Studi pengaruh jumlah lapisan buttering dan jenis elektroda terhadap sifat mekanis dan ketahanan retak hasil hardfacing pada baja tahan aus creusabro 8000 dengan pengelasan SMAW = Effect of buttering layer and electode variation on mechanical properties and crack susceptibility of the hardfaced wear resistance steel CREUSABRO 8000 by SMAW process

Achsanul Rizqi; Winarto, supervisor; Dwi Marta Nurjaya, examiner; Badrul Munir, examiner (Fakultas Teknik Universitas Indonesia, 2012)

 Abstrak

ABSTRAK
Hardfacing merupakan salah satu alternatif dalam mendapatkan
permukaan logam dengan sifat mekanis tinggi. Penelitian ini memvariasikan
jumlah lapisan buttering dan jenis elektroda untuk melihat pengaruh variabel
tersebut terhadap hasil hardfacing baja tahan aus CREUSABRO 8000. Elektroda
yang digunakan adalah MG DUR-3 dan AWS 309L sebagai lapisan buttering, dan
MG DUR-65 sebagai lapisan hardfacing. Pengujian yang dilakukan meliputi
pengamatan visual, pengamatan radiografi, pengujian kekerasan, pengujian
keausan, dan pengamatan metalografi. Hasil pengujian menunjukkan bahwa
semakin banyak jumlah lapisan akan meminimalisir retak yang timbul dari proses
hardfacing. Selain itu elektroda AWS 309L menjadi lapisan buttering yang lebih
baik dibanding MG DUR-3 untuk menghindari timbulnya retak.
ABSTRACT
Hardfacing is one of the alternatives to obtain highly mechanical
properties of metal surface. This study vary the amount of layer of buttering and
use different electrodes to see the effect of those variables related to the result of
hardfacing of wear resistance steel CREUSABRO 8000. The electode used were
MG DUR-3 and AWS 309L as buttering layer and MG DUR-65 as hardfacing
layer. A series of tests conducted were visual examination, radiographic
inspection, hardness measurement, wear test, and metallography analysis. The
results showed that as the number of buttering layer increased, there is a decrease
amount of cracks that formed during hardfacing process. Besides, the AWS 309 L
electrode is better than MG DUR-3 as buttering layer to resist formation of cracks.

 File Digital: 1

Shelf
 S42805-Studi pengaruh.pdf :: Unduh

 Metadata

No. Panggil : S42805
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Penerbitan : [Place of publication not identified]: Fakultas Teknik Universitas Indonesia, 2012
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resources
Deskripsi Fisik : xiv, 55 pages ; 30 cm
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S42805 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20308740
 See also