Formulasi film transdermal ketoprofen menggunakan kompleks polielektrolit kitosan xanthan sebagai eksipien pembentuk film = Ketoprofen transdermal film formulation using chitosan xanthan polyelectrolyte complex as film forming excipient / Dessy Dian Septysari

Dessy Dian Septysari; Kurnia Sari Setio Putri, supervisor; Joshi, J.B., editor; Silvia Surini, examiner; Iskandarsyah, examiner (Fakultas Farmasi Universitas Indonesia, 2014)

 Abstrak

Film transdermal merupakan sistem penghantaran obat yang diaplikasikan melalui kulit untuk menghantarkan obat ke sistemik. Penelitian ini bertujuan untuk mempelajari eksipien kompleks polielektrolit kitosan-xanthan (KPKX) sebagai eksipien pembentuk film yang dibuat dengan mencampurkan larutan gum xanthan 1% ke dalam larutan kitosan 1% dengan cara diteteskan dan disertai pengadukan. KPKX yang diperoleh dikarakterisasi gugus fungsi, indeks mengembang, kekuatan gel, dan sifat mekanik filmnya. Film transdermal dibuat dengan menggunakan KPKX 1:1 sebagai matriks, propilenglikol-gliserol (8:2) 50% sebagai plasticizer, dan ketoprofen sebagai model obat. Film transdermal ketoprofen yang dihasilkan memiliki sifat mekanis yang baik dengan persentasi elongasi sebesar 108,70 ± 1,56% dan tensile strength sebesar 791,05 ± 5,30 N/m2. Uji disolusi in vitro menunjukkan pelepasan ketoprofen dari film transdermal ketoprofen sebesar 99,57 ± 4,67% selama 12 jam dengan mekanisme difusi terkendali. Uji penetrasi in vitro menunjukkan bahwa penetrasi in vitro dari film transdermal ketoprofen sebesar 12,34 ± 0,22 mg/cm2 selama 12 jam dengan kecepatan penetrasi 1,051 ± 0,074 mg/cm2.jam. Berdasarkan hasil tersebut, dapat disimpulkan bahwa KPKX merupakan eksipien yang baik digunakan sebagai pembentuk film transdermal.

Transdermal film is a drug delivery system that is applied through the skin to deliver drugs to the systemic. This present study was intended to evaluate the ability of chitosan-xanthan polyelectrolyte complex (CXPC) as film-forming excipient which were made by dropwise a solution of 1% xanthan gum in a solution of 1% chitosan and aided with stirring. The obtained CXPC was characterized, including its functional group, swelling index, gel strength, and film mechanical properties. Transdermal films made using CXPC 1:1 as matrix, propylene glycol-glycerine (8:2) 50% as plasticizer, and ketoprofen as model of drug. Ketoprofen transdermal film which were produced from CXPC possessed good mechanical properties with elongation percentage of 108.70 ± 1.56% and the tensile strength of 791.05 ± 5.30 N/mm2. The in-vitro drug release study showed that 99.57 ± 4.67% of ketoprofen has been released from transdermal film in 12 hours by diffusion-controlled mechanism. In-vitro drug release study showed that 12.34 ± 0.22 mg/cm2 of ketoprofen able to penetrate through skin membrane with the flux of 1.051 ± 0.074 mg/cm2.hour. Therefore, it can be concluded that CXPC had good characteristics to be applied as excipient transdermal film.

 File Digital: 1

Shelf
 S57662-Dessy Dian Septysari.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : S57662
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Subjek :
Penerbitan : [Place of publication not identified]: Fakultas Farmasi Universitas Indonesia, 2014
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xv, 50 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S57662 S57662 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20387059