Abstrak :
Penelitian mengenai polikristalin perovskite manganit telah dilakukan, dimulai dengan mensintesis material La0,7(Ba0.97Ca0.03)0.3Mn1-xCuxO3 (x = 0; 0,03; 0,05; 0.07 dan 0,10) dengan menggunakan metode sol-gel, karakterisasi menggunakan X-ray diffractometer, menunjukkan sampel memiliki struktur kristal rhombohedral dengan space group R-3c, substitusi Cu yang dilakukan tidak mengubah struktur kristal sampel akan tetapi hanya merubah parameter latis, volume unit sel, ukuran kristalit rata-rata, Panjang ikatan dan sudut ikatan antara Mn/Cu terhadap oksigen. Karakterisasi SEM menunjukkan bahwa terjadi perubahan ukuran grain yang membesar saat konsentrasi Cu ≤ 5% dan ukuran grain akan mengecil kembali saat kosentrasi melebihi 5%. Karakterisasi menggunakan VSM menunjukkan bahwa terjadi penurunan magnetisasi seiring penambahan konsentrasi Cu. Hasil uji kelistrikan menunjukkan bahwa resistivitas menurun drastis ketika konsentrasi Cu ≤ 5% dan meningkat kembali ketika konsentrasi Cu melebih 5 %. Hasil permodelan menggunakan persamaan perkolasi menunjukkan penurunan Tcmod seiring dengan penambahan konsentrasi Cu. ......Research on polycrystalline perovskite manganite has been carried out, starting with materials synthesizing La0.7(Ba0.97Ca0.03)0.3Mn1-xCuxO3 (x = 0; 0.03; 0.05; 0.07 and 0.10) using the sol-gel method, characterization using X-ray diffractometer, shows the sample has a rhombohedral structure with R-3c space group, Cu substitution that is not changing the crystal structure of the sample, but only change lattice parameters, unit cell volume, average crystallite size, bond length and the bond angle between Mn / Cu and oxygen. Characterization of SEM showed changes in grain size which increase when concentration of Cu ≤ 5% and grain size will decrease when Cu concentration increases by 5%. Characterization using VSM showed a decrease the magnetization. Electrical characterization results showed that the resistivity decrease dramatically while Cu concentrations ≤ 5% and increased while Cu concentrations increased by 5%. The modeling results using the percolation equation showed the Tcmod decrease according to the ratio of Cu concentration.

Abstrak :
Partikel logam mulia dengan permukaan high energy facets diketahui memiliki aktivitas katalitik yang tinggi. Pada penelitian ini berhasil dilakukan sintesis partikel Pt diatas elektroda ITO dengan teknik elektrodeposisi mode Square-Wave Pulse (SWP) dengan variasi parameter potensial atas (0,5, 1,0, 1,5 dan 2,0 V), jenis elektrolit (H2SO4, H2SO4 + KCl dan KCl) serta pulse deposition time (0,05 s dan 0,25 s). Partikel Pt ini kemudian  digunakan sebagai katalis hidrogenasi aseton dibawah pengaruh gelombang mikro. Hasil penelitian menunjukkan bahwa potensial atas hingga 1,5 V menyediakan driving force yang cukup untuk terbentuk partikel dengan kelopak tajam seperti nanoflower. Bentuk permukaan seperti ini merupakan high energy facets yang dikonfirmasi sebagai puncak difraksi (220) dan (311). Laju penumbuhan kristal pada bidang kristal (220) dan (311) juga akibat adanya ion-ion elektrolit HSO4- dan SO42- yang cenderung untuk teradsorpsi secara selektif pada bidang permukaan Pt tertentu yang mendorong pembentukan partikel anisotropik. Penambahan Pulse Deposition Time (t) dari 0,05 s ke 0,25 s menghasilkan ukuran partikel yang lebih kecil. Aktivitas katalitik partikel Pt pada proses hidrogenasi aseton bergantung kepada keberadaan high index facets dan densitas sebaran partikelnya. Diperoleh hasil yang paling tinggi yaitu 30,9% dalam waktu 300 s ketika sintesis menggunakan elektrolit H2SO4 dengan tegangan 1,0 V. 

