ABSTRAK
Deposit laterit adalah salah satu jenis bijih nikel yang memiliki kandungan nikelterbanyak di bumi. Di dalam lapisan laterit, saprolit memiliki kandungan nikelyang lebih tinggi dibandingkan lapisan lainnya. Saprolite biasanya diproses secarasmelting (pirometalurgi) karena memiliki kandungan magnesium yang tinggi.Penelitian ini bertujuan untuk mengetahui sejauh mana keefektifan proseshidrometalurgi dengan lixiviant amonium bikarbonat terhadap perolehan nikel.Bijih saprolit dikarakerisasi secara EDX dan AAS untuk mengetahui komposisiawal bijih. Saprolit direduksi menggunakan batubara 33.33 % wt pada temperatur1250 oC selama 120 menit. Hasil reduksi pemanggangan kemudian diuji denganXRD. Proses pelindihan agitasi pada bijih saprolit yang direduksi dan bijih yangtidak direduksi dilakukan dengan menggunakan larutan amonium bikarbonat padavariasi konsentrasi yaitu 1 M, 2 M, 3 M, 4 M. Kandungan nikel yang larut dalampregnant leach solutiont dihitung menggunakan Atomic Absorbance Spectroscopy(AAS).Hasil XRD saprolit menunjukkan terjadi transformasi fasa dari goethite dan Fe2O3sebelum reduksi pemanggangan menjadi Fe3O4, NiO dan FeNi setelah reduksipemanggangan Hasil penelitian menunjukan % perolehan Ni semakin meningkatdengan peningkatan konsentrasi amonium bikarbonat. Perolehan nikel tertinggiyang diperoleh adalah 1.61 % pada konsentrasi pada konsentrasi 4 M amoniumbikarbonat.
Abstract
Laterite deposit is a kind of nickel ores that has the greatest of nickel reserves in theworld. In the lateritic layer, saprolite has higher nickel content more than otherlayers. Saprolite is usually process with smelting method (pyrometallurgy)because it has higher magnesium content.The aim of this research is to know the effectiveness of hydrometallurgy processusing ammonium bicarbonate as lixiviant to nickel recovery from saprolite ore.Saprolite was caracterized with Energy Dispersive X-Ray (EDX) and AtomicAbsorbance Spectroscopy (AAS) to determine it?s chemical composition. Floatsinkprocess was apllied to saprolite to separate material based on it?s weigth.Saprolite was reduced at 1250 oC for 120 minutes utilized coal 33.33% wt as areductant, then it was tested with XRD. Agitation leaching process was applied toreduced and unreduced saprolite utilized ammonium bicarbonate solution as lixiviantat various concentration which was 1 M, 2 M, 3 M, 4 M. Nickel content thatdissolved in lixiviant was determined with Atomic Absorbance Spectroscopy(AAS).Result of XRD characterization shows phase transformation in saprolite fromgoethite and Fe2O3 before reduction roasting to Fe3O4, NiO and FeNi afterreduction roasting. The result of research shows that % recovery of Ni is tend toincrease along with the increasing of ammonium bicarbonat concentration. Thehigest nickel recovery in research is 1.61 % at 4 M ammonium bicarbonatconcentration. |