Hasil Pencarian  ::  Simpan CSV :: Kembali

"Telah dilakukan pengukuran Dose area Product dan Dose Area Product Rate menggunakan Dose Area Product Meter (DAP meter), Entrance Surface Dose menggunakan Thermoluminiscense (TLD) pada pemeriksaan fluoroskopi dengan obyek phantom akrilik 10 cm, 15 cm, 20 cm dan 25 cm serta phantom rando dengan fokus pada paru-paru. Pengukuran dilakukan dengan menggunakan variasi waktu paparan 20 detik, 40 detik, 60 detik, 80 detik, 100 detik dan 120 detik. Untuk phantom akrilik 20 cm dan 25 cm ditambahkan variasi waktu 240 detik. Nilai DAP/mAs yang didapat adalah 0.70, 1.0, 1.4, 1.9 dan 0.83 µGym2/mAs masing-masing untuk phantom akrilik 10, 15 ,20, 25 cm dan phantom rando. Nilai ESD/mAs adalah (32.4±2.2), (35.7±1.5), (85.7±2.3), dan (143.5±10.6) dan (67.4±6.6) µGy /mAs untuk phantom akrilik 10, 15, 20, 25 dan phantom rando. Rasio antara ESD/mAs dengan DAP/mAs adalah (46.2 ± 3.1), (35.2 ± 1.3), (61.0 ± 2.9), 75.6(±5.4), dan (81.0 ± 8.0) untuk phantom akrilik 10, 15 ,20, 25 cm dan phantom rando .Nilai entrance surface dose dan nilai dose area product cenderung mempunyai hubungan yang kuat karena adanya linearitas pada relasi keduanya di setiap variasi ketebalan phantom akrilik dan phantom rando. Nilai entrance surface dose akan meningkat seiring dengan pertambahan nilai dose area product, tapi dari hubungan diantara keduanya tidak dapat dicari nilai yang pasti, sehingga nilai dose area product hanya dapat dipakai untuk memperkirakan dosis entrance surface dan untuk memonitor eksposure terhadap pasien.

---

Dose area Product and Dose Area Product Rate have been determined by Dose Area Product Meter (DAP meter), Entrance Surface Dose by Thermoluminiscent dosimeter (TLD) in the fluoroscopy examination of an acrylic phantom 10cm, 15 cm, 20 cm dan 25 cm and rando phantom at lung. Measurement is done by using exposure time variation within 20 ,40, 60 , 80 , 100 and 120 seconds .For acrylic phantom 20 cm and 25 cm in added time variation 240 seconds. The average values of DAP/mAs were 0.70, 1.0, 1.4 and 1.9 µGy-m2/mAs for phantom thickness of 10, 15, 20, and 25 cm, and about 0.83 - 0.84 µGy-m2/mAs for rando phantom. The average values of ESD/mAs were (32.4±2.2), (35.7±1.5), (85.7±2.3), and (143.5±10.6) and (67.4±6.6) µGy /mAs for phantom thickness 10, 15, 20, 25 and rando phantom. The ratio of ESD/mAs to DAP/mAs varied with phantom thickness were (46.2 ± 3.1)/ m2, (35.2 ± 1.3)/ m2, (61.0 ± 2.9)/ m2, 75.6(±5.4) for phantom thickness of 10 , 15, 20 and 25 cm respectively, and (81.0 ± 8.0)/ m2 for rando phantom. The values of entrance surface dose and dose area product have good correlation cause the DAP values correlate linearly with ESD for every phantom thickness and for rando phantom as well. The increase of entrance surface dose values based on the increase of dose area product values, but the relation from both of it can not find the absolute values, so that dose area product is used to estimate entrance surface dose and to monitor the patient exposure."

