Optimalisasi morfologi dan kristalinitas TiO2 nanotubes pada Ti6Al4v sebagai penghambat pembentukan biofilm pada implantasi gigi = Morphology and crystalinity optimalization of TiO2 nanotubes on Ti6Al4v for inhibiting biofilm forming in tooth implantation
Billy Aprianto;
Slamet, supervisor; Boy M. Bachtiar, supervisor; Eny Kusrini, promotor; Setiadi, examiner; Praswasti Pembangun Dyah Kencana Wulan, examiner
(Fakultas Teknik Universitas Indonesia, 2014)
|
|
Optimalisasi morfologi dan kristalinitas TiO2 nanotubes (TNT) yang difabrikasi pada permukaan Ti6Al4V dengan metode anodisasi dan dikristalisasi menggunakan variasi metode, yaitu pemanasan menggunakan furnace yang dialiri udara dengan variasi suhu operasi 500° - 800°C dan metode hydrothermal treatment dengan variasi suhu 150°-200°C selama 3 jam telah dilakukan. Hasil karakterisasi pada sampel menunjukkan adanya peralihan fase kristal dari anatase menjadi rutile pada rentang suhu 600°C - 650°C dengan ukuran kristal rata-rata pada setiap variasi adalah 18 nm. Hasil uji pembentukan biofilm secara in vitro dengan bakteri Streptococcus mutans menunjukkan sampel Ti6Al4V/TNT yang dikristalisasi pada suhu 600°C memiliki kinerja fotokatalitik yang paling baik, dengan hasil sebesar 21% konsentrasi bakteri yang menempel pada plat Ti6Al4V/TNT dibandingkan dengan model kontrol pada jam ke-24 pengukuran. Hasil ini menunjukkan sampel Ti6Al4V/TNT dengan suhu kristalisasi 600°C merupakan kondisi optimum untuk menghambat pembentukan biofilm dalam penelitian ini. Kinerja fotokatalitik pada bahan Ti6Al4V/TNT berpotensi untuk ditingkatkan menggunakan kombinasi teknologi lainnya. Morphology and crystalinity optimalization of TiO2 nanotubes (TNT) on Ti6Al4V using anodization method and various crystalization method (heat treatment by furnace within air stream at 500°-800°C and heat treatment using hydrothermal treatment method at 150°-200°C) had been done. Characterizations of the samples show that there are a crystal phase changing from anatase to rutile at 600°-650°C in heat treatment using furnace, with 18 nm for crystal size in average. Biofilm's test exhibit that Ti6Al4V/TNT sample that crystalized at 600°C has the best performance in inhibiting biofilm formation, which can achieve 19% of biofilm concentration on the material, compared to the control. The result show that Ti6Al4V/TNT that crystalized at 600°C has the optimum morpholgy and crystalinity to inhibit the biofilm formation. The modified Ti6Al4V has great potential in biomedical application, due to its photocatalytic performance and TiO2 characteristics that can be combined with others technology to make better implants. |
 T41808-Billy Aprianto.pdf :: Unduh
|
| No. Panggil : | T41808 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Penerbitan : | Depok: Fakultas Teknik Universitas Indonesia, 2014 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ind rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xvi, 82 pages : illustration ; 30 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| T41808 | 15-17-709865695 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20388788 |