contact time 30 and 50 minutes at a temperature of 700oC. Results In this research, formation of two intermetallic layer on the surface of H13 steel, the compact layer which is a solid phase, and broken layer, which is a semi-solid phase. Results from this research showed that treatment of normal H13 steel tempering (tempering temperature of 5500C) has a higher hardness than the H13 steel treated with over-tempering (tempering temperature 6000C) and H13 steel with annealed condition. And the addition of Mn element in Al-7% Si and Al-12% Si no effect on the violence in the intermetallic layer. Compact layer hardness is higher compared with the violence in the broken layer. Later research also shows that the higher the concentration of Mn has a tendency of the compact layer on the alloy Al-12% Si and Al-7% Si will be reduced.

Abstrak :
[ABSTRAK
KWh meter prabayar 1 phasa merupakan kWh meter elektronik dengan sistem pelanggan harus mendeposit kWh sebelum dapat menggunakan energi listrik. KWh meter prabayar memiliki tingkat akurasi yang lebih baik dibanding kWh meter elektromekanik dan tersusun atas sensor arus, sensor tegangan, rangkaian pengkondisi sinyal dan mikrokontroller. Sistem penginderaan arus menggunakan sistem double sensing pada phasa dan netral. Keluaran dari sensor arus akan dibandingkan dan diambil nilai tertinggi yang digunakan sebagai perhitungan energi listrik. KWh meter prabayar mampu mengukur hingga harmonisa ke-15 dan dilengkapi anti tempering. Fitur yang dimiliki kWh meter prabayar ini pada aplikasinya ditemukan permasalahan yaitu kWh meter tetap mengukur pada keadaan MCB off atau tanpa beban. Kejadian tersebut ditemukan pada pelanggan yang memasang sistem pentanahan (grounding) pada instalasi kWh meter dan instalasi bangunan. Dari permasalahan yang timbul tersebut maka perlu dilakukan penelitian pengaruh sistem pentanahan terhadap kesalahan pengukuran pada kWh meter prabayar.

---

ABSTRACT One phase prepaid energy meter is an electronic energy meter with system customers must deposit kWh before customers can use electrical energy. Prepaid energy meter have an accuracy rate of better than electromechanical energy meters and is composed of the current sensor, voltage sensor, signal conditioning circuit and microcontroller. Current sensing system uses a system of double sensing the phase and neutral. The Output of the current sensor will be compared and taken the highest value is used as the energy calculations. Prepayment energy meter capable of measuring up to the 15th harmonic and equipped with anti tempering. Fitur owned prepayment energy meter is the application found that problems remain energy meter gauge on the condition MCB off or no load. The incident was found at customers who install the grounding system in energy meter installation and installation of the building. The problems arising from it is necessary to study the effect of the grounding system of the measurement errors on prepayment energy met, One phase prepaid energy meter is an electronic energy meter with system customers must deposit kWh before customers can use electrical energy. Prepaid energy meter have an accuracy rate of better than electromechanical energy meters and is composed of the current sensor, voltage sensor, signal conditioning circuit and microcontroller. Current sensing system uses a system of double sensing the phase and neutral. The Output of the current sensor will be compared and taken the highest value is used as the energy calculations. Prepayment energy meter capable of measuring up to the 15th harmonic and equipped with anti tempering. Fitur owned prepayment energy meter is the application found that problems remain energy meter gauge on the condition MCB off or no load. The incident was found at customers who install the grounding system in energy meter installation and installation of the building. The problems arising from it is necessary to study the effect of the grounding system of the measurement errors on prepayment energy met]