Formulasi hidrogel transdermal menggunakan eksipien Tersambungsilang-12 dari Koproses Amilosa - Xanthan Gum: studi penetrasi in vitro dan in vivo = Formulation of transdermal hydrogel using 12 12-Crosslinked Excipients from Co-processed Amylose – Xanthan Gum: in vitro and in vivo penetration studies / Laily Alawiyah
Laily Alawiyah;
Silvia Surini, supervisor; Harahap, Yahdiana, supervisor; Mahdi Jufri, examiner; Hayun, promotor
([Publisher not identified]
, 2014)
|
ABSTRACT Hidrogel transdermal merupakan sediaan yang terdiri dari jaringan polimer tigadimensi yang mampu mengikat air atau cairan biologis dalam jumlah besar danditujukan untuk sistem penghantaran transdermal. Pada penelitian sebelumnya,eksipien tersambungsilang-12 dari koproses amilosa-xanthan gum 1:1 (CL12-Ko-A-XG 1:1) memiliki karakteristik sebagai matriks hidrogel, berupa kekuatan gel,viskositas dan kemampuan mengembang yang cukup besar serta derajat substitusisebesar 0,288 ± 0,013. Penelitian ini bertujuan untuk memformulasikan eksipienCL12-Ko-A-XG 1:1 sebagai matriks pada sediaan hidrogel transdermal danmengetahui kemampuannya untuk menghantarkan obat melalui uji penetrasisecara in vitro dan in vivo. Hidrogel transdermal diformulasikan dengankonsentrasi eksipien CL12-Ko-A-XG 1:1 sebesar 5%. Uji penetrasi secara in vitrodilakukan dengan alat sel difusi Franz menggunakan membran abdomen tikusjantan galur Sprague-Dawley. Uji penetrasi secara in vivo dilakukan pada 6 ekortikus jantan galur Sprague-Dawley dengan dosis 25mg/kg selama 12 jam. Hasiluji penetrasi in vitro menunjukkan fluks natrium diklofenak dari sediaan hidrogeltransdermal sebesar 520,28 ± 16,19 μg cm-2 jam-1. Melalui uji penetrasi in vivodiketahui nilai AUC0-t sebesar 26,99 ± 8,78 μg jam mL-1. Berdasarkan hasiltersebut dapat disimpulkan bahwa eksipien CL12-Ko-A-XG 1:1 dapatdiaplikasikan sebagai eksipien pembentuk matriks pada sediaan transdermal danterbukti secara in vitro maupun in vivo mampu menghantarkan obat secaratransdermal. ABSTRACT Transdermal hydrogel is a dosage form consisting of three-dimensional polymernetwork that is able to bind water or biological fluids in large quantities and isintended for transdermal delivery systems. In the previous study, 12-crosslinkedexcipient from co-processed amylose-xanthan gum 1:1 (CL12-Ko-A-XG 1:1) wasproven to have charactheristic as hydrogel matrix based on sufficient gel strength,viscosity, swelling index, and also substitution degree as 0.288 ± 0.013. The aimsof this study were to formulate CL12-Ko-A-XG 1:1 excipients as a matrix ontransdermal hydrogel dosage forms and to evaluate its ability on delivering drugsubstances by in vitro and in vivo penetration test. Transdermal hydrogel wasformulated using 5% CL12-Ko-A-XG 1:1. In vitro test was performed by Franzdiffusion cell using abdominal membrane of Sprague-Dawley strain male rats. Invivo penetration test was performed on six Sprague-Dawley strain male rats at adose of 25mg/kg for 12 hours. Flux of sodium diclofenac from transdermalhydrogel dosage form was 520.28 ± 16.19 μg cm-2 hour-1. The value of AUC0-twas 26.99 ± 8.78 μg jam mL-1. Based on those result, it could be concluded thatCL12-Ko-A-XG 1:1 can be applied as a matrix former excipients on transdermalhydrogel dosage forms and is capable of delivering drugs transdermally, provenby in vitro and in vivo test. |
![]()
|
No. Panggil : | S56960 |
Entri utama-Nama orang : | |
Entri tambahan-Nama orang : | |
Entri tambahan-Nama badan : | |
Subjek : | |
Penerbitan : | [Place of publication not identified]: [Publisher not identified], 2014 |
Program Studi : |
Bahasa : | ind |
Sumber Pengatalogan : | LibUI ind rda |
Tipe Konten : | text |
Tipe Media : | unmediated ; Computer (rdadontent) |
Tipe Carrier : | volume ; online resource |
Deskripsi Fisik : | xvii, 75 pages : illustration ; 29 cm + appendix |
Naskah Ringkas : | |
Lembaga Pemilik : | Universitas Indonesia |
Lokasi : | Perpustakaan UI, Lantai 3 |
No. Panggil | No. Barkod | Ketersediaan |
---|---|---|
S56960 | TERSEDIA |
Ulasan: |
Tidak ada ulasan pada koleksi ini: 20386623 |