---

It is known that noble metal particles with high energy facets have high catalytic activity. In this study, Pt particles were successfully synthesized on ITO electrodes using the Square-Wave Pulse (SWP) electrodeposition technique with variations in the upper potential parameters (0.5, 1.0, 1.5 and 2.0 V, electrolyte type (H2SO4, H2SO4 + KCl and KCl) and pulse deposition time (0.05 s and 0.25 s). Pt particles were then used as catalysts for hydrogenation acetone under the microwaves exposure. The results show that the upper potential of up to 1.5 V provides sufficient driving force for the formation of microflowers with sharp petals such as nanoflower that is confirmed as the diffraction peak of (220) and (311). In addition, the crystal growth rate in the crystal plane (220) and (311) is also due to the presence of electrolyte ions HSO4- and SO42- which tend to be selectively adsorbed in certain Pt surface facets which encourage the formation of anisotropic particles. In addition, the increase Pulse Deposition Time from 0.05s to 0.25s results in smaller particle size. The catalytic activity of Pt particles in the hydrogenation process of acetone depends on the presence of high index facets and its particle density and achieves the highest yield of 30.9% at 275s when using H2SO4 electrolyte with an upper voltage of 1 volt.

Abstrak :
Material lapisan Ni80CoxFe20-x (x = 0, 5, 10, 15, dan 20) disintesis dengan metode elektrodeposisi pada substrat ITO-PET. Struktur kristal, fasa material, sifat magnetik dan perubahan resistivitas akibat pengaruh komposisi Ni80CoxFe20-x diteliti melalui karakterisasi X-Ray Diffractometer (XRD), Scanning Electron Microscope (SEM), Energy Dispersive Spectroscopy (EDS)-Mapping, Vibrating Sample Magnetometer (VSM), dan metode Four-Point Probe pada Cryogenic Magnetometer (Oxford Teslatron Instrument). Hasil XRD menunjukkan struktur kristal FCC dengan space group Fm3m. Komposisi dari seluruh sampel mencapai komposisi target (dengan toleransi ±5) dan homogenitas yang baik melalui karakterisasi EDS-Mapping dan SEM. Hasil VSM menunjukkan seluruh sampel merupakan material soft feromagnetik pada suhu ruang. Seluruh sampel berhasil menghasilkan lapisan dengan saturasi magnetisasi >80 emu/gram dan nilai koersivitas <250 Oe. Kelima sampel memiliki rentang saturasi magnetisasi dari 90,387-159,792 emu/g dan koersivitas dari 95,84-191,33 Oe di mana saturasi magnetisasi tertinggi terjadi pada komposisi Ni80Co10Fe10 sedangkan koersivitas terendah terjadi pada komposisi Ni80Co15Fe5. Pengujian nilai resistivitas listrik terhadap perubahan temperatur (5-300 K) menunjukkan bahwa seluruh sampel bersifat konduktor dikarenakan nilai resistivitasnya meningkat seiring dengan meningkatnya temperatur. Hasil penelitian ini menunjukkan bahwa komposisi suatu material memengaruhi sifat magnetik dan nilai resistivitasnya. Komposisi lapisan Ni80CoxFe20-x (x = 0, 5, 10, 15, dan 20) yang memiliki fasa tunggal, lapisan yang homogen, komposisi yang mencapai target, bersifat soft magnetic dengan koersivitas rendah (<250 Oe) dan saturasi magnetisasi yang tinggi (>80 emu/gram) serta perubahan resistivitas yang kecil terhadap temperatur adalah x = 15, yaitu Ni80Co15Fe5.

