Pengaruh penyikatan menggunakan pasta gigi nano calcium carbonate terhadap kekasaran permukaan resin komposit nanofil = Effect of brushing with toothpaste containing nano calcium carbonate towards nanofill composite resin surface roughness / Alviani Martha Ramadhani
Alviani Martha Ramadhani;
Ellyza Herda, supervisor; Siti Triaminingsih, supervisor; Decky Joesiana Indrani, examiner; Ali Noerdin, examiner
(Fakultas Kedokteran Gigi Universitas Indonesia, 2014)
|
ABSTRAK Penelitian ini bertujuan untuk mengetahui pengaruh penyikatan menggunakan pastagigi nano calcium carbonate terhadap kekasaran permukaan resin komposit nanofil.Penyikatan menggunakan 3 jenis bahan penyikat dengan lama penyikatan 10, 20, dan30 menit. Kekasaran permukaan diuji menggunakan surface roughness tester danhasil dianalisis dengan uji repeated ANOVA dan one way ANOVA. Morfologipermukaan setelah disikat selama 30 menit diamati menggunakan SEM. Nilaikekasaran permukaan resin komposit nanofil meningkat secara bermakna (p < 0.005)setelah dilakukan penyikatan dengan pasta gigi nano calcium carbonate tetapipeningkatan nilai tidak setinggi penyikatan dengan pasta gigi lainnya. ABSTRACT This study aimed to determine the effect of brushing using toothpaste containingnano calcium carbonate on the surface roughness of composite resin nanofill.Brushing use 3 types of materials with brushing period within 10, 20, and 30minutes. Surface roughness measured using surface roughness tester and the resultswere analyzed by repeated ANOVA and one way ANOVA test. Surface morphologyafter brushing for 30 minutes was observed using SEM. Nanofill Composite resinsurface roughness value increased significantly after brushing with toothpastecontaining nano calcium carbonate but the increase was not as high as the value ofbrushing with other toothpastes. |
![]()
|
No. Panggil : | S-Pdf |
Entri utama-Nama orang : | |
Entri tambahan-Nama orang : | |
Subjek : | |
Penerbitan : | [Place of publication not identified]: Fakultas Kedokteran Gigi Universitas Indonesia, 2014 |
Program Studi : |
Bahasa : | ind |
Sumber Pengatalogan : | LibUI ita rda |
Tipe Konten : | text |
Tipe Media : | unmediated ; computer |
Tipe Carrier : | volume ; online resource |
Deskripsi Fisik : | xiii, 33 pages : illustration ; 28 cm + appendix |
Naskah Ringkas : | |
Lembaga Pemilik : | Universitas Indonesia |
Lokasi : | Perpustakaan UI, Lantai 3 |
No. Panggil | No. Barkod | Ketersediaan |
---|---|---|
S-Pdf | TERSEDIA |
Ulasan: |
Tidak ada ulasan pada koleksi ini: 20402089 |