Kajian karakteristik fisik dan mekanik bata tidak dibakar campuran tanah dan kapur yang diperkuat serabut kelapa (0%, 2%, 4%, 6%, dari massa kapur) dengan panjang potongan 2,5 cm = Physical and mechanical characteristic study of unfired soil lime bricks reinforced with 2 5 cm coconut fibres ((0%, 2%, 4%, 6%, from lime mass).
(Fakultas Teknik Universitas Indonesia, 2013)
|
[Skripsi ini membahas hubungan antara kekuatan bata terhadap waktu dari batayang menggunakan serabut kelapa dan tanpa serabut kelapa. Serabut kelapa yangtidak mendapat perlakuan khusus dan yang mendapat perlakuan khusus denganpanjang 2,5 cm yang dapat menguatkan bata campuran kapur dan tanah. Pengaruhdari perkuatan serabut 2,5 cm persentase 4% dengan perlakuan khususdibandingkan pengaruh dari perkuatan serabut 4% tanpa perlakuan khusus,menjadi dasar acuan kadar 4% serabut untuk campuran bata dengan serabutkombinasi panjang 1 cm, 2.5 cm dan 4cm. Penyerapan air pada batu bata jugadievaluasi. Penelitian eksperimental mengungkapkan bahwa untuk semua jenisbatu bata, hingga pada umur 90 hari kuat tekan terjadi sedikit penurunan tetapikuat lentur mengalami penurunan yang tinggi seiring bertambahnya umur. Hasilini menunjukkan bahwa batu bata tidak dibakar yang ditambah dengan serabutkelapa perlakuan khusus menghasilkan nilai kekuatan yang lebih baikdibandingkan dengan batu bata yang ditambah dengan serabut kelapa tanpaperlakuan khusus dan batu bata tanpa serabut kelapa., This undergraduate thesis discusses strength-time relation of unfired bricksreinforced with and without natural fibers. Untreated and treated coconut fiberswith lengths 2.5 cm were prepared for soil lime bricks reinforcements. The effectsof 4% uniform 2.5 cm fiber reinforcement was compared to the effects of 4% nonuniformfiber reinforcement, and its become the basic percentage 4 % fiber forbrick mixed design with combination of fiber length 1 cm, 2,5 cm and 4 cm.Absorption of brick was also evaluated. Experimental investigations reveal thatfor all type of bricks, up to 90 days compressive strengths decrease a little butbending strengths rapidly decrease with time. The results show that unfired bricksadded with uniform treated fiber resulted in better strength performancescompared to those added with untreated, and also to those without fibers.] |
S53829-Mochamad Reza Syaifulloh.pdf :: Unduh
|
No. Panggil : | S53829 |
Subjek : | |
Penerbitan : | [Place of publication not identified]: Fakultas Teknik Universitas Indonesia, 2013 |
Program Studi : |
Bahasa : | ind |
Sumber Pengatalogan : | |
Tipe Konten : | |
Tipe Media : | |
Tipe Carrier : | |
Deskripsi Fisik : | xxii, 64 hlm. : ill. ; 30 cm. + lamp. |
Naskah Ringkas : | |
Lembaga Pemilik : | Universitas Indonesia |
Lokasi : | Perpustakaan UI, Lantai 3 |
No. Panggil | No. Barkod | Ketersediaan |
---|---|---|
S53829 | TERSEDIA |
Ulasan: |
Tidak ada ulasan pada koleksi ini: 20368554 |