Pengaruh aplikasi pasta CPP- ACP terhadap kekasaran permukaan semen ionomer kaca konvensional setelah perendaman dalam Coca Cola = The effect of CPP-ACP paste on surface roughness of conventional glass ionomer cement after Coca Cola immersion
Puti Bianca Sari;
Ellyza Herda, supervisor; Mia Damiyanti, supervisor
(Fakultas Kedokteran Gigi Universitas Indonesia, 2013)
|
|
Skripsi ini membahas pengaruh aplikasi pasta CPP-ACP terhadap kekasaran permukaan semen ionomer kaca (SIK) konvensional setelah perendaman Coca Cola® dengan cara merendam dalam akuabides (kontrol), Coca Cola®, serta pengaplikasian pasta CPP-ACP yang didiamkan 30 menit atau langsung direndam Coca Cola®. Hasil penelitian menunjukkan terjadi peningkatan kekasaran permukaan yang signifikan pada kelompok rendaman Coca Cola®, penurunan kekasaran permukaan yang tidak signifikan pada SIK konvensional yang diaplikasikan pasta CPP-ACP langsung direndam Coca Cola® dan penurunan kekasaran permukaan yang signifikan pada SIK konvensional yang diaplikasikan pasta CPP-ACP dan didiamkan 30 menit sebelum direndam Coca Cola®. Kesimpulan dari penelitian ini pengaplikasian pasta CPP-ACP baik didiamkan selama 30 menit ataupun langsung direndam Coca Cola® tidak menunjukkan perbedaan penurunan kekasaran permukaan yang signifikan. This research discusses about the efficacy of application CPP-ACP paste toward surface roughness of conventional glass ionomer cement (GIC) after immersion in Coca Cola® by immersing the specimens in aquabides (control group), Coca Cola®, applying CPP-ACP paste then immersed in Coca Cola® directly or in the next 30 minutes. This research showed that the surface roughness of conventional GIC increased significantly after immersing in Coca Cola®, while after applying CPP-ACP paste then immersed in Coca Cola®, surface roughness of conventional GIC decreased. Furthermore, there were significant decreasing of surface roughness of conventional GIC after applying CPP-ACP paste then immersed in Coca Cola® in the next 30 minutes. The conclusion is the decreasing surface roughness of conventional GIC between after applying CPP-ACP paste then immersed in Coca Cola® directly and in the next 30 minutes are not significantly different. |
 S45410 Puti Bianca Sari.pdf :: Unduh
|
| No. Panggil : | S45410 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Subjek : | |
| Penerbitan : | Jakarta: Fakultas Kedokteran Gigi Universitas Indonesia, 2013 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | |
| Tipe Konten : | |
| Tipe Media : | |
| Tipe Carrier : | |
| Deskripsi Fisik : | xii, 41 hlm. : ill. ; 28 cm. + lamp. |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S45410 | 14-22-95832753 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20331002 |