Studi penggunaan campuran ekstrak daun sirsak dan ubi ungu sebagai inhibitor korosi organik untuk material baja api 5L pada lingkungan larutan 3,5% NaCl = Study of the use of mixture of annona muricata leaves and purple sweet potato extracts as an organic corrosion inhibitor for api 5L steel in 3,5% NaCl solution
Rinaldi Maulana;
Johny Wahyuadi Soedarsono, supervisor; Sutopo, examiner; R. Bambang Jaya Bangkit, examiner
([Publisher not identified]
, 2014)
|
ABSTRAK Korosi merupakan suatu proses degradasi material akibat interaksi denganlingkungannya. Inhibitor korosi merupakan suatu zat yang dapat menghambatproses korosi. Bahan organik dipilih sebagai alternatif karena bersifat aman,mudah didapatkan, bersifat biodegradable, biaya murah, dan ramah lingkungan.Penelitian ini merupakan studi tentang inhibitor korosi menggunakan senyawaorganik yang dilakukan pada material baja API 5L di lingkungan larutan NaCl3,5%. Penelitian ini dilakukan untuk mempelajari efek penggunaan campuranekstrak daun sirsak dan ubi ungu sebagai inhibitor korosi dengan variasikonsentrasi. Ekstrak daun sirsak dan ubi ungu dipilih sebagai inhibitor korosikarena mengandung senyawa antioksidan yang dapat menghambat laju korosi.Pengukuran laju korosi dilakukan dengan menggunakan metode kehilangan beratdan polarisasi. Mekanisme terjadinya korosi diuji dengan menggunakanElectrochemical Impedance Spectroscopy (EIS) sementara karakterisasi darimaterial inhibitor organik dilakukan dengan menggunakan metode FourierTransform Infra-Red (FTIR). Tipe ikatan kimia yang terbentuk di lapisanpermukaan baja dianalisa dengan metode FTIR yang mengindikasikan adanyagugus fungsi karbonil (C=O) dan hidroksil (O-H) yang berkombinasi membentuksuatu lapisan. Di dalam larutan 100 mL NaCl 3,5%, penambahan ekstrak daunsirsak sebanyak 1 mL menghasilkan efisiensi inhibitor sekitar 73,38% (melaluipengujian polarisasi) dan di dalam larutan 520 mL NaCl 3,5%, penambahanekstrak daun sirsak sebanyak 1 mL menghasilkan efisiensi inhibitor sekitar 50%(melalui pengujian kehilangan berat). Kemudian, penambahan ekstrak ubi ungusebanyak 1-5 mL menyebabkan terjadinya penurunan efisiensi inhibitor. Ekstrakdaun sirsak dan ubi ungu bekerja dengan membentuk suatu lapisan tipis yangmengendap (adsorpsi) pada permukaan logam sebagai lapisan pelindung yangdapat menghambat reaksi logam tersebut dengan lingkungannya. Mekanisme inijuga didukung dengan meningkatnya nilai tahanan polarisasi dari permukaan bajasetelah ditambahkan inhibitor. ABSTRACT Corrosion is a degradation of the material due to its interaction with theenvironment. Corrosion inhibitor is a substance that can inhibit the corrosionprocess. The use of organic corrosion inhibitor become a new alternative toachieve that goal, it happen because the organic corrosion inhibitor is safe, cheap,biodegradable, and environmentally friendly. This research is the study ofcorrosion inhibitor using organic compounds for API 5L steel in 3.5% NaClsolution. This research was conducted to study the use of mixture of annonamuricata leaves and purple sweet potato extracts as corrosion inhibitor withvariable concentration. Annona muricata leaves and purple sweet potato extractsare selected as corrosion inhibitor because they contain antioxidant compoundsthat can inhibit the corrosion rate. Corrosion rate measurement method wasconducted by using the weight loss and polarization methods. Corrosionmechanism was examined by Electrochemical Impedance Spectroscopy (EIS)while the characterization of organic inhibitor material was carried out using themethod of Fourier Transform Infra-Red (FTIR). The type of chemical bonds onthe steel surface layer was analyzed by FTIR method which indicated the presenceof functional groups carbonyl (C=O) and hydroxyl (O-H) which combined as filmforming. In a solution containing 100 mL 3.5% NaCl, the addition of 1 mLannona muricata leaves extract resulted in approximately 73.38% inhibitorefficiency (using the polarization method) and in a solution containing 520 mL3.5% NaCl, the addition of 1 mL annona muricata leaves extract resulted inapproximately 50% inhibitor efficiency (using the weight loss method). Then, theaddition of 1-5 mL purple sweet potato extract resulted the decreasing of inhibitorefficiency. Annona muricata leaves and purple sweet potato extracts work byforming a thin layer which settles (adsorption) to metal surfaces as a protectivelayer that can inhibit the reaction of the metal with its environment. Thismechanism is also supported by the increased value of the polarization resistanceof the steel surface after addition of inhibitor. |
![]()
|
No. Panggil : | S55381 |
Entri utama-Nama orang : | |
Entri tambahan-Nama orang : | |
Entri tambahan-Nama badan : | |
Subjek : | |
Penerbitan : | [Place of publication not identified]: [Publisher not identified], 2014 |
Program Studi : |
Bahasa : | ind |
Sumber Pengatalogan : | LibUI ind rda |
Tipe Konten : | text |
Tipe Media : | unmediated ; computer |
Tipe Carrier : | volume ; online resource |
Deskripsi Fisik : | xvii, 80 pages : illustration ; 28 cm + appendix |
Naskah Ringkas : | |
Lembaga Pemilik : | Universitas Indonesia |
Lokasi : | Perpustakaan UI, Lantai 3 |
No. Panggil | No. Barkod | Ketersediaan |
---|---|---|
S55381 | 14-17-392967015 | TERSEDIA |
Ulasan: |
Tidak ada ulasan pada koleksi ini: 20392615 |