Perancangan dan simulasi pengecoran pada pembuatan casing turbin uap direct condensing 3,5 MW

Khamda Herbandono; Bambang Suharno, supervisor ([Publisher not identified] , 2011)

 Abstrak

ABSTRAK
Latar belakang penelitian ini adalah dijumpainya cacat coran berupa penyusutan
pada casing turbin uap. Program pengembangan turbin uap ini merupakan
program nasional untuk peningkatan TKDN dan kemandirian industri manufaktur
dalam negeri. Perkembangan teknologi CAE dapat dimanfaatkan dalam proses
optimalisasi desain untuk memverifikasi desain coran yang telah dibuat dan
memprediksi kemungkinan cacat-cacat yang dapat timbul. Penelitian ini
menggunakan software simulasi pengecoran (Z-Cast) untuk memberikan
penjelasan ilmiah pada proses perancangan dan simulasi pengecoran casing
TUDC 3,5 MW. Penelitian dilakukan dalam tiga tahap yaitu review coran casing
TUBP, perancangan dan simulasi pengecoran TUDC 3,5 MW serta tahap ketiga
untuk perbaikan desain (improvement) dan kajian tekno ekonomi.
Hasil dari tahap pertama ini dapat diketahui bahwa munculnya cacat coran yang
menyebabkan casing TUBP harus mengalami kegagalan karena adanya kesalahan
desain pengecoran dan kurang optimalnya fungsi riser dalam mensuplai logam
coran. Sedangkan pada tahap kedua, melalui pemanfaatan software Z-Cast secara
optimal dan setelah dilakukan pengecoran dengan cetakan pasir didapatkan
produk coran casing yang dapat diterima oleh standar material JIS SCPH2 dan
standar pengujian ultrasonik ASTM A 609 Security Level 2. Kemudian dalam
tahap ketiga, dilakukan perbaikan desain yang ada dengan orientasi peningkatan
yield casting. Hasil dari tahap akhir penelitian ini, didapatkan desain coran yang
mampu meningkatkan yield casting 5-10% dari desain coran semula. Peningkatan
tersebut mampu mengurangi penggunaan material 485 kg dan menurunkan biaya
produksi sebesar Rp14.417.000,- atau 6,3%.

ABSTRACT
Research background is met casting defect have the shape of shrinkage at
houshing steam turbine. The program of steam turbine development is national
program for improvement local content and manufacture industry independence.
The CAE technology evolution can be exploited in design optimization for
verification casting design which have been made and predict potencial casting
defect. This research use casting simulation software (Z-Cast) to give the
scientifically explanation at casting design and simulation of TUDC 3,5 MW
houshing. Research done in three phase, there are casting review for TUBP
houshing, casting design and simulation for TUDC 3,5 MW houshing and also
third phase for improvement design and techno-economic analisys.
Result of this first phase knowable that casting defect appearance causing TUBP
houshing have to failure caused by casting design fault and less optimal of riser
function to supply casting metal. At second phase, through Z-Cast exploiting in an
optimal design process and after done by sand mould process got the houshing
product able to be accepted by material standard JIS SCPH2 and ultrasonic test
standard ASTM A 609 Security Level 2. Then the result of third phase, yield
casting of early design could be improved about 5-10%. Those improvement
could reduce the 485 kgs material usage and drop off the production cost in
amount of IDR 14.417.000 or equal 6,3%.

 File Digital: 1

 Metadata

No. Panggil : T41454
Entri utama-Nama orang :
Entri tambahan-Nama orang :
Entri tambahan-Nama badan :
Subjek :
Penerbitan : [Place of publication not identified]: [Publisher not identified], 2011
Program Studi :
Bahasa : ind
Sumber Pengatalogan : LibUI ind rda
Tipe Konten : text
Tipe Media : unmediated ; computer
Tipe Carrier : volume ; online resource
Deskripsi Fisik : xv, 192 pages : illustration ; 30 cm + appendix
Naskah Ringkas :
Lembaga Pemilik : Universitas Indoensia
Lokasi : Perpustakaan UI, Lantai 3
  • Ketersediaan
  • Ulasan
No. Panggil No. Barkod Ketersediaan
T41454 15-17-273415186 TERSEDIA
Ulasan:
Tidak ada ulasan pada koleksi ini: 20392444