Sintesis dan karakterisasi Zeolit Mn/ZSM-5 dengan metode impregnasi sebagai katalis dalam konversi Glukosa menjadi Asam Levulinat = Synthesis and characterization of Mn/ZSM-5 Zeolite using impregnation method as a catalyst for conversion of Glucose to Levulinic Acid
Yessica Savitri;
Yuni Krisyuningsih Krisnandi, supervisor; Endang Saepudin, supervisor
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013)
|
|
Sintesis zeolit ZSM-5 mikropori menggunakan template TPAOH pada sistem hidrotermal di dalam autoclav pada suhu 150°C selama 144 jam. Karakterisasi menggunakan FTIR, XRD, SEM-EDS dan BET. Hasil karakterisasi dapat disimpulkan bahwa zeolit yang terbentuk adalah ZSM-5 Mikropori. Hal tersebut ditandakan dengan kurva isoterm adsorpsi yang menyerupai tipe I. Katalis disiapkan dengan metode impregnasi ion Mangan (II) sebesar 1 wt% dan 2 wt% sehingga diperoleh Mn/ZSM-5. Zeolit Mn/ZSM-5 dikarakterisasi menggunakan AAS, FTIR, EDX dan XRD. Hasil AAS menunjukan kadar Mn di dalam ZSM-5 adalah sebesar 1,5% dan 2,26%. Sedangkan hasil EDX menunjukan kadar Mn dalam ZSM-5 sebesar 1,05% dan 2,20%. Karakterisasi menggunakan FTIR memperlihatkan adanya puncak vibrasi ulur Mn-O pada 625.91 cm-1. Hasil XRD menunjukan penurunan kristalinitas di puncak difraktogram Mn/ZSM-5. Uji aplikasi katalis adalah melakukan reaksi dehidrasi dengan menggunakan kombinasi sistem mirip fenton, yaitu masing-masing katalis hasil sintesis, H3PO4, H2O2, dan glukosa murni sebagai reaktan. Reaksi dilakukan pada suhu 130°C dan menggunakan variasi waktu 24 jam. Produk dianalisis dengan HPLC untuk melihat hasil konversi glukosa menjadi asam levulinat. Katalis yang paling baik adalah Mn/ZSM-5 2 wt % dengan konversi glukosa sebesar 96 % dan yield asam levulinat sebesar 67 %. Microporous ZSM-5 zeolite was hydrothermally synthesized using TPAOH template in autoclav at 150°C in 144 hours. Characterization by SEM-EDS, XRD, FTIR and BET showed that both as synthesized zeolites are microporous ZSM-5, as they had type I of isotherm adsorption curves. Catalysts were prepared by impregnating Manganese ions (Mn (II)) 1 wt% and 2 wt% in each microporous ZSM-5 and characterized by AAS, FTIR, EDX and XRD. The result of AAS showed the value of Mn in ZSM-5 were 1.50% and 2.26% whereas the result of EDX showed the value of Mn in ZSM-5 were 1.05% and 2.20%. FTIR characterization showed a shoulder peak at 626 cm-1 attributed to VMn-O. The result of XRD showed decreasing crystallinity of Mn/ZSM-5 as the peaks were broadening and had lower intensity. Catalyst was employed in dehidration reaction of pure glucose as starting material with combined fenton-like system such as : each ZSM-5, H3PO4, H2O2 as catalyst. Reaction was performed at 130°C with 24 hour variation of time. The data of glucose conversion into levulinic acid was collected by performing HPLC to the product of reaction. The best catalyst was Mn/ZSM-5 2 wt % which had 96% of glucose conversion and 57% of yield levulinic acid. |
 S45603 Yessica Savitri.pdf :: Unduh
|
| No. Panggil : | S45603 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | |
| Tipe Konten : | |
| Tipe Media : | |
| Tipe Carrier : | |
| Deskripsi Fisik : | xiv, 61 hlm. : ill. ; 28 cm. + lamp. |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S45603 | 14-22-80272201 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20331471 |