---

Films of Ni80CoxFe20-x (x = 0, 5, 10, 15, and 20) was synthesized by electrodeposition method on ITO-PET substrate. The crystal structure, material phase, magnetic properties and change of resistivity as a result of composition changes on Ni80CoxFe20-x was characterized by X-Ray Diffractometer (XRD), Scanning Electron Microscope (SEM), Energy Dispersive Spectroscopy (EDS)-Mapping, Vibrating Sample Magnetometer (VSM), and Four-Point Probe Method using Cryogenic Magnetometer (Oxford Teslatron Instrument). XRD results show FCC crystal structure with the Fm3m space group. The composition of all samples was successfully close to the target composition (with ±5 tolerance) and even homogeneity through EDS-Mapping and SEM. VSM results show that all samples are soft ferromagnetic in room temperature. All samples successfully achieve saturation of magnetization >80 emu/gram and coercivities <250 Oe. All samples resulted with saturation of magnetization ranging from 90,387-159,792 emu/g and coercivity ranging from 95,84-191,33 Oe where the highest saturation of magnetization was found at the composition of Ni80Co10Fe10 while the lowest coercivity was found at the composition of Ni80Co15Fe5. Characterization of resistivity values under the influence of temperature change (5-300 K) shows that all samples are conductors because of the increase of resistivity values when temperature is increased. The result of this experiment shows that the composition of a material affects the magnetic properties and resistivity value. The composition of Ni80CoxFe20-x (x = 0, 5, 10, 15, dan 20) films that has a single phase, uniform film, composition that reaches the target, is soft magnetic with low coercevities (<250 Oe) and high saturation of magnetization (>80 emu/gram), and low resistivity value change under the influence of increased temperature is x = 15, that is Ni80Co15Fe5.

Abstrak :

Lapisan paduan NiCoFeCr telah berhasil disintesis menggunakan metode elektrodeposisi dengan penambahan zat aditif Na-sakarin dalam pengaruh arus deposisi sebesar-25mA selama lima menit pada suhu ruang. Pengaruh komposisi Kromium (Cr) sebesar 0 hingga 39,78at% Cr terhadap struktur, morfologi, dan sifat magnetik lapisan paduan NiCoFeCr telah diteliti. Berdasarkan hasil X-Ray Diffractometer (XRD), peningkatan komposisi Cr tidak mengubah struktur kristal FCC dan space group Fm-3m. Hasil karakterisasi Scanning Electron Microscopy (SEM) menunjukkan terbentuknya microvoids dan microcracks yang diindikasikan oleh evolusi gelembung gas hidrogen ketika komposisi Cr bertambah. Lapisan paduan NiCoFeCr (0 hingga 39,78at% Cr) menunjukkan sifat feromagnetik berdasarkan hasil Vibrating Sample Magnetometer (VSM). Lapisan paduan NiCoFeCr (0 hingga 39,78at% Cr) mengalami penurunan saturasi magnetisasi (Ms) sebesar 159,85 emu/g hingga 4,20 emu/g dan mengalami peningkatan koersivitas (Hc) sebesar 51,84 Oe hingga 257,73 Oe. Peningkatan komposisi Cr menyebabkan saturasi magnetisasi (Ms) menurun dan koersivitas (Hc) meningkat.

 

---

NiCoFeCr film alloys were synthesized using the electrodeposition method by adding Na-saccharin additives under the deposition current of -25mA for five minutes at room temperature. The effect of chromium (Cr) addition with composition 0 to 39.78at%  on the structure, morphology, and magnetic properties were investigated. From the X-Ray Diffractometer (XRD) results, the increase in Cr composition does not change the FCC crystal structure and Fm-3m space group. The result of the Scanning Electron Microscopy (SEM) observation reveals a formation of microvoids and microcracks indicated by the evolution of hydrogen gas bubbles when the Cr composition is increased. The NiCoFeCr (0 to 39.78at% Cr) film alloys exhibit ferromagnetic properties based on the results of the Vibrating Sample Magnetometer (VSM). The saturation magnetization (Ms) and coercivity (Hc) of NiCoFeCr (0 to 39.78at% Cr) varied between 159.85 emu/g to 4.20 emu/g and 51.84 Oe to 257.73 Oe, respectively. The decrease in saturation magnetization (Ms) and the increase in coercivity (Hc) values are due to an increase in Cr composition.

