Kekerasan permukaan komposit resin dipolimerisasi dengan Light Curing Unit berbeda iradiansi = Hardness of resin composite polimerized by light curing unit different light irradiance / Sarah Azkianisa
Sarah Azkianisa;
Decky Joesiana Indrani, supervisor; Mia Damiyanti, supervisor; Siti Triaminingsih, examiner; Andi Soufyan, examiner
(Fakultas Kedokteran Gigi Universitas Indonesia, 2014)
|
|
ABSTRAK Latar Belakang: LCU prototip dengan metode PWM-kombinasi dengan iradiansi sinar 800, 900, dan 1.000 mW/cm2 telah dibuat untuk mencegah kenaikan suhu pulpa akibat polimerisasi. Tujuan: Menganalisis kekerasan komposit resin yang dipolimerisasi dengan LCU berbeda iradiansi sinar. Metode: Spesimen merupakan komposit resin yang dipolimerisasi dengan LCU prototip (PWMkombinasi) beriradiansi sinar 800, 900, atau 1.000 mW/cm2 atau dengan LCU pembanding (900 mW/cm2). Kekerasan komposit resin diukur menggunakan sistem Knoop. Hasil: Kekerasan komposit resin antar kelompok berbeda bermakna (p<0,05) kecuali yang diberi iradiansi sinar 900 mW/cm2 dari LCUprototip dan LCU pembanding. Kesimpulan: Kekerasan komposit resin dipengaruhi oleh iradiansi sinar dari LCU prototip. LCU prototip atau LCU pembanding dengan iradiansi 900 mW/cm2 menghasilkan kekerasan komposit resin yang sama. ABSTRACT Background: Prototype light curing unit (LCU) with PWM-combined lightirradiance of 800, 900, and 1.000 mW/cm2 was made to prevent the pulp temperature rise due to the polymerization. Objective: To analyze the hardness of resin composites polymerized by LCU different light irradiation. Methods: The specimen is resin composites polymerized by prototype LCU light irradiance 800, 900, or 1.000 mW/cm2 or with comparison LCU (900 mW/cm2). Hardness of resin composite test performed by Knoop system. Result: There is significant differences (p<0.05) among the groups except those between using the prototype LCU and comparison LCU that have irradiance of 900 mW/cm2. Conclusions: The hardness of resin composite was influenced by the irradiance of prototype LCU. The hardness of resin composite from prototype LCU is equal to those from comparison LCU irradiance of 900 mW/cm2. |
 S-Sarah Azkianisa.pdf :: Unduh
|
| No. Panggil : | S-Pdf |
| Entri utama-Nama orang : | |
| Entri tambahan-Nama orang : | |
| Subjek : | |
| Penerbitan : | [Place of publication not identified]: Fakultas Kedokteran Gigi Universitas Indonesia, 2014 |
| Program Studi : |
| Bahasa : | ind |
| Sumber Pengatalogan : | LibUI ita rda |
| Tipe Konten : | text |
| Tipe Media : | unmediated ; computer |
| Tipe Carrier : | volume ; online resource |
| Deskripsi Fisik : | xii, 24 pages : illustration ; 28 cm + appendix |
| Naskah Ringkas : | |
| Lembaga Pemilik : | Universitas Indonesia |
| Lokasi : | Perpustakaan UI, Lantai 3 |
| No. Panggil | No. Barkod | Ketersediaan |
|---|---|---|
| S-Pdf | TERSEDIA |
| Ulasan: |
| Tidak ada ulasan pada koleksi ini: 20402148 |