"Pada pengecoran Besi Tuang Dinding Tipis terjadi fenomena unik, yaitu terbentuknya lapisan kulit. Lapisan tersebut menjadi pusat stress konsentrasi untuk terjadinya retak material. Salah satu cara untuk meminimalisir terbentuknya lapisan kulit adalah menjaga kecepatan pendinginan pada keadaan optimum. Penelitian ini dilakukan untuk mengetahui pengaruh ketebalan isolator glasswool terhadap kecepatan pendinginan dalam pembentukan lapisan kulit. Variasi modifikasi cetakan yang digunakan adalah tanpa isolator (P4M1), isolator glasswool tebal 40mm sebelah kiri benda dan 50mm sebelah kanan benda(P5M1), dan isolator ketebalan 50mm dikedua sisi benda(P7M1). Dilakukan karakterisasi metalografi non etsa dan etsa, uji mekanis berupa uji tarik, dan uji kecepatan pendinginan pada plat urutan ketiga masing-masing benda cor. Hasil menunjukkan bahwa adanya pengaruh ketebalan isolator terhadap kecepatan pendinginan benda cor. Kecepatan pendinginan tertinggi hingga terendah adalah 21,59⁰C/menit, 3,75⁰C/menit, dan 3,61⁰C/menit. Lapisan kulit ketebalan rata-rata yang didapat P7M1 324μm, P4M1 105μm dan P5M1 71μm. Jumlah nodul tertinggi hingga terendah P4M1 1121 nodul/mm2, P7M1 916 nodul/mm2, dan P5M1 801 nodul/mm2. Nodularitas yang didapat P4M1 78%, P5M1 75% dan P7M1 64%. Nilai tensile strength yang didapat dengan nilai 287MPa, 288MPa sampai 383 MPa. Matriks yang didapat adalah full ferit.

---

Thin wall ductile iron has unique phenomena in manufacturing called skin effect. Skin effect becomes stress concentration to form crack initiation. One of many methods to decrease skin effect is providing optimum cooling rate. This research used the influence of glasswool isolator thickness leading to different cooling rate as variable. Variation of casting also investigated which are molding without isolator (P4M1), molding using isolator glasswool with thickness 40mm on the left side and 50mm on the left side of plate (P5M1) and the last is molding using isolator glaswool with 50mm on both of sides (P7M1). Samples were characterized using metallograpy technique (etching and non etching), mechanical testing especially tensile test and cooling rate testing.

The result shows that thickness of isolator glasswool has influences on cooling rate. The cooling rate varies from fastest to slowest which are 21,59⁰C/minutes, 3,75⁰C/minutes, and 3,61⁰C/minutes. The skin thickness is produced from the thickest to thinnest on the mold using 50mm thickness glaswool isolator, the mold without glasswool isolator and the mold using 40mm glasswool isolator on left side and 50mm glasswool isolator on the right side. High nodul counting resulted from the mold without isolator, the mold using 50mm glasswool isolator and the mold using 40mm glasswool isolator on left side and 50mm glasswool isolator on the right side. Highest nodularity was produced on the mold without isolator which is 78%, the mold using isolator glasswool 40mm and 50mm thickness produced 75% nodularity dan the mold using glasswool isolator 50mm produced 64% nodularity. Tensile test showed tensile strength alter from 287MPa, 288MPa until 383 MPa. The matrix obtains full ferritic"