Abstrak :
Elektrokatalitik water splitting diketahui merupakan teknologi yang menjanjikan untuk produksi hidrogen dan oksigen yang menyediakan energi bersih yang terjangkau dan mengurangi ketergantungan pada bahan bakar fosil. Elektrokatalis digunakan untuk meningkatkan laju reaksi elektrokimia reaksi evolusi hidrogen (HER) dan reaksi evolusi oksigen (OER). Dibandingkan dengan logam mulia lain, Platinum (Pt) merupakan elektrokatalis HER yang paling efisien dan stabil dalam elektrolit asam atau basa. Studi literatur menunjukkan efisiensi elektrokatalitik dari bahan platinum berstruktur nano sangat dipengaruhi oleh bentuk, ukuran, dan bidang kristal permukaannya. Untuk itu dalam penelitian ini dilakukan sintesis partikel Pt diatas substrat ITO dengan metode elektrodeposisi mode Square-Wave Pulse (SWP) dengan variasi larutan elektrolit dengan KCl dan KCl + H2SO4 untuk mendapatkan bentuk dan bidang kristal tertentu di permukaan. Hasil penelitian menunjukkan bahwa pertumbuhan partikel Pt dipegaruhi oleh adanya ion-ion elektrolit asam sulfat (H2SO4), yaitu HSO4- dan SO42- yang mendorong pembentukan partikel anisotropik, yaitu berbentuk bulat dengan duri runcing yang berbentuk seperti kelopak bunga (flower-like). Sedangkan elektrolit KCl saja hanya menghasilkan partikel Pt dengan kecenderungan berbentuk bulat (sphere). Pt MF menunjukkan kinerja katalitik HER yang lebih baik dimana overpotential dan kemiringan yang lebih rendah daripada Pt MS. Hal tersebut mungkin disebabkan adanya bidang berindeks tinggi yaitu bidang (220) dan (311) pada Pt MF yang berkerja sebagai situs aktif yang dapat memutus rantai ikatan senyawa. Sedangkan Pt MS dominan memiliki bidang kristal (100) dan (002) yang lebih baik untuk meningkatkan aktivitas katalitik OER.

---

Electrocatalytic water splitting is considered as a promising technology for the production of hydrogen as affordable clean energy and reduces dependence on fossil fuels. Electrocatalysts used to increase the electrokinetics reaction of hydrogen evolution reaction (HER) and oxygen evolution reaction (OER). Compared to other noble metals materials, Platinum (Pt) is the most efficient and stable HER electrocatalyst in acid or alkaline electrolytes. Literature studies show the electrocatalytic efficiency of nanostructured Pt influenced by the shape, size, and surface crystal facets. For this reason, this research carried out the synthesis of Pt particles on the ITO-coated glass substrate using the Square-Wave Pulse (SWP) mode electrodeposition method with two variations in the electrolyte solution, namely KCl and KCl + H2SO4 to obtain certain crystal facets on the surface. The results show that the growth of Pt particles was affected by the presence of sulfuric acid electrolyte ions (HSO4- and SO42-) promoting the formation of anisotropic particles, which is flower-like particles, while the single electrolytes KCl only produces Pt particles with a spherical shape. Pt MFs shows a better catalytic performance of HER, where overpotential and slope are lower than Pt MSs. That might be due to high index facets (220) and (311), which work as active sites that can break the bonding chains of compounds. Meanwhile, the crystal facets of Pt MSs are dominated by (100) and (002) facets which are better for the catalytic activity of OER.