Modifikasi serat Rayon dengan teknik radiasi sebagai Adsorben Uranium = modification of rayon fiber usin radiation techniques as uranium adsorbent

Asep Setiawan; Endang Asijati Widijaningsih Ichsan, supervisor; Zainus Salimi, supervisor; Asep Saefumillah, examiner; Jarnuzi Gunlazuardi, examiner; Helmiyati, examiner; Rahmat Wibowo, examiner ([Publisher not identified] , 2012)

 Abstrak

ABSTRAK
Modifikasi serat rayon menggunakan teknik radiasi sebagai adsorben uranium
telah dilakukan. Modifikasi dilakukan dengan cara kopolimerisasi cangkok
dengan teknik radiasi secara simultan menggunakan monomer N,N'-
metilendiakrilamid (NBA), monomer glycidil metacrylate (GMA), serta
campuran NBA dan GMA yang dicangkokkan pada serat rayon, juga dilakukan
pengikatan asam sitrat sebagai ligan pada serat tercangkok monomer, sehingga
diperoleh kopolimer cangkok Rayon-g-NBA, Rayon-g-NBA-CA, Rayon-g-GMA,
Rayon-g-GMA-CA, Rayon-g-NBA-GMA, dan Rayon-g-NBA-GMA-CA.
Penelitian ini bertujuan untuk membuat serat penukar ion yang dapat
mengadsorpsi uranium dengan kapasitas tukar ionnya yang baik. Parameter yang
dipelajari adalah pengaruh dosis serap, volume monomer, konsentrasi monomer,
dan rasio volume larutan. Serat yang telah dimodifikasi dikarakterisasi sifat
fisiknya diantaranya ditentukan persen cangkok, topologi, sifat termal,
kristalinitas, serta kapasitas tukar ionnya. Hasil yang diperoleh adalah kondisi
optimum untuk memodifikasi serat rayon. Dosis radiasi yang digunakan 0,5 kGy
untuk R-g-NBA dan R-g-GMA; 0,75 kGy R-g-NBA-CA, R-g-GMA-CA, dan Rg-
NBA-GMA; dan 1 kGy untuk R-g-NBA-GMA-CA. Volume monomer
optimum untuk semua serat termodifikasi dengan berat serat 100 mg adalah 10
mL, konsentrasi optimum adalah 5%, rasio volume larutan adalah 8:2 untuk R-g-
NBA-CA, 5:5 untuk R-g-GMA-CA, dan R-g-NBA-GMA, dan 4:2:4 untuk R-g-
NBA-GMA-CA. Dari karakterisasi yang dilakukan terlihat bahwa pencangkokan
berhasil dilakukan dengan melihat persen grafting, spektra IR, sifat panas,
diameter, dan kristalinitas dari serat termodifikasi dibandingkan dengan serat asli.
Serat termodifikasi dengan GMA dan asam sitrat (R-g-GMA-CA) memberikan
hasil terbaik dengan kapasitas adsorpsi terhadap uranium terbesar yaitu 0,3 meq/g
serat.

Abstract
Rayon fiber modification using radiation techniques for uranium metal adsorbent
has been conducted. Modifications conducted by grafting copolymerization with
simultaneous radiation technique using the monomer N, N'-metilendiakrilamid
(NBA), glycidil metacrylate monomer (GMA), as well as a mixture of NBA and
GMA is grafted on a rayon fiber, also made of citric acid as a ligand binding to
the grafted fiber monomer, in order to obtain a graft copolymer Rayon -g-NBA,
Rayon-g-NBA-CA, Rayon-g-GMA, Rayon-g-GMA-CA, Rayon-g-GMA-NBA,
and Rayon-g-NBA-GMA-CA. The study aims to create an ion exchange fibers
which can adsorb uranium with a fine ion exchange capacity. Parameters studied
are, respectively, the influence of absorbed doses, the volume of monomers,
monomer concentrations, and the ratio of solution volumes. Modified fibers were
characterized physical properties of which are determined percentage of,
respectively, persent grafts, topologies, thermal properties, crystallinities, and ion
exchange capacities. The results obtained are optimum conditions for modifying
the rayon fiber. Dose of 0.5 kGy of radiation used for R-g-NBA and R-g-GMA;
0.75 kGy for R-g-NBA-CA, R-g- GMA-CA and R-g-NBA-GMA, and 1 kGy for
R-g-NBA-GMA-CA. Optimum monomer volume for all the fibers modified with
fiber weight of 100 mg was 10 mL, the optimum concentration was 5%, the
solution volume ratio is 8:2 for the R-g-NBA-CA, 5:5 for R-g-GMA-CA- and Rg-
NBA -GMA, and 4:2:4 for the R-g-NBA-GMA-CA. From the characterization
performed shows that the transplant has been successed by observing at,
respectively, the percentage of graftings, IR spectras, thermal properties,
diameters, and crystallinities of the fiber-modified compared to its original fiber.
Fibers modified with GMA and citric acid (R-g-GMA-CA) provided the best
results with the adsorption capacity of the largest uranium metal is 0.3 meq / g
fiber.

 File Digital: 1

 Metadata

No. Panggil : T30997
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2012
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiii, 50 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
T30997 15-18-332623328 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20309333