"Latar belakang: Laporan mengenai hubungan obesitas dan GERD semakin meningkat dalam beberapa tahun terakhir. Dengan meningkatnya pemahaman mengenai mekanisme GERD, diketahui terdapat peran sitokin proinflamasi dan adipositokin yang banyak terdapat di jaringan lemak viseral. Pada beberapa populasi di dunia, ketebalan lemak viseral diketahui berhubungan dengan meningkatnya insiden esofagitis erosif.Tujuan: Mengetahui profil ketebalan lemak viseral pasien GERD di RSCM.Metode: Penelitian ini merupakan studi potong lintang pada 56 subyek GERD. Subyek direkrut secara konsekutif pada bulan April hingga Oktober 2018 di RSUPN Cipto Mangunkusumo, Jakarta. Pemilihan subyek GERD berdasarkan Gastroesophageal Reflux Disease Questionnaires(GERDQ) dan pengukuran tebal lemak viseral menggunakan ultrasonografi. Erosi esofagus ditegakkan berdasarkan hasil endoskopi saluran cerna bagian atas. Analisis bivariat digunakan untuk menentukan perbedaan ketebalan lemak viseral antara grup esofagitis dan non-esofagitis.Hasil: Lebih dari separuh subyek penelitian ini menderita erosive reflux disease(ERD) (55,4%), didominasi oleh pasien dengan esofagitis kelas A berdasarkan klasifikasi Los Angeles sebanyak 64,5%. Rerata ketebalan lemak viseral grup NERD sedikit lebih rendah daripada grup ERD (47,9 mm untuk NERD dan 49,0 mm utk ERD). Terdapat kecenderungan peningkatan rerata ketebalan lemak viseral seiring dengan peningkatan derajat esofagitis (47,6 mm untuk esofagitis derajat A, 50,0 mm untuk esofagitis derajat B, dan 53,5 mm untuk esofagitis derajat C).Kesimpulan: Subjek ERD lebih banyak daripada NERD pada populasi GERD di RSUPN Cipto Mangunkusumo. Rerata ketebalan lemak viseral subjek NERD lebih rendah daripada ERD. Terdapat kecenderungan peningkatan rerata ketebalan lemak viseral seiring dengan peningkatan derajat esofagitis.

---

Background: Reports about thecorrelation between obesity and GERD had been increasedin the past few years. Along with the increasing understanding of GERD, there are roles of proinflammatory cytokines and adipocytokines which are mostly contained in abdominal fat tissue. In several populations, visceral fat thicknessis associated with the increased incidence of erosive esophagitis.

Objective: To determine visceral fat thickness profile in GERD population in Cipto Mangunkusumo National General Hospital.

Methods: A cross-sectional study of 56 adult patients with GERD symptoms was conducted. The subjects were recruited consecutively between April and Oktober 2018 at Cipto Mangunkusumo National Hospital in Jakarta. Gastroesophageal Reflux Disease Questionnaires (GERDQ) were used to select research subjects and Ultrasonography examination was used to determine visceral fat thickness. Esophageal erosions were diagnosed using upper gastrointestinal endoscopy. Bivariate analysis was used to determine visceral fat thickness difference between esophagitis and non-esophagitis group.

Results: More than half of this research subject were patients who suffer erosive reflux disease(55,4%), which dominated by patient with esophagitis class A, regarding to Los Angeles (LA) classifications, there were 64,5% of all ERD patients. The mean visceral fat thickness in erosive reflux disease (ERD) group slightly higher than in non-erosive reflux disease (NERD) group (49,0 mm vs 47,9 mm respectively). There is an increasing trend in mean visceral fat thickness as the esophageal erosion progresses (47.6 mm for grade A, 50.0 mm for grade B, and 53,5 for grade C).

Conclusion: ERD is more common than NERD in Cipto Mangunkusumo General Hospital's GERD population. The mean visceral fat thickness in ERD group is higher than in NERD group. There is an increasing trend in mean visceral fat thickness as the esophageal erosion progresses."

"Penelitian ini bertujuan untuk mengetahui pengaruh ketebalan resin terhadap depth of cure resin komposit serat sebagai substruktur. Lima belas spesimen dibagi menjadi 3 kelompok ketebalan berbeda: 3, 4, dan 5 mm n=5 . Masing-masing spesimen disinari dengan iradiansi 800 mW/cm selama 20 detik. Hasil penelitian menunjukkan depth of cure kelompok 1 adalah 81 , kelompok 2 adalah 78 dan kelompok 3 adalah 34. Nilai tersebut berbeda bermakna secara statistik melalui uji One-way ANOVA dan Post-hoc. Games-Howell. Disimpulkan bahwa ketebalan mempengaruhi depth of cure resin komposit serat sebagai substruktur.

