Pengaruh aplikasi pasta CPP-ACP terhadap kekasaran permukaan semen ionomer kaca Pit dan Fissure Sealant setelah perendaman dalam Coca Cola = The effect of CPP-ACP paste to surface roughness of Pit and Fissure Sealant glass ionomer cement in Coca Cola
Putri Fatimatus Zahro;
Ellyza Herda, supervisor; Mia Damiyanti, supervisor
(Fakultas Kedokteran Gigi Universitas Indonesia, 2013)
|
Skripsi ini membahas mengenai pengaruh aplikasi pasta CPP-ACP terhadap kekasaran permukaan semen ionomer kaca (SIK) pit dan fissure sealant (PFS) setelah perendaman dalam Coca Cola® dengan melakukan perendaman spesimen SIK PFS dalam akuabides (kontrol), perendaman Coca Cola®, pengaplikasian pasta CPP-ACP yang dilanjutkan dengan perendaman dalam Coca Cola® serta pengaplikasian pasta CPP-ACP yang didiamkan selama 30 menit lalu dilanjutkan dengan perendaman dalam Coca Cola®. Hasil penelitian menunjukkan peningkatan kekasaran permukaan yang signifikan pada spesimen yang direndam dalam Coca Cola®, penurunan kekasaran permukaan yang tidak signifikan pada spesimen yang diaplikasikan pasta CPP-ACP lalu direndam dalam Coca Cola®, serta penurunan kekasaran permukaan yang signifikan pada spesimen yang diaplikasikan pasta CPP-ACP dan didiamkan selama 30 menit kemudian direndam dalam Coca Cola®. Pengaplikasian pasta CPP-ACP yang didiamkan selama 30 menit menunjukkan perbedaan penurunan kekasaran permukaan yang signifikan dengan yang langsung direndam dalam Coca Cola®. This thesis aims to analyze the effect CPP-ACP paste to surface roughness of pit and fissure sealant (PFS) Glass Ionomer Cement (GIC) after placed in Coca Cola® drink. Speciments placed in aquabidest, placed in Coca Cola®, application of CPP-ACP paste then immediately placed in Coca Cola®, and application of CPP-ACP, waited for 30 minutes then placed in Coca Cola®. Surface roughness increased significantly after placed in Coca Cola®. No significant differences were found after application of CPP-ACP placed in Coca Cola® immediately. Surface roughness decreased significantly after application of CPP-ACP waited for 30 minutes then placed in Coca Cola®. The application of CPP-ACP pasteafter waited for 30 minutes then placed in Coca Cola® shows significant differences of PFS GIC’s surface roughness with speciments applicated by CPP-ACP paste and immediately placed in Coca Cola®. |
![]()
|
No. Panggil : | S44517 |
Entri utama-Nama orang : | |
Entri tambahan-Nama orang : | |
Subjek : | |
Penerbitan : | Jakarta: Fakultas Kedokteran Gigi Universitas Indonesia, 2013 |
Program Studi : |
Bahasa : | ind |
Sumber Pengatalogan : | |
Tipe Konten : | |
Tipe Media : | |
Tipe Carrier : | |
Deskripsi Fisik : | xii, 64 hlm. : ill. ; 28 cm. + lamp. |
Naskah Ringkas : | |
Lembaga Pemilik : | Universitas Indonesia |
Lokasi : | Perpustakaan UI, Lantai 3 |
No. Panggil | No. Barkod | Ketersediaan |
---|---|---|
S44517 | 14-22-76810626 | TERSEDIA |
Ulasan: |
Tidak ada ulasan pada koleksi ini: 20330879 |