Effect of Processing Temperature on Pure Al/Sic Metal Matrix Composites Produced by The Lanxide Process
Anne Zulfia (Fakultas Teknik Universitas Indonesia, 2001)
|
| Pure Al/SiC metal matrix composites (MMC) have been successful produced by the Lanxide process with different processing temperature for 8 hours. The process is simply without aid externally pressure. However, N2 oxygen free was flushed during the process. Molten pure Al has fully infiltrated to the preform with Sl/1% Mg at 750, 800, 850, 900 and 1000°C§ but infiltration did not occur to the preform with 3Vj'% Mg. Voids exist above the infiltrated preform in the systems with higher temperature (900 °C and 1000°C) for 8 hours. Such voids were not formed in the systems with low temperature. This paper described the investigation into the production of pure Al matrix composites, the eject of processing temperature will be investigated and the resulting will be fully characterised. |
|
|
| No. Panggil : | JUTE-15-2-Jun2001-202 |
| Entri utama-Nama orang : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2001 |
| Sumber Pengatalogan : | |
| ISSN : | |
| Majalah/Jurnal : | Jurnal Teknologi |
| Volume : | 15 (2) Juni 2001 : 202-213 |
| Tipe Konten : | |
| Tipe Media : | |
| Tipe Carrier : | |
| Akses Elektronik : | |
| Institusi Pemilik : | Universitas Indonesia |
| Lokasi : |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| JUTE-15-2-Jun2001-202 | 03-20-662522498 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20305664 |