---

The aim of this study is to know the effect of resin thickness on the depth of cure of fiber reinforced resin composite as substructure. Fifteen specimens are divided into 3 different thickness groups 3, 4, and 5 mm n 5 . Each specimen was cured with irradiation of 800 mW cm for 20 seconds. The result showed the depth of cure of group 1 was 81 , group 2 78 and group 3 34. The result was significantly different using One way ANOVA and Games Howell Post hoc test. It was concluded that resin thickness has effect on the depth of cure of fiber reinforced resin composit as substructure."

"Latar Belakang: CT scan orbita merupakan modalitas radiologi yang mudah dan efisien untuk menilai adanya penebalan otot ekstraokular pada penderita oftalmopati Graves. Penebalan otot ekstraokular memiliki korelasi dengan masing-masing derajat oftalmopati Graves. Di Indonesia, belum ada korelasi antara ketebalan otot ekstraokular dengan derajat oftalmopati Graves menurut klasifikasi NOSPECS. Tujuan: Mendapatkan nilai korelasi antara ketebalan otot ekstraokular pada CT scan orbita dengan derajat oftalmopati Graves. Metode: Penelitian ini menggunakan desain potong lintang dengan metode consecutive sampling. Sampel penelitian berjumlah 89 orbita yang berasal dari 50 pasien penderita oftalmopati Graves yang telah menjalani pemeriksaan CT scan orbita di Departemen Radiologi RSUPN Cipto Mangunkusumo periode Januari 2012 hingga Desember 2016. Penelitian dilakukan sejak Februari hingga Maret 2017. Pengukuran ketebalan otot ekstraokular pada CT scan orbita dilakukan setelah meninjau ulang derajat oftalmopati Graves melalui hasil pemeriksaan oftalmologi. Hasil: Terdapat perbedaan bermakna di antara rerata ketebalan otot ekstraokular menurut derajat oftalmopati Graves (p<0,05). Uji korelasi Spearman didapatkan korelasi yang bermakna dan nilai r yang bervariasi di antara ketebalan otot ekstraokular dengan derajat oftalmopati Graves. Nilai r=0,43 untuk rektus medial, r=0,37 untuk rektus lateral, r=0,49 untuk rektus superior, r=0,45 untuk rektus inferior dan r=0,57 untuk ketebalan total ekstraokular. Kesimpulan: Terdapat korelasi positif sedang antara ketebalan otot ekstraokular pada CT scan orbita dengan derajat oftalmopati Graves.

---

Background: CT scan is an easy and efficient radiological modality to measure extraocular enlargement in the patient with Graves' ophthalmopathy disease. Extraocular muscles enlargements were had correlated with each grade of Graves' ophthalmopathy. In Indonesia, there is not yet a study about correlation between extraocular muscles diameter in orbital CT scan with Graves' ophthalmopathy severity based on NOCPECS classification.Purpose: To obtain the correlation values between extraocular muscles diameter in orbital CT scan with Graves' ophthalmopathy severity.Method: This study used a cross sectional design. Eighty nine samples from fifty patients with Graves' opthalmopathy were chosen using consecutive sampling from patients that underwent orbital CT scan at the Radiology Departement of the Indonesia University's Faculty of Medicine' Cipto Mangunkusumo Hospital from time periode January 2012 until December 2016. This study was done from February until March 2017. The measurement of extraocular muscles diameter in orbital CT scan was performed after had reviewed Graves' ophthalmopathy severity from ophthalmology examination on medical record.Results: There are significantly differences between extraocular muscles diameter mean with Graves' ophthalmopathy severity (p<0,05). Spearman correlation test between extraocular muscles diameter with Graves' ophthalmopathy grading shows significant correlation with varied r values, r=0,43 for rectus medial, r=0,37 for rectus lateral, r=0,49 for rektus superior, r=0,45 for rectus inferior and r=0,57 for total diameters of extraocular muscles. Conclusion: There is a moderate positive correlation between extraocular muscles diameter in orbital CT scan with Graves' ophthalmopathy severity."

