Hydrogen absorption induced slow crack growth in austenitic stainless steels for petrochemical pressure vessel industries
([Direktorat Riset dan Pengabdian Masyarakat Universitas Indonesia, Fakultas Teknik Universitas Indonesia], 2010)
|
Type 304L and type 309 austenitic stainless steels were tested either by exposed to gaseous hydrogen or undergoing polarized cathodic charging. Slow crack growth by straining was observed in type 304L, and the formation of α? martensite was indicated to be precursor for such cracking. Gross plastic deformation was observed at the tip of the notch, and a single crack grew slowly from this region in a direction approximately perpendicular to the tensile axis. Martensite formation is not a necessary condition for hydrogen embrittlement in the austenitic phase. |
No. Panggil : | |
Subjek : | |
Penerbitan : | [Place of publication not identified]: [Direktorat Riset dan Pengabdian Masyarakat Universitas Indonesia, Fakultas Teknik Universitas Indonesia], 2010 |
Sumber Pengatalogan : | |
ISSN : | |
Majalah/Jurnal : | Makara : Teknologi |
Volume : | Vol. 14, No. 2, November 2010: 111-115 |
Tipe Konten : | |
Tipe Media : | |
Tipe Carrier : | |
Akses Elektronik : | http://journal.ui.ac.id/index.php/technology/article/viewFile/702/668 |
Institusi Pemilik : | Universitas Indonesia |
Lokasi : | Direktorat Riset dan Pengabdian Masyarakat UI |
No. Panggil | No. Barkod | Ketersediaan |
---|---|---|
TERSEDIA |
Ulasan: |
Tidak ada ulasan pada koleksi ini: 20328617 |