Pengaruh penambahan molibdenum pada paduan zirkonium diproduksi melalui metalurgi serbuk untuk aplikasi biomaterial = The effect of addition molybdenum on zirconium alloy produced by powder metallurgy for biomaterial application / Yoza Kurniawan
Yoza Kurniawan;
Badrul Munir; Sri Harjanto, examiner; Yudha Pratesa, examiner; R. Bambang Jaya Bangkit; Sri Harjanto, examiner; Yudha Pratesa, examiner
([Publisher not identified]
, 2014)
|
ABSTRAK Pengembangan paduan zirkonium sebagai biomaterial diproduksi melaluimetode metalurgi serbuk diteliti dengan penambahan unsur paduan molibdenum1%, 3%, 6% dan 9% dan hubungannya terhadap densitas dan porositas, strukturmikro, kekerasan Rockwell C dan sifat bioaktivitas dengan simulated body fluid(SBF). Hasil dari pengujian densitas dan porositas didapatkan bahwa seiringdengan penambahan molibdenum akan menghasilkan porositas yang semakinbanyak. Hal ini terjadi karena seiring dengan penambahan molibdenum akanmenurunkan koefisien difusivitas pada paduan zirkonium. Struktur mikro yangterbentuk didominasi fasa α-Zr dan Mo2Zr. Namun seiring dengan penambahanmolibdenum, akan terbentuk fasa γ-Mo yang merupakan serbuk molibdenum yangtidak terdifusi ke dalam β-Zr dalam proses sinter. Kekerasan yang dicapai padapenambahan molibdenum bervariasi antara 42 HRC hingga 45 HRC, dimanaterendah dicapai 3% Mo dengan 42,14 HRC dan tertinggi 6% Mo dengan 45,08HRC. Hal ini dipengaruhi oleh jumlah porositas dan fasa Mo2Zr yang terbentuk didalam paduan. Sifat bioaktivitas logam zirkonium semakin menurun seiringdengan penambahan molibdenum yang disebabkan oleh terbentuknya fasa γ-Mopada struktur mikro. ABSTRACT Development of zirconium alloy as biomaterial produced with powdermetallurgy method is observed from the effect of 1%, 3%, 6% and 9%molybdenum addition on density and porosity, microstructure, Rockwell Chardness and bioactivity properties with simulated body fluid (SBF). The result ofdensity and porosity testing shows the increasing molybdenum content canproduce more porosity on alloys. That caused by the addition of molybdenumwould decrease coefficient of diffusivity in zirconium alloys. Microstructureformed predominantly α-Zr phase and Mo2Zr. But along with the addition ofmolybdenum, will form γ-Mo phase which is the molybdenum powders did notdiffuse into β-Zr on sintering process. Hardness on addition of molybdenumvaries between 42 HRC to 45 HRC, which in the lowest achieved by 3% Mo with42,12 HRC and the highest achieved by 6% Mo with 45,08 HRC. That ininfluenced by the amount of porosity and Mo2Zr phase in the alloys. Bioactivityproperties in zirconium alloy will decrease along with the addition ofmolybdenum, which caused the formation of γ-Mo phase on the microstructure. |
S53849-Yoza Kurniawan.pdf :: Unduh
|
No. Panggil : | S53849 |
Entri utama-Nama orang : | |
Entri tambahan-Nama orang : | |
Entri tambahan-Nama badan : | |
Subjek : | |
Penerbitan : | [Place of publication not identified]: [Publisher not identified], 2014 |
Program Studi : |
Bahasa : | ind |
Sumber Pengatalogan : | LibUI ind rda |
Tipe Konten : | text |
Tipe Media : | unmediated ; computer |
Tipe Carrier : | volume ; online source |
Deskripsi Fisik : | xiii, 57 pages : illustration ; 30 cm + appendix |
Naskah Ringkas : | |
Lembaga Pemilik : | Universitas Indonesia |
Lokasi : | Perpustakaan UI, Lantai 3 |
No. Panggil | No. Barkod | Ketersediaan |
---|---|---|
S53849 | TERSEDIA |
Ulasan: |
Tidak ada ulasan pada koleksi ini: 20368622 |