"Pengujian ultrasonik, sebagai bagian dari metode evaluasi tak merusak saat ini menjadi sangat penting karena penerapannya tidak hanya digunakan sebagai metode pendeteksian cacat, tetapi lebih jauh digunakan sebagai metode karakterisasi material, seperti untuk prediksi pengukuran ketebalan lapisan pada baja yang terkarburisasi, sehingga pada aplikasinya dapat mencegah terjadinya degradasi material.Penelitian ini bertujuan untuk memprediksi kedalaman difusi baja rendah karbon yang terkarburisasi dengan menggunakan pengujian ultrasonik.Pada penelitian ini dilakukan karburisasi pada sampel menggunakan metode pack carburizing, dengan variabel temperatur dan waktu tahan yang berbeda. Kemudian dilakukan pengujian ultrasonik menggunakan metode water immersion dengan probe berfrekuensi 10 MHz, untuk mengetahui kedalaman difusi masingmasing sampel.Hasil dari penelitian ini menunjukkan bahwa prediksi untuk kedalaman difusi menggunakan pengujian ultrasonik dapat dilakukan, dengan hasil nilai yang tidak jauh berbeda dengan standar untuk kesesuaian kedalaman difusi. Besar penyimpangan rata-rata dari setiap sampel yang diujikan adalah 19.3 %.

---

Ultrasonic testing as a part of Non Destructive Evaluation method become very important nowadays, because it?s not only applicable for flaw detection but also can be used for material characteristization method, such as prediction for diffusion thickness of carburized surface layer. By this prediction, the output is for preventing material degradation.The objective of this experiment is to predict diffusion thickness as a result of carburizing for low carbon steel with longitudinal ultrasonic velocity waves.This experiment is performed using nine samples that carburized using parameters with austenitization temperature and holding time. Ultrasonic testing is done by using water immersion method with frequency 10 MHz.The result of this experiment show that the prediction for diffusion thickness using ultrasonic test can be allowed, in which the result is not significantly different if compared to diffusion thickness standard. The average value of deviation for each sampel is 19.3 %."

"Latar Belakang: Ventilasi mekanik diperlukan pasien kritis di unit perawatan intensif dengan tujuan menormalkan kadar gas darah arteri dan menyeimbangkan kadar asam basa, namun penggunaan ventilasi mekanik yang berkepanjangan dapat menyebabkan terjadinya Ventilator Associated Pneumonia, cedera paru, infeksi nosokomial, dan sepsis. Ketebalan diafragma memiliki korelasi signifikan dengan lama penggunaan ventilasi mekanik. Penelitian ini bertujuan menganalisis hubungan faktor-faktor risiko dengan ketebalan diafragma pasien kritis di ICU, sehingga dapat membantu untuk memprediksi lamanya penggunaan ventilasi mekanik.Metode: Penelitian ini merupakan studi analitik observasional terhadap 30 subjek penelitian yang memenuhi kriteria penerimaan selama periode September 2018- Desember 2018 di Ruang Perawatan Intensif RSUP Dr. Mohammad Hoesin. Ketebalan diafragma pasien kritis yang menggunakan ventilasi mekanik diukur pada hari ke-0, ke-3, ke-5 dan kemudian dibandingkan.Hasil: Penelitian menunjukkan bahwa penggunaan ventilasi mekanik didominasi oleh laki-laki (63,33 %), usia 40-70 tahun (63,33%), dengan status nutrisi kategori tidak obes (90%). Penurunan ketebalan diafragma signifikan terjadi pada hari ke-3 (nilai P = 0,026). Penurunan ketebalan diafragma memiliki hubungan yang bermakna dengan RNL (nilai P = 0,003), kadar prealbumin (nilai P = 0,025), IMT (nilai P = 0,015), sepsis (nilai P = 0,010), dan pemberian albumin artifisial (nilai P = 0,013). Sedangkan usia (nilai P = 0,603), jenis kelamin (nilai P = 0,906), opioid (nilai P = 0,315), dan kadar glukosa (nilai P = 0,303) menunjukkan hubungan yang tidak bermakna secara statistik.Simpulan: Penurunan ketebalan diafragma terjadi pada subjek yang menggunakan ventilasi mekanik dipengaruhi oleh RNL, kadar prealbumin serum, IMT, sepsis, dan penggunaan albumin intravena, namun tidak dipengaruhi usia, jenis kelamin, penggunaan opioid, dan pemberian infus albumin intravena.

