Pengaruh substitusi Ion Fe dan Ti pada senyawa Perovskite LSMO terhadap sifat absorpsi gelombang mikro = Microwave absorption properties of Fe and Ti substituted LSMO Perovskite

Koko Budiarto; Azwar Maas, supervisor; Bambang Soegijono, examiner; Muhammad Hikam, supervisor; Soehardjo Poertadji, supervisor (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013)

 Abstrak

Penelitian ini mempelajari pengaruh substitusi ion Fe dan Ti terhadap struktur kristal,sifat magnet, dan sifat penyerapan gelombang mikro pada bahan La0.67Sr0.33Mn1-xFexO3 (x= 0;0.5;0.75;1 ) dan La0,67Sr0,33FeyMn(1-y)/2Ti(1-y)/2O3 (y=0,25;0,5;0,75) yang dibuat melalui reaksi padatan konvensional dari bahan dasar La2O3, SrCO3, Fe2O3, MnCO3, TiO2. Pola difraksi XRD menunjukkan bahwa untuk semua nilai x dan y bahan terdiri atas satu fasa yakni La0,9125MnO3 dengan struktur monoklinik (space group I 1 2/a 1). Ditinjau dari kurva histeris, sifat magnet bahan La0,67Sr0,33Mn1-xFexO3 adalah ferromagnet untuk x=0, dan lebih khusus lagi dapat dikategorikan sebagai softmagnet. Sedangkan saat dilakukan substitusi Fe ternyata nilai saturasi magnet mendekati nol. Pada bahan La0,67Sr0,33FeyMn(1-y)/2Ti(1-y)/2O3 kurva histerisis memperlihatkan bahwa bahan tersebut memiliki sifat magnet permanen, meskipun dengan nilai saturasi yang rendah. Pada bahan La0,67Sr0,33Mn1-xFexO3 , penyerapan gelombang akan optimum untuk x=0,5 di frekuensi 15,2 GHz dengan nilai Reflection loss sebesar -13 dB. Sedangkan pada bahan La0,67Sr0,33FeyMn(1-y)/2Ti(1-y)/2O3, penyerapan gelombang optimum untuk y=0,75 di frekuensi 15,2 GHz dengan nilai Reflektansi loss sebesar -18,2 dB.

Crystal structure, magnetic properties, and microwave absorption were investigated on La0.67Sr0.33Mn1-xFexO3 (x= 0;0.5;0.75;1 ) and La0,67Sr0,33FeyMn(1-y)/2Ti(1-y)/2O3 (y=0,25;0,5’0,75). The compounds were made by mixing of high purity La2O3, SrCO3, Fe2O3, MnCO3, and TiO2 through mechanical milling. For all x and y , the diffraction pattern showed that all compounds are single phase, which is La0.9125MnO3 and the structure is monoclinic (space group I 1 2/a 1). Referring to hysterisis curve, La0.67Sr0.33Mn1-xFexO3 behaved as a ferromagnet for x=0, and it was a softmagnet particularly. Addition of Fe decreased the magnetic saturation near to zero. On the other hand, La0,67Sr0,33FeyMn(1-y)/2Ti(1-y)/2O3 was a permanent magnet with high coercive force. La0.67Sr0.33Mn1-xFexO3 showed an optimum reflection loss as high as -13 dB when x=0.5 at 15.2 GHz. Whereas the absorption peak of La0.67Sr0.33Fey(Mn,Ti)½(1-y)O3 showed appeared when y=0.75 at 15.2 GHz with height of -18.2 dB.

 File Digital: 1

Shelf
 T 32738-Koko Budiarto.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : T32738
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xii, 46 pages : illustration ; 28 cm
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
T32738 15-23-28106582 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20330311