Dekomposisi selulosa asetat dan selulosa asetat-selulosa asetat butirat dengan penguat organoclay terinterkalasi surfaktan HDTMA-Brr = Decomposition of cellulose acetate and cellulose acetate cellulose acetate butyrate with organoclay intercalated surfactant HDTMA-Br as nanofiller / Ghuzan Al Abrar
Ghuzan Al Abrar;
Ariadne Lakshmidevi Juwono, supervisor; Yuni Krisyuningsih, examiner; Cuk Imawan, examiner; Riswijanto, examiner
(Universitas Indonesia, 2014)
|
|
ABSTRAKSintesis nanokomposit selulosa asetat - selulosa asetat butirat/ organoclay-HDTMA-Br (OCT-C16). Sebagai perbandingan, dalam penelitian ini juga disintesis nanokomposit selulosa asetat. Sintesis organoclay meliputi tiga tahapan yaitu purifikasi karbonat, sintesis Na-Bentonit Purifikasi dan sintesis OCT-C16. Pada tiap tahapan dilakukan karakterisasi dengan XRD, hasil pada sampel organoclay menunjukkan interkalasi pada surfaktan HDTMABr dapat meningkatkan basal spacing organoclay menjadi 19,76 Å. Dilakukan penambahkan variasi persen berat OCT-C16 sebagai nanofiller sebanyak 0 wt%, 1 wt%, 3 wt%, 5 wt%, dan 7 wt% pada nanokomposit selulosa asetat - selulosa asetat butirat. Hasil sintesis dalam bentuk membran di uji tarik, uji dekomposisi dan SEM. Nanokomposit yang dihasilkan mudah terdekomposisi di alam. ABSTRACTThe formation of nanocomposite cellulose acetate - cellulose acetate butyrate / organoclay ? HDTMA-Br (OCT-C16). As a comparison, in this study also synthesized cellulose acetate nanocomposite. Organoclay synthesis involves three stages , namely purification of carbonate , synthesis of Na - Bentonite Purification and synthesis of OCT-C16 . at each stage were characterized by XRD and the results on samples showed intercalation of organoclay on HDTMABr surfactant can increase the basal spacing of organoclay to 19.76 Å . In the synthesis of nanocomposite cellulose acetate - cellulose acetate butyrate done every additional variation of weight percent OCT-C16 as much as 0 wt% , 1 wt % , 3 wt% , 5 wt% , and wt7 %. Tensile test , decomposition test and SEM to the nanocomposite. The result is biodegradable nanocomposite. |
 S57761-Ghuzan Al Abrar.pdf :: Unduh
|
| No. Panggil : | S57761 |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Entri tambahan-Nama badan : | |
| Penerbitan : | Depok: Universitas Indonesia, 2014 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ita rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xiii, 38 pages ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S57761 | 14-17-180708866 | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20402127 |