Analisa sistem kristal dan ukuran kristal pada material la0 67ba0 33mn1 xtixo3dengan variasi x 0 0 02 0 04 0 06 melalui proses mechanical alloying = Crystal system and size analysis of the la0 67ba0 33mn1 xtixo3with the variation x 0 0 02 0 04 0 06 material through mechanical alloying process
Gabriella Permata Widyaputrie;
Budhy Kurniawan, supervisor
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013)
|
|
Telah dilakukan penelitian pada paduan La0.67Ba0.33Mn1-xTixO3 dengan variasi x=0; 0.02; 0.04; 0.06 dengan mensintesa dan mengkarakterisasi bahan tersebut. Sintesa dilakukan menggunakan metode mechanical alloying dengan mencampurkan bahan-bahan dasar penyusun yakni La2O3, BaCO3, MnCO3, dan TiO2. Campuran ini kemudian dimilling selama 10 jam kemudian dikarakterisasi menggunakan Thermogravimetry Analysis (TGA). Kemudian dilakukan proses kalsinasi pada suhu 800º C selama 8 jam dan dilanjutkan dengan proses sintering pada suhu 1100º C selama 12 jam. Karakterisasi lainnya menggunakan difraksi sinar-X (XRD) sebelum sintering dan setelah sintering yang menunjukkan paduan La0.67Ba0.33Mn1-xTixO3 telah memiliki fasa tunggal dengan sistem kristal monoklinik,dengan parameter kisi a=5.53 Å ; b=5.54 Å ; c=7.8 Å dan space group I 1 2/c 1 (15), Particle Size Analyzer (PSA) menunjukkan hasil ukuran partikel besar untuk sampel yang tidak disintering. Scanning Electron Microscopy (SEM) untuk melihat morfologi permukaan. Hasil ukuran kristalit rata-rata menggunakan metode Debye-Scherrer.menghasilkan ukuran kristalit rata-rata material LBMO sebesar 60.3 nm dan LBMTO untuk setiap variasi x sebesar `~78.8 nm. This research focuses on the mixture La0.67Ba0.33Mn1-xTixO3with the value x=0; 0.02; 0.04; 0.06. The x variation is done through synthesis and characterizing the sample. The method of synthesis is mechanical alloying, by mixing the basic compounds La2O3, BaCO3, MnCO3 with TiO2. The milling process of this mixture is 10 hours, then characterized using Thermogravimetry Analysis (TGA). Then, calcination at 800º C for 8 hours followed by sintering at 1100º C for 12 hours. XRD is done, in addition, before and after sintering. Results show the mixture La0.67Ba0.33Mn1-xTixO3have a single phase monoclinic crystal structure with cell parameter a=5.53 Å ; b=5.54 Å ; c=7.8 Åand space group I 1 2/c 1 (15). PSA shows big particles for samples not undergoing sintering. SEM is used to analyze the surface morphology. The Debye-Scherrer method calculates the average resulting crystallites, with values LBMO = 60.3nm and for LBMTO = 78.8nm (for each x variation). |
 S46122-Analisa sistem.pdf :: Unduh
|
| No. Panggil : | S46122 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | |
| Tipe Konten : | |
| Tipe Media : | |
| Tipe Carrier : | |
| Deskripsi Fisik : | xi, 54 hlm. : ill. ; 28 cm + lamp. |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S46122 | 14-22-16117639 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20347502 |