Studi adsorpsi fosfat oleh mineral gibsit dan gibsit diinterkalasi litium (LIG) = Study of phosphate adsorption by gibbsite mineral and lithium intercalated gibbsite (LIG)

Hariska Lukmana; Sihombing, Riwandi, supervisor; Yuni Krisyuningsih, supervisor (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013)

 Abstrak

Dalam penelitian ini, dilakukan preparasi gibsit diinterkalasi litium (LIG) dari mineral gibsit alam. LIG dipreparasi melalui interkalasi LiCl ke gibsit dan membentuk struktur [LiAl2(OH)6]+ dengan lapisan interlayer ion Cl- dan air. LIG ini memiliki efektivitas dan kapasitas lebih baik dibanding mineral gibsit untuk menghilangkan fosfat dalam air. Adsorpsi terjadi melalui pertukaran anion Cl- di- interlayer dalam LIG dengan fosfat. Adsorpsi maksimum pada pH 4,5 dan menurun dengan meningkatnya pH, karena adanya kompetisi dengan anion OH- seiring kenaikan pH. Pertukaran anion adalah reaksi yang cepat, selesai dalam beberapa menit. Sebaliknya, adsorpsi pada permukaan adalah proses yang lambat dan membutuhkan beberapa hari untuk mencapai kesetimbangan. Adsorpsi pada pH asam lebih banyak dalam bentuk ion monovalen H2PO4-, dan adsorpsi pada pH yang lebih tinggi cenderung lebih selektif terhadap ion divalen HPO42- dan OH-. Hasil ini menunjukkan bahwa LIG menjadi pengadsorpsi yang efektif untuk menghilangkan fosfat dalam air pada kondisi pH 4,5.

In this research, preparation gibbsite intercalated lithium (LIG) of mineral gibbsite nature. LIG was prepared by intercalation of LiCl into gibbsite and form structures [LiAl2(OH)6]+ with ion Cl- layers and interlayer water. LIG has better effectiveness and capacity than gibbsite mineral to eliminate phosphates in the water. Adsorption occurs through anion exchange of Cl- in LIG with phosphate in the interlayer. Maximum adsorption at pH 4.5 and decreased with increasing pH, due to competition with OH- anions with increasing pH. Anion exchange reaction is rapid, complete in a few minutes. In contrast, adsorption on the surface is a slow process and can take several days to reach equilibrium. Adsorption at pH more acidic in the form of monovalent ion H2PO4-, and adsorption at higher pH tend to be more selective about divalent ion HPO42- and OH-. These results suggest that LIG be effective adsorbent for removing phosphate in water at pH 4.5 conditions.

 File Digital: 1

Shelf
 S44353-Studi adsorpsi.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : S44353
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013
Program Studi :
Bahasa : ind
Sumber Pengatalogan :
Tipe Konten :
Tipe Media :
Tipe Carrier :
Deskripsi Fisik : xiv, 45 hlm. : ill. ; 28 cm. + lamp.
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S44353 14-20-146985245 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20331408