Efek penambahan Ni terhadap struktur dan sifat optik nanopartikel TiO2 yang disintesis dengan metode kopresipitasi = The effect of Ni doping on structural and optical properties of TiO2 nanoparticles prepared by coprecipitation method
Dwi Cahayaningsih;
Rosari Saleh, supervisor
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013)
|
|
Satu seri nanopartikel TiO2 didop Ni dengan variasi konsentrasi Ni dibuat dengan metode kopresipitasi. Komposisi elemen, sifat strukFtur, dan optik dikarakterisasi menggunakan X-Ray Diffraction, Electron Dispersive X-Ray dan UV-VIS diffuse reflectance spectroscopy. Identifikasi spesies paramagnetik dilakukan menggunakan Electron Spin Resonance. Berdasarkan pola difraksi XRD, hanya fase tunggal anatase yang muncul karena radius ionik Ni2+ dan Ti4+ yang hampir sama sehingga dapat menggantikan ion-ion Ti4+ pada kristal TiO2. Ukuran kristal rata-rata menurun seiring dengan peningkatan konsentrasi Ni.Fenomena ini kemungkinan terjadi akibat kehadiran ion-ion Ni2+ yang menghambat pertumbuhan kristal. Spektrum reflektansi difus UV-VIS menunjukkan bahwa penyerapan UV bergeser ke arah panjang gelombang sinar merah dan celah pita energi menurun. Hal ini disebabkan oleh atom-atom Ni yang membentuk levellevel energi localized dibawah pita konduksi pada kristal TiO2. Studi ESR pada nanopartikel TiO2 didop Ni menunjukkan adanya kehadiran Ni+, Ti3+, dan defek oksigen pada semua sampel. A series Ni doped TiO2 nanoparticles with different Ni dopant concentration were facricated by coprecipitation method. The element composition, structural, and optical properties were characterized using X-Ray Diffraction, Electron Dispersive X-Ray and UV-VIS diffuse reflectance spectroscopy. Identification of paramagnetic species are conducted using Electron Spin Resonance. Based on XRD pattern, only single phase of anatase were appeared because the almost similar ionic radius of Ni2+ to that of Ti4+ which was found to replace some portion of Ti4+ ions in TiO2 lattice. The crystallite size decreases with increasing Ni content.This phenomena probably arisen from introducing of Ni2+ ions which decrease crystalline growth. The UV-VIS diffuse reflectance spectra showed that the UV absorption moved to a longer wavelength (red shift) and the band gap energy was decreased. It caused the doped Ni atoms formed a localized energy states below conduction band of TiO2 lattice. ESR studies of Ni doped TiO2 nanoparticles revealed the presence of Ni+, Ti3+, and oxygen defects in all samples. |
 S46654-dwi_cahayaningsih.pdf :: Unduh
|
| No. Panggil : | S46654 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | |
| Tipe Konten : | |
| Tipe Media : | |
| Tipe Carrier : | |
| Deskripsi Fisik : | xii, 46 hlm. : il. ; 28 cm. |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S46654 | 14-22-04805778 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20345464 |