---

Background: Mechanical ventilation required by critical patients in intensive care unit to normalizing arterial blood gas and balancing acid-base levels, but prolonged use of mechanical ventilation can cause ventilator associated pneumonia, lung injury, nosocomial infections, and sepsis. Diaphragm thickness has a significant correlation with the duration of mechanical ventilation uses. This study aims to analyze the relations of risk factors with the thickness of the diaphragm of critical patients in the ICU. Hopefully it can help to predict the length of the mechanical ventilation uses.

Methods: This study was an observational analytic study of 30 research subjects who met the acceptance criteria during the period September 2018-January 2019 in the Intensive Care Unit of Dr. Mohammad Hoesin Hospital. The diaphragm thickness of critical patients using mechanical ventilation was measured on the 0th, 3rd, 5th and then compared by days.

Results: The study showed that the use of mechanical ventilation was dominated by men (63.33%), ages 40-70 years (63.33%), with nutritional status in the category of not obese (90%). A significant decrease in the thickness of the diaphragm occurred on the 3rd day (p-value = 0.026). The decrease in diaphragm thickness has a significant relations with RNL (p-value = 0.003), prealbumin level (p-value = 0.025), BMI (p-value = 0.015), sepsis (p-value = 0.010), and artificial albumin (p-value = 0.013). Whereas age (p-value = 0.603), gender (p-value = 0.906), opioid (p-value = 0.315), and glucose level (p-value = 0.303) showed a relations that did not reach statistical significance.it

Conclusion: The decrease in diaphragm thickness occurred in subjects using mechanical ventilation affected by RNL, serum prealbumin levels, BMI, sepsis, and intravenous albumin uses, but were not affected by age, sex, opioid use, and intravenous albumin infusion."

"Lapis Iindung dengan pengecatan adalah salah satu cara yang paling banyak dipakai untuk mencegah terjadinya korosi. Ketebalan lapisan dan konsentrasi dari inhibitor pada Iapisan cat adalah salah satu faktor yang menentukan keberhasilan dari suatu sistem pengecatan. Penelitian ini bertujuan untuk mempelajari pengaruh ketebalan lapisan cat dan pengaruh konsentrasi inhibitor Zn3(PO4)2 terhadap kebzotan adlzesif dan kemhanan korosi dad lapisan cat. Variasi ketebalan cat yang digunakan adalah 50pm, 75pm, dan 100pm dengan konsentrasi inhibitor Zn3(PO4)2 0%, 15% dan 30%. Proses pelapisan benda uji dilakukan dengan cara disemprot dengan Spraying Gun setelah sebelumnya dilakukan persiapan permukaan dengan Sand Blasting. Ketebalan kering lapisan cat (Dry Film Thickness) diukur dengan mengunakan alat Magnetic Elcometer A5134 D U86-SZ Pengujian ketahanan korosi dilakukan dengan metode Salt Spray ASTM B 117-85 selama 504 jam, sedangkan untuk mengetahui kekuatan adhesif dari Iapisan cat dilakukan dengan metode Pull-Off Strength ASIM D 4541. Hasil pengujian diamati dengan menggunakan mikroskop optik (fota makro) dan dilakukan klasifikasi ketahanan korosi dengan menggunakan standar JIS Z2371. Hasil penelitian menunjukkan bahwa peningkatan ketebalan lapisan cat akan meningkatkan kekuatan adgesif dan ketahanan korosi. Sedangkan peningkatan konsentrasi inhibitor Zn3(PO4)2 akan meningkatkan ketahanan korosi meskipun terjadi penurunan nilai kekuatan adhesif dari lapisan cat."

