Efek substitusi Ti (x=0, 0.1, 0.15, 0.2) pada parameter kristal dan morfologi bahan La0.85Ba0.15Mn(1-x)Ti(x)O3 = Substitution effect of Ti (x=0, 0.1, 0.15, 0.2) on crystal parameter and morphology of the La0.85Ba0.15Mn(1-x)Ti(x)O3 compound
Haniyah Nadhira;
Budhy Kurniawan, supervisor
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013)
|
|
Penelitian efek substitusi Ti pada paduan La0.85Ba0.15Mn(1-x)TixO3 ( x = 0, 0.1, 0.15, and 0.2) dipersiapkan dengan metode mechanical milling selama 25 jam, suhu kalsinasi sebesar 800oC selama 10 jam dan suhu sintering 1200oC selama 12 jam berdasarkan hasil uji TGA dan DSC. Kurva XRD (X-Ray Diffraction) menunjukkan fasa tunggal, sistem kristal monoklinik dengan group ruang (space group) ’I 1 2/c 1’ pada suhu ruang. Terdapat kenaikan pada parameter kisi, volum unit sel, dan ukuran kristalit rata-rata dengan meningkatnya substitusi Ti. Hasil SEM (Scanning Electron Microscopy) menunjukkan morfologi bahan, distribusi ukuran partikel dan porositas pada paduan. Ukuran partikel rata-rata paduan didapatkan dengan menggunakan Particle Size Analyzer (PSA). Rata-rata ukuran partikel meningkat setelah mendapatkan perlakuan pemanasan sintering. Research on the effect of titanium substitution on the structure and the particle morphology characterization of manganites with La0.85Ba0.15Mn(1-x)TixO3 ( x = 0, 0.1, 0.15, and 0.2) was carried out. Materials were prepared by using a mechanical milling method for 25 hours. The calcination and sintering temperatures attained based on TGA and DSC results were 800o C for 10 hours and 1200o C for 12 hours. X-ray diffraction patterns of the width La0.85Ba0.15Mn(1-x)TixO3 ( x = 0, 0.1, 0.15, and 0.2) showed single phase, monoclinic system and space group ’I 1 2/c 1’at room temperature. Lattice parameters, volume unit cell, and mean crystallite size increased along with increases in Ti substitution. Scanning electron microscopy (SEM) showed the morphology, surface, distribution of particle size, and porosity of the compound. The mean particle size of the obtained compounds was determined by using a Particle Size Analyzer. Mean particle size increased after the use of the sintering process. |
 S52597-Haniyah Nadhira.pdf :: Unduh
|
| No. Panggil : | S52597 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | |
| Tipe Konten : | |
| Tipe Media : | |
| Tipe Carrier : | |
| Deskripsi Fisik : | xiv, 64 hlm. : il. ; 28 cm. + lamp. |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S52597 | 14-23-23505169 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20347838 |