Pengaruh penambahan silikon si terhadap karakteristik komposit al 12zn 6mg 1cu dengan partikel penguat 7 5 vol zro2 menggunakan proses squeeze casting untuk aplikasi balistik = Effect of silicon addition on characteristics of al 12zn 6mg 1cu composite with 7 5 vol zro2 reinforcement produced by squeeze casting for ballistic application
Rizky Nur Fadhillah;
Bondan Widiawan, supervisor; Dwi Rahmalina, supervisor; Anne Zulfia, examiner; Myrna Ariati Mochtar, examiner
([Publisher not identified]
, 2014)
|
ABSTRAK Material untuk aplikasi peralatan militer seperti kendaraan taktis dibuat supayaringan dan mampu menahan tembakan peluru yang merupakan beban impakberkecepatan tinggi. Untuk itu material yang kuat dan ringan seperti metal matrixcomposite merupakan salah satu alternatif. Matriks aluminium sedang banyakdikembangkan karena sifatnya yang ringan dan memiliki sifat mekanis yang baik.Namun kekerasan yang tidak cukup tinggi menjadi permasalahan. Oleh karena itudibutuhkan partikel penguat untuk meningkatkan kekerasan dan kekuatan tanpamengorbankan ketangguhan material misalnya partikel zirkonia yang memilikifracture thoughness cukup baik.Pada penelitian ini dikembangkan material komposit Al-12Zn-6Mg-1Cuberpartikel penguat 7,5 vol.% ZrO2 dengan variasi 1, 3,86, dan 4 wt.% Simenggunakan proses squeeze casting. Material komposit ini diharapkan memilikikarakteristik yang baik untuk aplikasi balistik.Karakterisasi dilakukan untuk mengetahui efek penambahan Si pada komposit.Karakterisasi material didapatkan dengan melakukan beberapa pengujian sepertipengujian komposisi dengan Optical Emission Spectroscopy (OES), pengujiankekerasan dengan metode Rockwell B, pengujian impak, analisis struktur mikromenggunakan mikroskop optik dan Scanning Electron Microscopy (SEM), sertapengujian balistik dengan peluru tipe III berkaliber 7,62 mm.Hasil penelitian menunjukkan bahwa proses fabrikasi belum berhasilmencampurkan serbuk zirkonia secara homogen. Hal ini disebabkan karenawettability dan lapisan antar muka antara Al dan ZrO2 tidak cukup baik. Partikelzirkonia ditemukan berkelompok yang menginisiasi terbentuknya porositas didalam komposit yang mempengaruhi karakteristik komposit.Hasil pengujian kekerasan dan impak didapatkan bahwa kandungan Si 1 wt.%memiliki kekerasan paling tinggi yaitu 81 HRB dan harga impak 0,0157 J/mm2.Peningkatan sifat mekanik yang diharapkan dengan penambahan Si tidak terjadikarena tertutupi oleh kehadiran porositas. Pengujian balistik yang dilakukanmenggunakan komposit dengan variasi yang berbeda menunjukkan potensi yangcukup menjanjikan karena peluru tidak dapat menembus pelat lapisan ketigakomposit dengan partikel penguat zirkonia ini. ABSTRACT Material used for military equipment, such as tactical vehicle, should be light andhave bulletproof characteristic. Metal matrix composite is an alternative for that.Aluminium matrix is widely developed because of its light weight and goodmechanical properties, but the problem is that its hardness is not high enough tobe bulletproof. Therefore reinforcement with higher hardness and strength isadded, such as zirconium oxide which has good fracture toughness. This researchstudied composite material with Al-12Zn-6Mg-1Cu as matrix and reinforced by7.5 vol.% ZrO2. Silicon content was variated to 1, 3.86, and 4 wt.% and sampleswere fabricated by squeeze casting. This material is expected to have goodballistic characteristic. Materials characterization included Optical EmissionSpectroscopy (OES), Rockwell B hardness testing, impact testing, microstructureanalysis using optical microscope and Scanning Electron Microscopy (SEM), andballictic testing type III with 7.62 mm bullet.The results showed that the fabrication process was not able to produce plateswith homogeneous ZrO2 distribution. The ZrO2 particles were foundagglomerated and initiated porosities which then reduces the mechanicalproperties. This was due to poor wettability of ZrO2 particles in aluminium.Hardness and impact testing showed that the highest value were achieved by 1wt.% silicon containing alloy, with the values of 81 HRB and 0.0157 J/mm2.Higher mechanical properties which was expected with increasing silicon contentis not achieved because of the presence of porosity. Ballistic testing on 3 plateswith variated silicon content showed that this composite is potential enough to bebulletproof material. |
![]()
|
No. Panggil : | S53842 |
Entri utama-Nama orang : | |
Entri tambahan-Nama orang : | |
Entri tambahan-Nama badan : | |
Subjek : | |
Penerbitan : | [Place of publication not identified]: [Publisher not identified], 2014 |
Program Studi : |
Bahasa : | ind |
Sumber Pengatalogan : | LibUI ind rda |
Tipe Konten : | text |
Tipe Media : | unmediated ; computer |
Tipe Carrier : | volume ; online resource |
Deskripsi Fisik : | xiv, 68 pages : illustration ; 30 cm + appendix |
Naskah Ringkas : | |
Lembaga Pemilik : | Universitas Indonesia |
Lokasi : | Perpustakaan UI, Lantai 3 |
No. Panggil | No. Barkod | Ketersediaan |
---|---|---|
S53842 | 14-17-909795028 | TERSEDIA |
Ulasan: |
Tidak ada ulasan pada koleksi ini: 20368740 |