Analisis Penyerapan Gelombang Elektromagnetik Pada Material La0.5Ba0.5Mn1-xTixO3 Dengan Karakterisasi ESR dan VNA (x= 0; 0.05; 0.10; 0.15) = Electromagnetic Absorption Analysis on La0.5Ba0.5Mn1-xTixO3 (x= 0; 0.05; 0.10; 0.15) Materials Characterized by ESR and VNA
Riansyah Putra;
Budhy Kurniawan, supervisor
(Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013)
|
|
Material La0.5Ba0.5Mn1-xTixO3 (x= 0; 0.05; 0.10; 0.15) berfasa tunggal dengan sistem kristal monoklinik dibuat dengan metode penggerusan mekanik selama 25 jam dan perlakuan sintering pada temperatur 1200o C selama 12 jam. Karakterisasi yang diberikan meliputi pengolahan ulang hasil pengujian ESR (Electron Spin Resonance) untuk mengetahui sifat penyerapan gelombang mikro pada pengaruh medan magnet eksternal secara lebih lengkap dan karakterisasi VNA (Vector Network Analyzer) untuk mengetahui sifat penyerapan gelombang mikro tanpa adanya pengaruh medan magnet eksternal. Diketahui bahwa sifat paramagnetik Ti menurunkan sifat penyerapan senyawa La0.5Ba0.5Mn1-xTixO3 (x= 0; 0.05; 0.10; 0.15) seiring dengan bertambahnya komposisi x pada pengujian ESR. Senyawa dengan sifat penyerapan terbaik dengan pengaruh medan eksternal ditunjukkan oleh senyawa La0.5Ba0.5MnO3 dengan luas kurva penyerapan 4280,19 mT (a.u). Berdasarkan hasil karakterisasi VNA terhadap sampel dengan diameter 25 mm dan ketebalan ±2 mm didapatkan bahwa keseluruhan material La0.5Ba0.5Mn1-xTixO3 (x= 0; 0.05; 0.10; 0.15) memiliki kemampuan menyerap gelombang mikro pada jangkau frekuensi 6-12 GHz. Didapatkan bahwa sampel dengan sifat penyerapan gelombang mikro terbaik adalah senyawa La0.5Ba0.5Mn0.95Ti0.05O3 dengan ketebalan 1,6 mm yang memiliki nilai return loss (RL) terbesar yaitu -9,83 dB pada frekuensi 11,16 GHz dengan lebar frekuensi 1,62 GHz. Lanthanum manganese based materials of La0.5Ba0.5Mn1-xTixO3 (x= 0; 0.05; 0.10; 0.15) with single phase monoclinic crystal system has been made. Each material is prepared through mechanical alloying method for 25 hours and heat treatment through sintering process at 1200 o C for 12 hours. Characterization methods used includes re-calculation of Electron Spin Resonance (ESR) measurement to acquire more detail data to identify microwave absorption properties under external magnetic field and Vector Network Analyzer (VNA) to identify microwave absorption properties without external magnetic field. It was found that Ti paramagnetic properties caused the microwave absorption of La0.5Ba0.5Mn1-xTixO3 (x= 0; 0.05; 0.10; 0.15) to reduced in ESR characterization if more Ti ions substitutes the Mn ions. The ESR characterization showed that La0.5Ba0.5MnO3 (x=0) has the largest absorption curve value of 4280,19 mT (a.u). However, a 25 mm diameter and ±2 mm thickness of La0.5Ba0.5Mn1-xTixO3 (x= 0; 0.05; 0.10; 0.15) samples characterized by VNA showed that the samples are able to absorb microwave in a frequency range of 6-12 GHz. The results also showed that the La0.5Ba0.5Mn0.95Ti0.05O3 with 1,6 mm thick has the largest return loss (RL) value of -9,82 dB at frequency value of 11,16 GHz with bandwidth value of 1,62 GHz. |
 S52843-Riansyah Putra.pdf :: Unduh
|
| No. Panggil : | S52843 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Subjek : | |
| Penerbitan : | Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2013 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | |
| Tipe Konten : | |
| Tipe Media : | |
| Tipe Carrier : | |
| Deskripsi Fisik : | xiii, 57 hlm. : il., ; 28 cm + lamp. |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S52843 | 14-23-10843304 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20367483 |