Komposit zeolit hibrida NaY - ZSM-5 termodifikasi ion Co2+ sebagai material sensor gas amonia dengan metode EIS (Electrochemical Impedance Spectroscopy) = Zeolite hybrid composite NaY - ZSM-5 modified by Co2+ ion for ammonia gas sensor with EIS (Electrochemical Impedance Spectroscopy) method

Paputungan, Zulkarnaen; Yuni Krisyuningsih, supervisor; Djoko Triyono, supervisor; Ridla Bakri, examiner; Jarnuzi Gunlazuardi, examiner; Ivandini Tribidasari Anggraningrum, examiner (Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2014)

 Abstrak

Hibrida zeolit NaY - ZSM-5 telah berhasil dibuat di atas permukaan pelat kuarsa. Zeolit ZSM-5 dilapisi di atas permukaan pelat kuarsa dengan menggunakan metode spin coating menggunakan bubuk zeolit ZSM-5 yang sebelumnya disintesis dari koloid gel ZSM-5 dengan menggunakan metode sintesis double template dan metode hidrotermal. Dilanjutkan dengan pelapisan zeolit NaY menggunakan metode dip coating menggunakan bubuk zeolit NaY dari hasil sintesis menggunakan proses seeding. Hasil XRD menunjukkan bahwa zeolit yang dihasilkan merupakan zeolit ZSM-5 dan NaY. Diperkuat dengan hasil SEM dan EDS yang memperlihatkan rasio Si/Al pada ZSM-5 sebesar 41,3 dan pada NaY sebesar 2,08. Kemudian dilakukan modifikasi menggunakan ion Co2+ .Untuk melihat pengaruh gas amonia terhadap hibrida zeolit dihitung menggunakan metode EIS (Electrochemical Impedance Spectrometer) yang dengan rentang frekuensi 50 Hz ? 1 MHz. Didapatkan rentang deteksi amonia 0 ppm ? 1000 ppm. Serta dihitung hubungan antara konsentrasi dengan perubahan nilai impedansi pada frekuensi 2000 Hz dan diperoleh nilai r2 sebesar 0,9531. Sedangkan nilai r2 untuk komposit tanpa Co2+ pada 7000Hz didapatkan senilai 0,9991.

Zeolite hybrid NaY-ZSM-5 has been successfully made on quartz plate. ZSM-5 zeolite was synthesized using double template and hydrothermal technique and deposited using sipn coating method. The process was continued with depositing NaY zeolite that was synthesized with seeding technique using dip coating method. The XRD result show that the zeolite wich was synthesized was ZSM-5 and NaY zeolite. SEM and EDS characterization that have a good agree with XRD data show Si/Al ratio in ZSM-5 and NaY was 41.3 and 2.1, respectively. Modification was performed using Co2+ ion. The influence of ammonia gases on the zeolite hybrid was see using EIS (Electrochemical Impedance Spectrometer) method with frequency range 50 Hz ? 1 MHz. Correlation between concentration and impedance value was plotted at 2000Hz frequency and the obtained value was r2=0.9531. While value of r2 for composite without Co2+ at 7000Hz was 0,9991.

 File Digital: 1

Shelf
 S61462-Zulkarnaen Paputungan.pdf :: Unduh

LOGIN required

 Metadata

No. Panggil : S61462
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Subjek :
Penerbitan : Depok: Fakultas Matematika dan Ilmu Pengetahuan Alam Universitas Indonesia, 2014
Program Studi :
Bahasa : ind
Sumber Pengatalogan :
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xiii, 73 pages : illustration ; 30 cm
Naskah Ringkas :
Lembaga Pemilik : Universitas Indonesia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
S61462 14-21-904964129 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20388581