Sintesis dan Karakterisasi Membran Nanokomposit PVA - Organoclay Tapanuli Terinterkalasi Surfaktan HDTMABr = Synthesis and Characterization of Nanocomposite Membranes of PVA – Organoclay Tapanuli Intercalated by HDTMABr Surfactant
(Universitas Indonesia, 2013)
|
| [Sintesis membran nanokomposit PVA-Organoclay Tapanuli dilakukandengan tahap sintesis organoclay Tapanuli dan sintesis nanokomposit PVAOrganoclayTapanuli. Sintesis organoclay Tapanuli dilakukan denganmenginterkalasikan surfaktan HDTMABr ke dalam gallery clay melalui tahapanpurifikasi, sintesis Na-MMT dan sintesis Organoclay Tapanuli, sedangkanpembuatan membran komposit melalui proses solvent casting. Pengaruhinterkalasi surfaktan diamati dengan XRD dan FTIR. Dari karakterisasi XRD,diketahui bahwa interkalasi surfaktan ke dalam gallery clay meningkatkan nilaibasal spacing organoclay Tapanuli dari 15.96 Å menjadi 18.81 Å. Nanokompositdibuat dari PVA sebagai matriks dan organoclay Tapanuli – HDTMABr sebagainanofiller. Karakterisasi yang dilakukan adalah XRD, FTIR, SEM, dan uji tarik.Dari hasil uji tarik diperoleh pada komposisi 3 wt % organoclay Tapanuli-HDTMABr merupakan hasil yang terbaik. Hal ini dibuktikan dengan nilaimodulus tarik dan nilai kuat tarik yang paling tinggi dibandingkan dengankomposisi lainnya, dengan kenaikan masing-masing 162,3 % dan 13,55 %., PVA – Organoclay Tapanuli nanocomposite membranes were syntesized throughtwo steps, namely the organoclay Tapanuli intercalation process and the PVA –Organoclay Tapanuli nanocomposite syhthesis. The synthesis of organoclayTapanuli was conducted by intercalating the HDTMABr surfactant into the claygallery through purification, Na-MMT synthesis, and organoclay Tapanulisynthesis processes, while solvent casting technique was applied to produced thenanocmposite membranes. The effect of surfactant in the clay gallery wasobserved using XRD, and FTIR. The XRD results showed that, the surfactant wasintercalate into the clay gallery and increased the basal spacing of organoclayTapanuli from 15.96 Å to 18.81 Å. The nanocomposites were characterized usingXRD, FTIR, and SEM, and tensile test was also carried out. The tensile testresults showed that the 3 wt% organoclay Tapanuli – PVA was the best samplecompared to other clay compositions. It was proved that the values of tensilemodulus and tensile strength increased by 162,3 % and 13,55 % respectively.] |
 S52839-Lingga Ghufira Oktariza.pdf :: Unduh
|
| No. Panggil : | S52839 |
| Subjek : | |
| Penerbitan : | [Place of publication not identified]: Universitas Indonesia, 2013 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | |
| Tipe Konten : | |
| Tipe Media : | |
| Tipe Carrier : | |
| Deskripsi Fisik : | xiv, 40 hlm. : il., ; 28 cm |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S52839 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20367501 |