Sensor glukosa berbasis pada deposit logam nikel pada glassy carbon = Glucose sensor based on deposited nickel metal on glassy carbon electrode

Ishak Firdauzi Ruslan; Rahmat Wibowo, supervisor; Yoki Yulizar, examiner; Emil Budianto, examiner; Jarnuzi Gunlazuardi, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2014)

 Abstrak

Sensor elektrokimia non-enzimatis glukosa berbasis logam nikel dibuat secara elektrodeposisi menggunakan larutan NiCl2 5 mM dalam buffer asetat pH 5 0,1 M pada elektroda Glassy Carbon (GCE). Elektrodeposisi dilakukan dengan potensial -1,376 V vs Ag/AgCl dengan variasi waktu deposisi selama 60, 180, dan 300 s. Lama waktu deposisi mempengaruhi jumlah deposit pada permukaan GCE yang diketahui dengan metode SEM dan jumlah logam Ni diketahui dengan metode EDS. Elektroda GCE terdeposisi nikel selama 300 s (Ni-GCE 300 s) mampu mendeteksi glukosa dengan teknik voltametri siklik kisaran konsentrasi 0,099-0,909 mM dengan kelinearitasan sebesar R2= 0,9982 dan kemiringan sebesar 138,2. Ni-GCE 300 s mampu juga mendeteksi glukosa kisaran 0,999-9,9 mM dengan kelinearitasan sebesar R2= 0,9814 dan kemiringan sebesar 257,89. Ni-GCE 300 s memiliki Repeatabilitas yang baik dimana pada pengukuran 0,909 mM glukosa menghasilkan nilai RSD (n=10) sebesar 0,58 %. Kestabilan Ni-GCE 300 s cukup baik untuk pengukuran glukosa 0,909 mM dengan rentang waktu 12 hari dengan respon arus kisaran 750-800 μA. Dari segi sensitifitas, Ni-GCE 300 s mengalami penurunan arus ketika mendeteksi glukosa 0,099 mM dengan penambahan asam askorbat dan fruktosa pada konsentrasi yang sama dan 1:10 dari glukosa.

Electrochemical non-enzimatic glucose sensor based on nickle metal was made by electrodeposition using NiCl2 5 mM in acetic buffer pH 5 0,1 M solution on Glassy Carbon electrode (GCE). Electrodeposition potential was set on -1,376 V vs Ag/AgCl with varying deposition time of 60, 180, and 300 s. Deposition time affects the amount of deposit at the electrode surface that was analyzed using SEM method and nickle composition was analyzed using EDS method. GCE electrode deposited with nickle for 300 s (Ni-GCE 300 s) can detect glucose using cyclic voltammetry technique with a range of 0,099-0909 mM concentration with a linearity of R2= 0,9982 and a slope of 138,2. Ni-GCE 300 s can also detect glucose with a range of 0,999-9,9 mM concentration with a linearity of R2=0,9814 and a slope of 257,89. Ni-GCE 300 s have a good reproducibillity for detecting 0,909 mM of glucose and gives a RSD (n=10) value of 0,58%. Ni-GCE stabillity was good for detecting 0,909 mM of glucose with a time range of 12 days that gives a current response range of 750-800 μA. In sensitivity, Ni-GCE 300 s experienced on decreasing current response while detecting 0,099 mM of glucose from addition of ascorbic acid and fructose with a same and 1:10 of glucose concentration.

 File Digital: 1

Shelf
 S57569-Ishak Firdauzi Ruslan.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : S57569
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2014
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xvi, 92 pages : illustration ; 28 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S57569 14-22-51229198 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20388060