Pengaruh substitusi ION Fe-Ti terhadap ION Mn pada sistem La1-xSrxMnO3 sebagai material penyerap gelombang mikro frekuensi 9-15 GHz = The influence of Fe-Ti ions substitution to MN in the La1-xSrxMnO3 as microwave absorbing materials in the frequency range 9-15 GHz
Abdul Qadir Azhar;
Azwar Manaf, supervisor
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013)
|
Telah dilakukan karakterisasi parameter kristal, sifat kemagnetan dan serapan gelombang mikro pada material berbasis lanthanum-strontium manganite komposisi La1-xSrxMnO3 (x=0-1) serta efek subsitusi parsial ion Fe dan Ti pada material komposisi La0.7Sr0.3Mn1-yFey/2Tiy/2O3 (y = 0-1). Preparasi material dilaksanakan melalui metode pemaduan mekanik diikuti dengan sintering pada temperatur 1100C selama 2 jam. Hasil pengujian dengan XRD terhadap material pasca perlakuan sintering memastikan material terdiri dari fasa kristalin. Diketahui bahwa ion Sr tidak dapat mensubsitusi ion La sepenuhnya pada senyawa komposisi La1-xSrxMnO3 dengan batas kelarutan x = 0.3 tanpa terjadi perubahan sistem kristal dan fasa tunggal. Substitusi ion Fe terhadap ion Mn pada senyawa komposisi La0.7Sr0.3Mn1-yFeyO3 (y=0-1) tidak menyebabkan perubahan struktur kristal yaiu tetap berstruktur monoklinik dikarenakan jari-jari ion Fe3+(6.4 nm) dan Mn4+ (5.4 nm) tidak jauh berbeda. Namun, tidak demikian dengan efek subsitusi parsial ion Ti4+ pada komposisi La0.7Sr0.3Mn1-yTiyO3 (y=0-0.8) ditandai dengan perubahan struktur kristal monoklinik pada y = 0 menjadi orthorombik pada komposisi 0 Crystal parameter as well as magnetic properties and microwave absorption characteristics of material based on lanthanum-strontium manganese with La1- xSrxMnO3 (x = 0-1) compositions have been characterized. These are including the effects of partial substitution of Fe ions in La0.7Sr0.3Mn1-yFey/2Tiy/2O3 (y=0-1) series. Material preparation was carried out through mechanical alloying method followed by sintering at a temperature of 1100 0C for 2 hours. Identification study of x-rays traces for sintered materials ensured that all materials consisted of crystalline phases. It is shown that Sr ion can completely substitutes La ion in the La1-xSrxMnO3 (x = 0.3) compositions with no change in the crystal system and remains as single phase materials. Similarly, there was also no crystal structure changing observed when Fe ion substituted the Mn ion in the La0.7Sr0.3Mn1-yFeyO3 (y=0-1) compositions. Apparently, the crystal structure was maintained due to almost similar size of ionic radii between Fe3+ (6.4 nm) and Mn4+ (5.4 nm). However, a different case occurred in Ti substituted La0.7Sr0.3Mn1-yTiyO3 (y=0-0.8) in which the crystal structure of monoclinic for y = 0 changed to orthorhombic for 0 |
![]()
|
No. Panggil : | S52501 |
Entri utama-Nama orang : | |
Entri tambahan-Nama orang : | |
Subjek : | |
Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013 |
Program Studi : |
Bahasa : | ind |
Sumber Pengatalogan : | |
Tipe Konten : | |
Tipe Media : | |
Tipe Carrier : | |
Deskripsi Fisik : | xv, 87 hlm.: ill.; 28cm + lamp. |
Naskah Ringkas : | |
Lembaga Pemilik : | Universitas Indonesia |
Lokasi : | Perpustakaan UI, Lantai 3 |
No. Panggil | No. Barkod | Ketersediaan |
---|---|---|
S52501 | 14-23-50530753 | TERSEDIA |
Ulasan: |
Tidak ada ulasan pada koleksi ini: 20345274 |