Pengaruh penambahan zirkonia (zro2) terhadap respon pengerasan penuaan pada al-12zn-5mg-1cu-1si hasil squeeze casting untuk aplikasi balistik = The effect of zirconia (zro2) addition to age hardening response of al-12zn-5mg-1cu-1si composite produced by squeeze casting for ballistic application
I Made Binar Andromeda;
Bondan Widiawan, supervisor; Dwi Rahmalina, supervisor; Anne Zulfia, examiner; Myrna Ariati Mochtar, examiner
([Publisher not identified]
, 2014)
|
|
ABSTRAK Kendaraan taktis (rantis) merupakan kendaraan yang digunakan dalamdunia militer dengan komponen penyusun utama berupa baja yang berat dengansifat balistik yang baik. Diperlukan material pengganti yang lebih ringan dengansifat balistik yang endekati. Aluminium komposit merupakan material yangdiharapkan mampu menjadi pengganti baja pada kendaraan taktis dikarenakansifatnya yang ringan, mudah dipadu dan dapat dilaku panas.Penelitian menggunakan paduan Al-12Zn-5Mg-1Cu-1Si dengan variasipenguat ZrO2 sebesar 5, 7,5 dan 10 vol. % hasil squeeze casting dengan proseslaku pelarutan pada temperatur 450 oC selama 1 jam kemudian dlakukanpendinginan cepat menggunakan media air pada temperatur ruang dan dilakukanpenuaan selama 200 jam. Karakterisasi yang dilakukan berupa pengujiankekerasan, impak, pengamatan struktur makro dan mikro, SEM, EDX danpengujian balistik tipe IIIA.Hasil penelitian menunjukkan bahwa pengerasan penuaan akanmeningkatkan kekerasan komposit. Semakin tinggi kandungan ZrO2 akanmenyebabkan turunnya kekerasan dan naiknya harga impak dikarenakan duafaktor yang mempengaruhi, yaitu porositas dan peningkatan ketangguhan olehpenguat ZrO2. Hasil pengujian balistik didapatkan bahwa lapisan pelat ketigamampu menahan beban peluru akan tetapi pelat mengalami hancur disebabkanharga impak pelat yang rendah dan hadirnya porositas yang mempercepatterjadinya kegagalan. ABSTRACT Tactical vehicle is used in military need with steel as the main componentthat is heavy with good ballistic property, so we need a subtitution material whichis lighter and having good ballistic property. Aluminium composite is designed tosubtitute the use of steel in tactical vehicle due to its low weight and strength.This study used Al-12Zn-5Mg-1Cu-1Si with the variation of ZrO2 by 5,7,5 and 10 vol. % that was produced by squeeze casting. The composite weresolution treated at 450 oC for 1 hour and then quenched in water at roomtemperature and aged for 200 oC. The characterization included hardness andimpact tests, analysis of microstructure and macrostructure, SEM, EDX and typeIIIA of ballistic test.The results show that by the increase in ZrO2 led to the decrease inhardness and the impact. These were due to two affecting factors, they areporosity and the ZrO2 that will increase the toughness. The ballistic test showedthat the third plate could resist the bullet but the plate was broken due to the lowimpact value and the presence of porosity. |
 S54351-I Made Binar Andromeda.pdf :: Unduh
|
| No. Panggil : | S54351 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Subjek : | |
| Penerbitan : | [Place of publication not identified]: [Publisher not identified], 2014 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online source |
| Deskripsi Fisik : | xv, 127 pages : illustration ; 30 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S54351 | 14-17-649905101 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20368741 |