"Aluminum matrix composite (AMC) menjadi material yang sangat potensial bagi aplikasi industri ketika terdapat kebutuhan untuk mendapatkan kombinasi sifat ringan dengan sifat lainnya yang menunjang seperti kekuatan, kekakuan, ketahanan aus, konduktivitas listrik dan termal tinggi, dan koefisien ekspansi termal rendah. Namun material AMC sangat rentan terkena korosi pitting dan galvanik, yang disebabkan oleh pembentukan pasangan galvanik antara matriks dan penguat, serta terbentuknya mikrostruktur pada interface penguat/matrix. Anodisasi merupakan proses modifikasi permukaan yang potensial untuk meningkatkan ketahanan korosi AMC dengan menghasilkan lapisan oksida berpori. Namun, adanya penguat dalam AMC menghalangi pembentukan lapisan oksida protektif dengan mendorong terbentuknya cavity dan retak mikro. Oleh karena itu, metode cerium sealing digunakan untuk memperbaiki cacat pada lapisan oksida hasil anodisasi, sehingga dapat meningkatkan ketahanan korosi pada lingkungan yang sangat agresif.Penelitian ini bertujuan untuk menganalisis pengaruh parameter proses yakni temperatur dan rapat arus anodisasi terhadap pembentukan lapisan anodik berpori. Anodisasi dilakukan pada tiga temperatur yakni 25°C,0°C dan -25°C dengan variasi rapat arus 25,20 dan 15 mA/cm2. Pengujian kekerasan mikro Vickers digunakan untuk mengetahui sifat mekanik lapisan anodik. Pengamatan struktur mikro menggunakan FE-SEM untuk mengetahui morfologi permukaan dan mengukur ketebalan lapisan anodik.Hasil pengujian menunjukkan penurunan temperatur dan rapat arus akan meningkatkan kekerasan permukaan lapisan anodik alumina dimana kekerasan tertinggi adalah 427 HV yang didapat pada temperatur -25°C dengan rapat arus 15mA/cm2. Penurunan temperatur dan rapat arus juga relatif akan meningkatkan kerapatan dan keseragaman permukaan hasil anodisasi. Serta penurunan temperatur hingga 0°C akan meningkatkan ketebalan lapisan oksida dimana ketebalan terbesar adalah 14,13 μm yang yang didapat pada temperatur 0°C dengan rapat arus 25mA/cm2. Namun ketebalan kembali menurun pada saat diturunkan ke temperatur -25°C.

---

Aluminum matrix composites (AMC) become potential materials for transport application where there is an obvious need for combination of weight saving and other properties, i.e. high specific strength, high specific stiffness, electrical and thermal conductivities, low coefficient of thermal expansion and wear resistance. However they are generally susceptible to corrosion in various environments, due to galvanic reactions between the reinforcements and the matrix, and selective corrosion on the interface due to the formation of new compounds. Anodizing has been considered as a potential modification treatment for enhancing corrosion resistant of AMC by forming porous anodic oxide on the surface area.

This study aims to analyze the influence of anodizing process parameters which is temperature and current density on the formation of porous anodic coating, Anodizing process has been done at three different temperatures which are 25°C,0°C and -25°C with variation of current density at 25,20 and 15 mA/cm2. Vickers microhardness testing was used to determine the mechanical properties of anodic layer. Observation of microstructure using FE-SEM to determine surface morphology and to measure anodic layer thickness.

Test results showed that decreasing temperature and current density would increase surface hardness of aluminium anodic layer. The highest surface hardness was 427 HV which was got by anodizing at temperature -25°C with using 15 mA/cm2 of current density. Decreasing temperature and current density would also relatively increasing density and make the surface smoother and looks more uniform. Decreasing temperature until 0°C would increase thickness of the oxide layer where the highest thickness was 14,13 μm which was got by anodizing at temperature 0°C with using 25 mA/cm2 of current density. But the thickness would decrease when the temperature was decreased to -25°C."