Efek perlakuan panas terhadap sifat magnet baja tahan karat tipe 304 dan pengaruhnya pada kesalahan penimbangan = Effect of heat treatment on magnetic properties of stainless steel 304 and its effect on the weighing error / Renanta Hayu Kresiani
Renanta Hayu Kresiani;
Bambang Soegijono, promotor; Babmabng Soegiono, examiner; Muhammad A.S. Hikam; Dede Djuhana, examiner
([Publisher not identified]
, 2013)
|
|
ABSTRAK Penggunaan timbangan kompensasi elektromagnetik dalam proses pengukuranmassa di laboratorium menimbulkan potensi peningkatan kesalahan penimbanganyang diakibatkan oleh interaksi antara medan magnet pada pinggan timbangandengan sifat suseptibilitas magnet standar massa yang terbuat dari baja tahankarat austenitik pada saat dilakukan kalibrasi. Penelitian ini dilakukan untukmengamati sifat suseptibilitas magnet serta kesalahan penimbangan pada bajatahan karat tipe 304 serta perubahan sifatnya setelah dilakukan perlakuan panaspada suhu 800 0C dan 1100 0C. Hasil penelitian ini menunjukkan bahwa nilaisuseptibilitas magnet serta kesalahan penimbangan menurun pada sampel yangmengalami perlakuan panas pada suhu 800 0C serta memenuhi persyaratan nilaisuseptibilitas magnet untuk standar massa kelas E2. Sedangkan sampel yangdipanaskan pada suhu 1100 0C nilai suseptibilitas magnet dan kesalahanpenimbangannya meningkat. Perubahan nilai suseptbilitas magnet ini konsistendengan perubahan fraksi massa fasa ferrit pada baja tahan karat tipe 304 yangdiperoleh dari hasil analisis XRD. ABSTRACT The use of electromagnetic force compensation balances in laboratory mayincrease potential error caused by interaction between electromagnetic fieldaffecting weghing pan of the balannce and magnetic succeptibility of massstandards which made of austenitic stainless steel. The evaluation of magneticsucceptibility and its effects to the weighing error of stainless steel 304 as well asmagnetic succeptibility change caused by heat treatment on 800 0C dan 1100 0Cwere examined in this research. The results shows that the magnetic succeptibilityand its weighing error of sample with heat treatment on 800 0C decrease and meetthe magnetic suseptbility requirements of E2 class. Whereas for sample with heattreatment on 11000C the value of magnetic suseptibility and error weighingincrease. The change of the magnetic suseptibility consistent with the change ofweight percent of ferrite on stainless steel 304 obtained based on XRD analysis. |
 T34960-Renata Hayu Kresiani.pdf :: Unduh
|
| No. Panggil : | T34960 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | [Place of publication not identified]: [Publisher not identified], 2013 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xii, 45 pages : illustration 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| T34960 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20350295 |