Hasil Pencarian  ::  Simpan CSV :: Kembali

"Logam niobium, tantalum dan logam tanah jarang LTJ merupakan logam yang sering digunakan dalam berbagai aplikasi. Terak timah dijadikan sumber sekunder untuk mendapatkan Nb, Ta dan LTJ. Dalam penelitian ini akan dilihat pengaruh dari pelindian asam dengan HClO4 pada konsentrasi 0,1 M; 0,4 M; 0,8 M selama 2 jam dengan temperatur 25 C terhadap terak timah. Sampel terak timah yang digunakan mengandung Nb 0,47; Ta 0,23; La 0,13; Ce 1,0.57; Th 0,15. Pengujian XRF dilakukan untuk melihat kadar pada residu hasil dari proses pelindian dimana kadar maksimum dari Nb 1,28; Ta 0,79; La 0,59; Ce 3,72; Th 0,38. Proses pelindian dengan HClO4 dapat melarutkan CaO, Al2O 3, dan Fe2O3. Hasil pada pengujian ICP-OES menunjukkan kadar maksimum Nb 0,208 ppm dan Th 0,138 ppm, sedangkan dari pengujian AAS kadar dari Ca dan Fe semakin meningkat saat konsentrasi HClO4 semakin besar.

---

Niobium, tantalum and rare earth elements REE are often used in many applications. Tin slag is a secondary source for Nb, Ta and REE. In this research will be seen the effect of acid leaching with HClO4 at concentration 0.1 M 0.4 M 0.8 M for 2 hours with temperature 25 C to tin slag. The tin slag sample used contained 0.47 Nb Ta 0.23 La 0.13 Ce 1.57 Th 0.15.

XRF test was performed to see the grade of residue result from leaching process where maximum content of Nb 1.28 Ta 0.79 La 0.59 Ce 3.72 Th 0.38 . The leaching process with HClO4 can dissolve Ca, Al, and Fe. The results of the ICP OES test showed maximum levels of Nb 0.208 ppm and Th 0.138 ppm, result from the AAS test the grade of Ca and Fe increased as the HClO4 concentration grew larger."

"Saat ini tantalum dan niobium yang merupakan salah satu dari empat belas unsur kritis di dunia telah mengalami defisit pasokan sejak tahun 2015. Oleh karena itu perlu dilakukan usaha untuk mendapatkan sumber lain dalam rangka memenuhi kebutuhan tantalum dan niobium di berbagai segmen industri yang semakin meningkat. Salah satu sumber alternatif untuk memenuhi kebutuhan tantalum dan niobium tersebut adalah terak timah Bangka (TTB) yang mengandung Ta2O5 0,33 % berat dan Nb2O5 0,64 % berat. Tinjauan pada terak timah Bangka yang telah dilakukan oleh peneliti sebelumnya menyatakan bahwa perolehan nilai rasio pengayaan yang rendah disebabkan kurang efektifnya proses pelindian, baik melalui rute asam-basa maupun basa-asam. Oleh karena itu, kebaruan penelitian ini difokuskan pada penggunaan proses roastingquenching (pemanggangan diikuti dengan pencelupan secara cepat ke dalam air) sebagai pre-treatment proses pelindian dengan lima rute berbeda. Dengan proses roasting-quenching tersebut diharapkan akan terjadi peretakan panas (thermal cracking), reduksi ukuran partikel yang akhirnya memperluas area pembasahan. Dengan lebih luasnya area pembasahan akan memudahkan terjadinya reaksi antara oksida berharga maupun oksida lain dengan larutan pelindi dan pada akhirnya diharapkan akan meningkatkan rasio pengayaan tantalum oksida dan niobium oksida dalam TTB tersebut. TTB yang telah mengalami pemanggangan pada suhu 900⁰C diikuti dengan pencelupan secara cepat ke dalam air dan pengayakan, hasil prosesnya disingkat TTB-TPP.Pada studi ini TTB-PPP dilakukan pelindian dengan 5 rute variasi pelarut dan variasi konsentrasi pelarut. Adapun 5 rute variasi pelarut adalah: (i) HF; (ii) HCl; dilanjutkan ke dalam NaOH; (iii) NaOH dilanjutkan ke dalam HClO4; (iv) NaOH dilanjutkan ke dalam H3PO4 dan (v) NaOH dilanjutkan ke dalam HClO4 terakhir H2SO4. Hasil karakterisasi menggunakan X-Ray Fluorescence (XRF), Scanning Electron Microscope-Energy Dispersive X-ray Analysis (SEM-EDAX), Atomic Absorption Spectroscopy (AAS) dan Inductively Coupled Plasma-Optical Emission Spectrometry (ICP-OES) yang dilakukan terhadap TTB, TTB-PPP, residu dan filtrate hasil pelindian ditemukan bahwa TTB-PPP yang dilakukan pelindian dengan larutan NaOH 8 M (2 jam), dilanjutkan pelindian dengan larutan HClO4 0,8 M (2 jam), dan terakhir dilakukan pelindian dengan larutan H2SO4 0,8 M (2 jam), menghasilkan rasio pengayaan paling optimum yaitu 4,09 untuk tantalum oksida dan 3,34 untuk niobium oksida. Sedangkan pelindian TTB-PPP dengan NaOH 8 M (2 jam) dilanjutkan dengan H3PO4 1,5 M (2 jam) menghasilkan rasio pengayaan tantalum oksida 3,7 dan niobium oksida 3,02.

