Pengaruh pemanasan awal dan perbedaan ketebalan pelat terhadap ketahanan retak dan sifat mekanis baja tahan aus CREUSABRO® 4800 dengan pengelasan SMAW multilayer = Effect of preheating and different thickness plate on crack resistance and sifat mekanis of creusabro 4800 wear resistance steel welded by multilayer SMAW process

Harahap, Heri Multi Juliandi; Winarto, supervisor; Badrul Munir, examiner; Dwi Marta Nurjaya, examiner (Fakultas Teknik Universitas Indonesia, 2012)

 Abstrak

ABSTRAK
Retak dingin merupakan salah satu permasalahan yang sering terjadi pada
pengelasan baja tahan aus. Skripsi ini berisi tentang penelitian pengaruh
pemanasan awal dan perbedaan ketebalan pelat Creusabro® 4800 dengan
menggunakan pengelasan Shielded Metal Arc Welding (SMAW) Multilayer.
Elektroda yang digunakan adalah elektroda E 7018 dan MG NOX 35. Sampel
yang digunakan terdiri dari delapan buah sambungan pelat baja CREUSABRO®
4800 dengan ketebalan 12 mm dan 16 mm yang dilas dengan variasi elektroda E
7018 dan MG NOX 35 sebagai root atau cap dengan sistem silang . Dua buah
sampel ketebalan 12 mm dan dua buah sampel ketebalan 16 mm diberikan proses
pemanasan awal yang dilakukan dengan menggunakan pemanas listrik dengan
temperatur pemanasan awal 2000C. Kemudian, dua buah sampel ketebalan 12
mm dan dua buah sampel ketebalan 16 mm tidak diberikan perlakuan pemansan
awal. Berdasarkan hasil analisa data, retak dingin tidak muncul pada sampel yang
dilas dengan pengelasan multilayer dengan perlakuan pemanasan awal dan tanpa
perlakuan pemanasan awal. Perlakuan pengelasan multilayer dengan variasi root
elektroda E 7018 dan MG NOX 35 memberikan sifat mekanis yang berbeda .
Pemanasan awal memberikan efek menurunkan kekerasan tetapi menambahkan
keuletan material. Laju keausan ditetukan oleh jenis elektroda yang digunakan.
Dalam hal ini laju keausan elektroda E7018 lebih rendah. Karakteristik HAZ yang
terbentuk oleh pengelasan multilayer ini sangat berbeda, dimana luas HAZ yang
terbentuk ketika pengelasan root lebih luas daripada ketika pengelasan cap. Fasa
yang terbentuk sepanjang daerah HAZ adalah fasa martensit. Begitu juga dengan
inti las elektroda E 7018 dan MG NOX 35 yang terbentuk setelah pengelasan
sangat berbeda ketika pengelasan root dan cap. Hal ini jugalah, yang berpengaruh
terhadap sifat mekanis material hasil lasan.
Abstract
Cold cracking is one of the problems that often occur in the welding of wear
resistant steel. This thesis contains a study about the influence of preheating and
the difference in thickness of the plate Creusabro ® 4800 using the Shielded
Metal Arc Welding welding (SMAW) Multilayer. The electrodes used were
electrode E 7018 and NOX MG 35. The sample used consisted of eight pieces of
steel plate joint CREUSABRO ® 4800 with the thickness 12 mm and 16 mm are
welded to the variation of the electrode E 7018 and NOX MG 35 as a root or a
cap with cross-system. Two samples of thickness 12 mm and two samples of
thickness 16 mm given preheating is performed using an electric heater with
preheating temperature of 200 oC. Then, two samples of thickness 12 mm and
two samples of 16 mm thickness are not given preheating treatment. Based on the
results of data analysis, cold cracks do not appear on the welded samples with
multilayer welding with preheating treatment and without pre-heating treatment.
Treatment with a variety of root multilayer welding electrodes E 7018 MG NOX
35 provide different mechanical properties. Preheating gives effect to reduce the
hardness but adds ductility of the material. Wear rate is influenced by the type of
electrodes used. In this case the E7018 electrode wear rate is lower.
Characteristics of the HAZ is formed by a multilayer welding is very different,
where the wide HAZ is formed when welding root wider than cap. Phase formed
along the HAZ was martensitic phase. Core welding electrodes E 7018 and NOX
MG 35 is formed after the welding is very different when weld root and cap. It is
also likely, which affects the mechanical properties of the weld material.

 File Digital: 1

 Kata Kunci

 Metadata

No. Panggil : S43575
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Subjek :
Penerbitan : [Place of publication not identified]: Fakultas Teknik Universitas Indonesia, 2012
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xvii, 92 pages : 30 cm
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S43575 14-17-361879950 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20312649
 See also