Transformasi martensit pada stainless steel AISI 304 dengan surface mechanical attrition treatment (SMAT) = Martensite transformation of surface mechanical attrition treated stainless steel AISI 304
Sigma Rizkyardiani Sigit;
Bondan Tiara Sofyan, supervisor; Anne Zulfia Syahrial, examiner; Myrna Ariati Mochtar, examiner
(Fakultas Teknik Universitas Indonesia, 2013)
|
|
Surface Mechanical Attritition Treatment adalah salah satu proses fabrikasi nano materialdengan cara memberikan deformasi mekanis strain-induced pada permukaan material.Penelitian ini memberi perlakuan SMAT pada stainless steel AISI 304 yang merupakanaustenitic stainless steel. Deformasi yang diperlakukan pada permukaan material akanmenghasilkan gradien regangan di seluruh bagian material. Perbedaan regangan dan strainrate mempengaruhi struktur yang terjadi. Semakin tinggi regangan yang diberikan (semakindekat dengan permukaan) menghasilkan butir yang lebih halus hingga skala nanometer. Dansebaliknya, semakin rendah regangan yang dialami maka akan dihasilkan butir yang kasar..Proses SMAT pada baja juga dapat menghasilkan transformasi fasa dari austenit kemartensit. Analisis XRD menunjukkan peningkatan kandungan martensit pada lapisan yangterkena regangan tinggi. Pengamatan TEM menunjukkan transformasi martensit terjadidengan dua mekanisme yaitu dari austenit yang berstruktur kristal FCC () menjadi martensityang berstruktur kristal HCP (ε) dan dari austenit yang berstruktur kristal FCC () menjadimartensit yang berstruktur kristal BCC (α’). Transformasi ini mengikuti arah dan hubungankristalografi Kurdjumov-Sachs (K-S) orientation yaitu 〈1-10〉γ//〈112-0〉ε//〈11-1〉α. Sementarapada bagian yang terkena regangan lebih rendah tetap mengandung fasa austenit.Kombinasi dari butir halus dan kasar serta austenit dan martensit pada material yang samamemungkinkan untuk mendapatkan material yang kuat sekaligus tangguh. Butir halus danfasa martensit pada permukaan akan meningkatkan kekerasan material, sementara butir kasardan fasa austenit pada bagian lebih dalam akan mempertahankan keuletan material. Surface Mechanical Attritition Treatment is one of nano material fabrication method whichdone by applying strain-induced mechanical deformation on the surface. This research treatedstainless steel AISI 304 which is austenitic stainless steel type, with SMAT. The deformationcause strain gradient through out the sample. Strain level differences give effect to materialstructure. Higher strain which happen closely to the surface region, result in finer grain up tonano scale, while lower strain cause more coarse grain.SMAT on stainless steel also could cause phase transformation from austenite to martensite.XRD analysis showed increase of martensite content on higher strain-affected layer. TEMobservations showed martensite transformation by two mechanism, austenite with FCCcrystal structure () to martensite with HCP crystal structure (ε) and austenite with FCCcrystal structure () to martensite with BCC crystal structure (α’). This transformation arefollowing crystalographic orientation relationship of Kurdjumov-Sachs (K-S), 〈1-10〉γ//〈112-0〉ε//〈11-1〉α. While on the other region that less-affected by strain still contain austenitephase.Combination of fine grain-coarse grain and austenite-martensite phase on the same materialcould result in higher properties material since it could has high strenght and high toughness.Fine grain and martensite phase on the surface will increase the hardness of material, whilecoarse grain and austenite phase on deeper layer will increase the ductility of material. |
 T35024-Sigma Rizkyardiani Sigit.pdf :: Unduh
|
| No. Panggil : | T35024 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2013 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | x, 42 pages : illustration ; 28 cm. + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| T35024 | 15-23-88032484 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20349942 |