Studi pengaruh jumlah lapisan buttering dan jenis elektroda buttering terhadap sifat mekanis dan ketahanan retak hasil hardfacing pada baja tahan aus CREUSABRO® 4800 dengan pengelasan Shielded Metal Arc Welding (SMAW) = Study the effect of buttering layer number and types of electrodes on mechanical properties and crack susceptibility of the hard-facing of wear resistance steel ? CREUSABRO® 4800 by Shielded Metal Arc Welding (SMAW) process

Wahidun Adam; Winarto, supervisor; Badrul Munir, examiner; Dwi Marta Nurjaya, examiner (Fakultas Teknik Universitas Indonesia, 2012)

 Abstrak

ABSTRAK
Teknologi Hardfacing pada prinsipnya adalah melapisi material induk dengan
material yang lebih keras agar kekerasan dan ketahanan ausnya meningkat dan
umur pakai dari material tersebut menjadi lebih lama. Masalah timbul ketika kita
ingin melakukan hardfacing pada material yang sudah keras. Hasil hardfacing
material keras selalu mengalami retak-retak halus. Untuk itu, dilakukanlah
penelitian guna mencari proses hardfacing yang tepat untuk material keras ini.
Penelitian ini dilakukan pada baja tahan aus CREUSABRO 4800, yang termasuk
baja paduan rendah. Sampel yang digunakan ada lima buah dan parameter
penelitiannya adalah jumlah lapisan dan jenis buttering. Elektroda yang dipakai
ada tiga jenis, untuk buttering memakai MG DUR 3 dan AWS ER309L, serta MG
DUR 65 untuk lapisan hardfacing. Metoda pengelasan yang dipakai adalah
metoda pengelasan Shielded Metal Arc Welding (SMAW). Pengujian yang
dilakukan meliputi pengujian visual dan radiografi, pengujian kekerasan mikro,
pengujian keausan, dan pengamatan metalografi. Hasil penelitian menunjukkan
bahwa lapisan buttering yang lebih banyak dan penggunaan elektroda AWS
ER309L menghasilkan retak yang lebih sedikit, tetapi terjadi penurunan sifat
mekanis. Dengan demikian, dapat disimpulkan bahwa penambahan lapisan
buttering hingga tiga lapis dan pemilihan elektroda yang lebih lunak akan
meningkatkan ketahanan retak hasil hardfacing. Namun, sebagai kompensasinya,
terjadi penurunan sifat mekanis lapisan hardfacing.

ABSTRACT
Hardfacing technology in principle is deposed a material with harder material, in
order to increase hardness, wear resistance and life time of the material. We find
a problem when we want to do hardfacing on material has been hard. The
hardfacing result of hard material always had fine cracks. Therefore, we
conducted this research to find the best of hardfacing processes for this material.
This research was conducted on a wear resistance steel CREUSABRO 4800,
which include on Low Alloy Steel. The samples used were five and research
parameter is the number of layers and types of buttering electrode. There are three
types of electrodes, MG-DUR 3 and AWS ER309L for buttering and MG-DUR
65 for hardfacing layer. The method used is Shielded Metal Arc Welding
(SMAW) process. Tests performed include visual and radiographic testing, micro
hardness testing, wear testing, and metallographic observations. The results
showed that more buttering layer and the use of electrode AWS ER309L produce
fewer cracks, but a decrease in mechanical properties. Thus, it can be concluded
that the addition of a layer of buttering up to three layers and selection of softer
electrodes improves crack susceptibility of hardfacing. However, as
compensation, a decrease in the mechanical properties of hardfacing layer.

 File Digital: 1

Shelf
 S42739-Studi pengaruh.pdf :: Unduh

 Metadata

No. Panggil : S42739
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Penerbitan : [Place of publication not identified]: Fakultas Teknik Universitas Indonesia, 2012
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resources
Deskripsi Fisik : xv, 49 pages ; 30 cm
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S42739 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20308667