---

Currently tantalum and niobium which are one of the fourteen critical elements in the world has experienced supply deficits since 2015. Therefore, efforts are needed to obtain alternative sources in order to meet the supplies of tantalum and niobium in various industry segments that are increased. One alternative source to meet the needs of tantalum and niobium is Bangka tin slag (BTS) containing Ta2O5 0.33 % wt and Nb2O5 0.64 % wt. A review of the Bangka tin slag that has been performed by previous researchers stated that low enrichment ratio values are due to ineffective leaching processes, both acid-base and acid-base routes. Therefore, the novelty of this research is focused on the use of roasting-quenching process (roasting followed by rapid quenching into water) as pre-treatment of leaching process with five different routes. With the roastingquenching process it is expected to provide thermal cracking, reduction of particle size which eventually expanded the wetting area. With a wider area of the wetting will facilitate the reaction between the precious oxide and other oxides with the leachate solution and ultimately it is expected to increase the ratio of enrichment of tantalum oxide and niobium oxide in tin slag Bangka. In the 900⁰C roasted BTS followed by a rapid quenching into the water and sieving, the result of the process is abbreviated as BTS-RQS.In this study, BTS-RQS leached with 5 routes of solvent variation and variation of solvent concentration. The 5 routes of solvent variation are: (i) HF; (ii) HCl is continued into NaOH; (iii) NaOH is continued into HClO4; (iv) NaOH is continued into H3PO4 and (v) NaOH is continued into HClO4 and the final into H2SO4. The results of characterization using X-Ray Fluorescence (XRF), Scanning Electron Microscope-Energy Dispersive X-ray Analysis (SEM-EDAX), Atomic Absorption Spectroscopy (AAS) and Inductively Coupled Plasma-Optical Emission Spectrometry (ICP-OES) performed on BTS, BTS-RQS, leaching residues and leaching filtrates found that BTS-RQS leached by 8 M NaOH solution (2 h), followed by leaching with HClO4 0.8 M (2 h), and lastly leached with a solution of H2SO4 0.8 M (2 h), yielding the most optimum enrichment ratio of 4.09 for Ta2O5 and 3.34 for Nb2O5. While BTS-RQS leaching with 8 M NaOH (2 h) followed by 1.5 M H3PO4 (2 h) resulted in an enrichment ratio of 3.7 for Ta2O5 and 3.02 for Nb2O5."

"Ekstratksi tin dari sumber sekunder terbukti menjadi alternatif yang atraktif melihat dari permintaan produksi timah yang terus bertumbuh. Terak timah, yang tergolong sumber sekunder, masih menyisakan timah oksida sekitar 1 sampai 3%. Literature studi menunjukkan, untuk melakukan leaching dari terak timah secara efektif, formasi silica gel harus di cegah, oleh karenanya asam oksalat dipilih. Empat parameter leaching, konsentrasi asam oksalat, waktu, temperature, dan rasio, dipilih untuk mengekstrak tin (sebagai target) beserta titanium, tantalum, dan niobium. Eksperimen menunjukan, bahwa parameter leaching paling optimum berada di 24 jam waktu leaching, pada 50?C dan 10% rasio cairan dan solid.

---

Recovering tin from secondary resource proves to be an attractive alternative tin resource to help satisfy the ever-growing tin demands. Tin slag, considered as a secondary resource, still consist of tin in the form of oxides approximately 1 – 3%. Studies found that in order to leach tin slag effectively the formation of silica gel has to be prevented, hence oxalic acid was chosen as the leaching reagent for the study. Four leaching parameters, oxalic acid concentration, leaching time, leaching temperature and solid liquid ratio, were tested through the experiment to extract tin as the primary metal, along with titanium, tantalum and niobium. The experiment concluded that the optimum leaching time is at 24 hours with a temperature of 50?C at 10% solid/liquid ratio."

"ABSTRAK<Ekstratksi tin dari sumber sekunderterbukti menjadi altematifyang atraktifmelihat dari permintaan produksi timah yang tems bertumbuh. Terak timah, yangtergolong sumber sekunder, masih menyisakan timah oksida sekitar 1 sampai 3%.Literature studi menunjukkan, untuk melakukan leaching dari terak timah secaraefektif, formasi silica gel hams di cegah, oleh karenanya asam oksalat dipilih. Empatparameter leaching, konsentrasi asam oksalat, waktu, temperature, dan rasio, dipilihuntuk mengekstrak tin (sebagai target) beserta titanium, tantalum, dan niobium.Eksperimen menunjukan, bahwa parameter leaching paling optimum berada di 24jam waktu leaching, pada 50 C dan 10% rasio cairan dan solid.

---

ABSTRACTRecovering tin from secondary resource proves to be an attractivealternative tin resource to help satisfy the ever-growing tin demands. Tin slag,considered as a secondary resource, still consist of tin in the form of oxidesapproximately 1 - 3%. Studies found that in order to leach tin slag effectively theformation of S,ilica gel has to be prevented, hence oxalic acid was chosen as theleaching reagentofor the study. Four leaching parameters, oxalic acid concentration,leaching time, leaching temperature and solid liquid ratio, were tested through theexperiment to extract tin as the primary metal, along with titanium, tantalum andniobium. The experiment concluded that the optimum leaching time is at 24 hourswith a temperature of 50 C at 10% solidiliqvid ratio."