Studi pengaruh penggunaan produk cat x dan y serta pengaruh metode preparasi pada temperatur ambient terhadap waktu fabrikasi dan kualitas hasil pengecatan pada aplikasi daerah non splash zone = Study of using painting product x and y and the effect of preparation methods at ambient temperature to fabrication time and the quality of painting at non splash zone area / Rizkia Nadira
Rizkia Nadira;
Johny Wahyuadi Mudaryoto, examiner; Soetopo; Badrul Munir, co-promotor
([Publisher not identified]
, 2014)
|
ABSTRAK Proses fabrikasi Pertamina PHE ONWJ membutuhkan proses fabrikasi yangselesai tepat waktu. Salah satu tahap fabrikasi adalah proses pengecatan bajakarbon agar terhindar dari peristiwa korosi.Penelitian ini menggunakan dua produk cat yang berbeda yaitu produk X(lama) dan produk Y (baru). Produk Y memiliki waktu pengeringan cat yang lebihcepat dibandingan produk X. Proses preparasi permukaan dilakukan dengantingkat kebersihan Sa 2,5 dan Sa 3 pada temperatur ambient saat mengaplikasikancat.Tingkat ketahanan korosi diketahui dengan pengujian kabut garam.Kekuatan daya lekat diketahui dengan pengujian adesi. Cacat poros diketahuidengan pengujian holiday. Mikrostruktur lapisan cat dilihat dengan pengujianmetalografi.Hasil pengujian kabut garam pada metode scratch dan unscratch didapatkankedua jenis cat memiliki ketahanan korosi yang sama. Hasil pengujian adesididapatkan kekuatan adesi produk Y lebih besar dibandingkan produk X. Hasilpengujian metalografi menunjukan adanya poros pada lapisan primer produk X.Waktu fabrikasi produk Y lebih cepat dibandingkan produk X.Kata kunci : Pengecatan, preparasi permukaan, temperatur ambient, non splashzone, Pengujian Kabut Garam, Pengujian Adesi, Holiday, Metalografi,perlindungan logam, korosi, waktu fabrikasi. ABSTRACT Fabrication process on Pertamina PHE ONWJ needs fabrication processthat finish at the right time. One of fabrication process is painting carbon steel toprotect them from corrosion.This research use two paint product, product X (the old product) andproduct Y (the new product). Product Y has faster fabrication time than productX. This research use surface preparation with cleanliness level Sa 25, and Sa 3 atambient temperature when painting application.The level of corrosion resistance is known by salt spray test. Paintadhesion is known by adhesion test. Porosity is known by holiday test.Microstructure of paint layer is known by metallography test.The result of salt spray test with scratch and unscratch method is the twoproducts have same corrosion resistance. The result of adhesion test is product Yhas higher adhesion than product X. The result of metallography is product X hasporous at primer layer. Fabrication time of product Y is faster than product X. |
![]()
|
No. Panggil : | S53792 |
Entri utama-Nama orang : | |
Entri tambahan-Nama orang : | |
Entri tambahan-Nama badan : | |
Subjek : | |
Penerbitan : | [Place of publication not identified]: [Publisher not identified], 2014 |
Program Studi : |
Bahasa : | ind |
Sumber Pengatalogan : | LibUI ind rda |
Tipe Konten : | text |
Tipe Media : | unmediated ; computer |
Tipe Carrier : | volume ; online source |
Deskripsi Fisik : | xvi, 64 pages : illustration ; 30 cm + appendix |
Naskah Ringkas : | |
Lembaga Pemilik : | Universitas Indonesia |
Lokasi : | Perpustakaan UI, Lantai 3 |
No. Panggil | No. Barkod | Ketersediaan |
---|---|---|
S53792 | TERSEDIA |
Ulasan: |
Tidak ada ulasan pada koleksi ini: 20368587 |